Golf tee with Tai Chi patterns and processing method thereof
A technology of golf pins and processing methods, which is applied to golf balls, golf clothes, golf accessories, etc. It can solve problems such as difficult to ensure the supply of solid wood pins, difficult to decompose plastic ball pins, and tight sources of raw materials, so as to enrich the market, Increase the added value and avoid the effect of overly single products
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
specific Embodiment approach
[0027] Step 1: Harvest 3-4 years old small-diameter bamboo, remove the sundries on the bamboo stem, and cut the bamboo stem into bamboo segments; then use bamboo mechanical carding equipment to comb it into small-diameter bamboo carding wood by rolling rollers ;
[0028] Step 2: Put part of the small-diameter bamboo carding material into a wood cooking tank, and pass through superheated steam at 110-150°C for carbonization for 60-180 minutes, making it carbonized small-diameter bamboo carding material, which is dark brown in color ;
[0029] Step 3: Put carbonized and non-carbonized small-diameter bamboo carding materials into wood drying kilns for drying respectively, the drying temperature is 100-110 ° C, and the drying time is 12-24 hours, so that the moisture content of the dried small-diameter bamboo carding materials is 8- 10%;
[0030] Step 4: Immerse the dried carbonized and non-carbonized small-diameter bamboo carding materials in 40% solid content of phenolic resin...
Embodiment 1
[0043] The specific steps of a processing method for golf nails with Taichi patterns are:
[0044] Step 3: Put the carded part of the small-diameter bamboo that has been processed into a wood cooking tank, and introduce superheated steam at 110°C for carbonization for 180 minutes, so that the small-diameter bamboo carding is brown, and the other part of the small-diameter bamboo that has not been carbonized Carding material spare;
[0045] Step 4: Put the carbonized and non-carbonized small-diameter bamboo carding materials into a wood drying kiln for drying, and the drying temperature is 100 ° C until the moisture content of the material is 10%;
[0046] Step 5: Submerge the dried carbonized and non-carbonized small-diameter bamboo carding materials in the phenolic resin glue solution with a solid content of 35%, take them out after 10 minutes, and store them for later use;
[0047] Step 6: Stack the carbonized and non-carbonized small-diameter bamboo carding materials immer...
Embodiment 2
[0056] The specific steps of a processing method for golf nails with Taichi patterns are:
[0057] Step 3: put the carded part of the small-diameter bamboo that has been processed into a wood cooking tank, and introduce superheated steam at 150 ° C for carbonization treatment for 60 minutes, so that the small-diameter bamboo carding material is brown, and the other part of the small-diameter bamboo that has not been carbonized Carding material spare;
[0058] Step 4: Put the carbonized and non-carbonized small-diameter bamboo carding materials into a wood drying kiln for drying, and the drying temperature is 110 ° C until the moisture content of the material is 8%;
[0059] Step 5: Submerge the dried carbonized and non-carbonized small-diameter bamboo carding materials in the phenolic resin glue solution with a solid content of 45%, take them out after 5 minutes, drain them, and store them for later use;
[0060] Step 6: Stack the carbonized and non-carbonized small-diameter ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction