Double-chamber high-temperature forging and forming device of TiAl intermetallic compound forge piece and method thereof

A technology of intermetallic compounds and forgings, applied in forging/pressing/hammer devices, metal processing equipment, manufacturing tools, etc., can solve the problems of difficult forging forming, excessive heat dissipation of blanks, large deformation resistance, etc., and achieve the deformation of blanks Effects of increasing and reducing forging passes and reducing energy loss

Active Publication Date: 2012-03-21
HARBIN INST OF TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention aims to solve the problems of excessive heat dissipation from the billet to the die, large deformation resistance, serious damage to the die, and difficulty in forging when the traditional forging technology is used to forge the TiAl intermetallic compound material, and proposes a TiAl intermetallic compound Double-chamber high-temperature forging forming device and method for forgings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-chamber high-temperature forging and forming device of TiAl intermetallic compound forge piece and method thereof
  • Double-chamber high-temperature forging and forming device of TiAl intermetallic compound forge piece and method thereof
  • Double-chamber high-temperature forging and forming device of TiAl intermetallic compound forge piece and method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0018] Specific implementation mode one: combine figure 1 , figure 2 , image 3 To illustrate this embodiment, the double-chamber high-temperature forging forming device for TiAl intermetallic compound forgings described in this embodiment includes a high-temperature heating element 5 for a billet, a high-temperature heating element 19 for a mold, a punch 14, and a die 17, which are characterized in that: The forming device also includes a blank heating chamber 7, a mold heating chamber 16, and a movable partition 10. The blank heating chamber 7 and the mold heating chamber 16 are adjacently arranged and a movable partition 10 is arranged between the two, which can be moved by pulling up and down. The partition 10 can realize the mutual penetration of the furnace of the billet heating chamber 7 and the furnace of the mold heating chamber 16 (when the movable partition 10 is pulled upward, the furnace of the blank heating chamber 7 and the furnace of the mold heating chamber ...

specific Embodiment approach 2

[0021] Specific implementation mode two: combination figure 1 , figure 2 , image 3 Describe this embodiment, the billet heating chamber 7 in this embodiment includes a billet heating chamber furnace body 3 and a billet heating chamber furnace door 8, and the billet heating chamber furnace door 8 is installed on the billet heating chamber furnace body away from the mold heating chamber 16 3 on the side wall. Other components and connections are the same as those in the first embodiment.

specific Embodiment approach 3

[0022] Specific implementation mode three: combination figure 1 , figure 2 , image 3 Describe this embodiment, the mold heating chamber 16 in this embodiment includes a mold heating chamber furnace body 20 and a mold heating chamber furnace door 18, and the mold heating chamber furnace door 18 is installed on the mold heating chamber furnace body far away from the billet heating chamber 7 20 on the side wall. Other components and connections are the same as those in the second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a double-chamber high-temperature forging and forming device of a TiAl intermetallic compound forge piece and a method thereof, belonging to forming methods and devices of TiAl intermetallic compound forge pieces. The invention solves the problems of large heat loss, large deformation resistance, small forging deformation, difficult forging and the like generated when thetraditional forging technology is used for forging the TiAl intermetallic compound forge piece. A blank heating chamber and a mould heating chamber are adjacently arranged and a movable baffle plate is arranged between the blank heating chamber and the mould heating chamber, and a hearth of the blank heating chamber and a hearth of the mould heating chamber are mutually penetrated and mutually independent by pulling the movable baffle plate up and down. TiAl blanks and a mould are heated to 1230-1300 DEG C and 800-1000 DEG C respectively in different heating chambers; the movable baffle plateis opened to push the TiAl blanks into the mould heating chamber along a carrying platform and put the TiAl blands into a mould cavity; and the mould is closed for forging. The invention is used for high-temperature forging and forming of TiAl intermetallic compound materials.

Description

technical field [0001] The invention relates to a forming method and device for a TiAl intermetallic compound forging, belonging to the technical field of forging forming technology. Background technique [0002] With the rapid development of industries such as aerospace and automobile manufacturing, the industry has put forward higher and higher requirements for the performance of lightweight heat-resistant structural materials. In this context, TiAl intermetallic compound materials with low density, high specific strength, high specific modulus, and excellent high-temperature mechanical properties and oxidation resistance have become the focus of material research in the past decade, and may be used in some Within a certain range of the field, it has successfully replaced some traditional high-temperature structural materials - titanium-based alloys and nickel-based alloys. [0003] However, TiAl intermetallic compounds have L1 0 Type-ordered crystal structure, low cryst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21K29/00B21J1/06
Inventor 胡连喜王尔德叶磊孙宏飞王欣
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap