Urea resin additive and preparation method and application thereof

A urea-formaldehyde resin and additive technology, applied in the direction of adhesive additives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of reducing the efficiency and mechanical properties of urea-formaldehyde resin in the production of wood-based panels, and achieve the elimination of formaldehyde Long-lasting effect, easy to use, and the effect of reducing formaldehyde emission

Inactive Publication Date: 2013-03-20
BEIJING FORESTRY UNIVERSITY +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The primary purpose of the present invention is to provide a urea-formaldehyde resin additive that can be directly added to the urea-formaldehyde resin adhesive for the problems existing in the prior art. The formaldehyde elimination rate of the additive is high and the effect is long-lasting, without reducing the efficiency of the urea-formaldehyde resin to produce wood-based panels. and mechanical properties, fundamentally eliminate the formaldehyde pollution problem in indoor air caused by wood-based panels and their products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Urea resin additive and preparation method and application thereof
  • Urea resin additive and preparation method and application thereof
  • Urea resin additive and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1. Prepare raw materials according to the following weight ratio

[0028] Water-emulsion epoxy resin (50% solid content): 200kg

[0029] Distilled water: 300kg

[0030] Borax: 0.5kg

[0031] Urea: 300kg

[0032] Sodium hydroxide solution (concentration 30%): appropriate amount

[0033] Formic acid solution (concentration 20%): appropriate amount

[0034] 2. Add distilled water, borax, and urea to the reaction kettle in turn, start stirring, raise the temperature to 40°C, stir well, and adjust the pH value of the reaction solution to 5.0-5.5 with formic acid;

[0035] 3. Raise the temperature to 70-72°C, react for 30 minutes, adjust the pH value to 6.0-8.0 with sodium hydroxide, cool down to 30°C, and discharge.

[0036] Table 1 Technical indicators of urea-formaldehyde resin additive products

[0037]

Embodiment 2

[0039] 1. Prepare raw materials according to the following weight ratio

[0040] Water-soluble epoxy resin (50% solid content): 300kg

[0041] Deionized water: 800kg

[0042] Borax: 1kg

[0043] Urea: 600kg

[0044] 2. The synthesis process is the same as in Example 1.

[0045] Table 2 Technical indicators of urea-formaldehyde resin additive products

[0046]

Embodiment 3

[0048] 1. Prepare raw materials according to the following weight ratio:

[0049] Waterborne epoxy resin (50% solid content): 500kg

[0050] Water: 1000kg

[0051] Borax and calcium metaborate (1:1 mix): 8kg

[0052] Urea: 1000kg

[0053] 2. The synthesis process is the same as in Example 1.

[0054] Table 3 Technical indicators of urea-formaldehyde resin additive products

[0055]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a urea resin and a preparation method thereof. The urea resin additive comprises the following raw materials in parts by weight: 100-300 parts of waterborne epoxy resin (solid), 100-1000 parts of urea, 50-1000 parts of water and 0.1-10 parts of stabilizing agent. The preparation method comprises the following steps: 1) adding the raw materials to a reaction kettle in sequence according to the proportion in claim 1 or 2, beginning stirring when the raw materials are added, raising the temperature and controlling the temperature at 40-60 DEG C, fully stirring the raw materials until the raw materials are uniform and regulating the pH value of the reaction liquid to be 5.0-5.5 with acid; and 2) raising the temperature to 70-72 DEG C and reacting for 30 minutes, regulating the pH value of the reaction liquid to be 6.0-8.0 with alkali, lowering the temperature to 30 DEG C and discharging the material.

Description

technical field [0001] The invention relates to a preparation for eliminating harmful chemical substances and a preparation method thereof, in particular to a preparation for eliminating formaldehyde and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, decoration and purchase of new furniture have become common things in people's lives. Various types of wood-based panels are often used in large quantities in decoration and furniture manufacturing, such as plywood, blockboard, medium-density fiberboard, and particle board. In 2009, the output of my country's wood-based panels has exceeded 100 million m 3 , ranked first in the world for many years in a row. However, 90% of the adhesives used in these wood-based panels are urea-formaldehyde resin and its modified products, which have the problem of formaldehyde release and often become the main source of formaldehyde pollution in indoor air. Although th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J11/08C09J11/06C09J11/04C09J161/24
Inventor 李建章张世锋刘江波于洋周文瑞高强
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com