High-dehydration hardenable plugging sealing agent

A kind of plugging agent, high water loss technology, applied in the field of plugging plugging agent, hardenable, high water loss, can solve the problems of plugging failure, difficult construction and other problems, achieve fast plugging speed, simplify drilling procedures, The effect of high success rate of plugging

Active Publication Date: 2013-04-24
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the plugging process of the curable cement slurry system, the cement slurry is not easy to stay in the lost channel, and the plugging failure is often caused by leakage into the deep formation. Moreover, due to the solidification characteristics of the cement slurry, its injection time must be strictly controlled, making construction difficult. Big

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-dehydration hardenable plugging sealing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Example 1, 35 Kg of solidified material, 25 Kg of composite plugging agent, 15 Kg of high water loss material, 10 Kg of elastic expansion material, and 15 Kg of fiber material.

Embodiment 2

[0011] Example 2: 40 Kg of cured material, 30 Kg of composite plugging agent, 10 Kg of high water loss material, 5 Kg of elastic expansion material, and 15 Kg of fiber material.

Embodiment 3

[0012] Example 3, 45 Kg of solidified material, 35 Kg of composite plugging agent, 5 Kg of high water loss material, 5 Kg of elastic expansion material, and 10 Kg of fiber material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-dehydration hardenable plugging sealing agent which comprises the following components by mass percent: 35-50% of solidifying material, 25-35% of composite sealing agent, 5-15% of high-dehydration material, 5-10% of elastic expending material and 10-15% of fiber material, wherein the composite sealing agent is formed by mixing granular husk, mica and cotton seed hull in a mass ratio of 5:2:1; the solidifying material is formed by mixing gypsum, cement, blast furnace slag and sodium phosphate in a mass ratio of 1:1:0.5:0.1; the high-dehydration material is kieselguhr or coal ash; the elastic expending material is formed by mixing coated water-sucking rubber and coated water-sucking resin in a mass ratio of 1:1; and the fiber material is polyacrylonitrile fiber of 9-11mm. The sealing agent integrates with high dehydration, delay expanding, plugging solidification and physical overlap joint; and the formed sealing layer is not easy to destroy in the subsequent drilling process, thereby effectively improving the sealing efficiency.

Description

technical field [0001] The invention relates to an additive used in the field of oil field drilling, in particular to a high water loss, hardenable, plugging and plugging agent. Background technique [0002] Lost circulation is a phenomenon in which drilling fluid, cement slurry or other working fluids are lost into the formation during drilling. The occurrence of lost circulation not only consumes drilling time and loss of drilling fluid, but also may cause a series of complex situations such as pipe sticking, blowout, and well collapse. In severe cases, the wellbore will be scrapped and cause major economic losses. [0003] Currently commonly used plugging materials are mainly divided into physical plugging materials and chemical plugging materials: physical plugging materials mainly include bridging plugging materials and high water loss plugging materials. The bridging plugging material is mainly based on the principle of particle gradation, using walnut shells, mica fl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/46
Inventor 竹学友刘永贵何恕郝立志赵晓竹闫晶姜强
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products