Target material and its application in recording layer material of magnetic recording media

A technology of magnetic recording and recording layer, applied in the direction of magnetic recording, coating with magnetic layer, data recording, etc., can solve the problems of oxide running in, the film can not meet the quality requirements, can not be provided, etc., to achieve the effect of improving efficiency

Inactive Publication Date: 2012-05-23
SOLAR APPLIED MATERIALS TECHNOLOGY CORPORATION
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. In order to reduce noise, it is necessary to increase the amount of oxides to achieve good isolation of magnetic particles; but when too much oxide is added, some oxides will run into the magnetic particles, which will cause increased noise
[0006] 2. During the sputtering process, if there are more oxides in the target, it is easier to cause arcing in the local area of ​​the target surface, which will affect the quality of the coating and cause the deposited film to fail to meet the quality requireme

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Target material and its application in recording layer material of magnetic recording media
  • Target material and its application in recording layer material of magnetic recording media
  • Target material and its application in recording layer material of magnetic recording media

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] In order to understand the technical features and practical effects of the present invention in detail, and to implement them according to the contents of the specification, the detailed descriptions are as follows:

[0024] Preferred embodiments of the target material provided by the present invention and its recording layer material used in magnetic recording media are as follows Figure 4 shown.

[0025] The present invention provides a recording layer material of a magnetic recording medium, which is formed by adding an oxide composition to the main material of CoPt, CoCrPt or CoCrPtB; wherein the oxide composition contains copper oxide (CuO) and at least One selected from the group consisting of: titanium oxide (TiO 2 ), chromium oxide (Cr 2 o 3 ), tantalum oxide (Ta 2 o 5 ), niobium oxide (Nb 2 o 5 ), yttrium oxide (Y 2 o 3 ), zirconia (ZrO 2 ), hafnium oxide (HfO 2 ) and combinations thereof.

[0026] In other words, the present invention provides a t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a target material, which is formed by the main material of: CoPt-copper oxide-oxide or CoCrPt-copper oxide-oxide or CoCrPtB-copper oxide-oxide. The added copper oxide is the main technological characteristic. With the application of the target material in the sputtering process of a recording layer material of a magnetic recording media, the sputtering process is stable and the required thickness of an intergranular layer of magnetic particles in the recording layer can be reduced. In addition, thermal stability is high. Therefore, recording density of the recording layer of the magnetic recording media can be raised, and recording capacity of the whole storage media is enhanced.

Description

technical field [0001] The invention relates to a storage medium, especially a target material and a recording layer material used in a magnetic recording medium. Background technique [0002] At present, the magnetic recording of hard disks can be divided into two types according to the direction of magnetization: horizontal recording (longitudinal magnetic recording) and vertical recording (perpendicular magnetic recording). Vertical disc surface. The structure of perpendicular recording media includes substrate (glass or aluminum), adhesion layer, soft underlayer, seed layer, intermediate layer, recording layer, cover layer ( covering layer) and lubricating layer (lubricative layer), such as figure 1 As shown, the most important key technology is the recording layer. Such as figure 2 As shown in the literature report IEEETrans.Magn., 38 (2002) 1976 pointed out that adding oxides in a very thin CoPt-based magnetic recording layer can effectively make the oxide segrega...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/34G11B5/64G11B5/851
Inventor 罗尚贤刘文灿林守贤
Owner SOLAR APPLIED MATERIALS TECHNOLOGY CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap