Orientated nano fiber bionic nerve conduit and manufacturing method thereof

A nerve conduit and nanofiber technology, applied in the field of nerve repair conduit and its production, can solve the problems of poor application effect and poor nerve regeneration effect, and achieve accelerated nerve regeneration speed, excellent tensile strength and shape maintenance ability, The effect of high fiber orientation

Active Publication Date: 2012-07-04
SHANGHAI SIXTH PEOPLES HOSPITAL
View PDF12 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above-mentioned patented technology can improve the strength of the nerve guide, the application effect is not good
[0005] Moreover, the nerve conduits disclosed in the above-mentioned patented technologies all adopt a transverse orientation, and the effect of nerve regeneration is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Orientated nano fiber bionic nerve conduit and manufacturing method thereof
  • Orientated nano fiber bionic nerve conduit and manufacturing method thereof
  • Orientated nano fiber bionic nerve conduit and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0045] The oriented nanofiber bionic nerve conduit of the present invention is made of oriented biodegradable nanofibers, the inner diameter of the nerve conduit is 0.5-5.0 mm, the outer diameter is 1.0-6.0 mm, and the inner and outer diameters can be adjusted according to needs; the degree of orientation ≥ 75%.

[0046] We take PLGA as an example, and adopt the spinning technology to make the nerve guide, the method is as follows:

[0047] Prepare the PLGA solution, connect the spinning device, adjust the spinning parameters such as the solution flow rate, voltage, roller speed, and receiving distance, and prepare a fiber film composed of uniaxially oriented nanofibers by roller stretching; the orientation direction of the nanofibers is In the axial direction, the fiber membrane is crimped to form a nerve fiber conduit, and the rolled nerve conduit can be fixedly connected by suturing or bonding.

[0048] Under the acceleration voltage of 10kv, the fiber morphology was obser...

Embodiment approach 2

[0052] On the basis of Embodiment 1, the nanofibers that make up the bionic nerve guide of the present invention are hollow fibers, and the cavity is filled with biologically active substances such as nerve growth factor (NGF), such as proteins, drugs, etc., to form a shell, core structure.

[0053] refer to figure 1 , taking the coaxial co-spinning electrospinning technology as an example, the manufacturing method of the oriented nanofiber bionic nerve guide of the present invention is as follows:

[0054] Prepare 8% concentration of PLGA solution as the shell solution 6; take 10 μg of NGF freeze-dried powder and dissolve it in phosphate buffered saline solution (PBS) with a pH value of 7.0~7.5, stir evenly to obtain the core solution 5 containing NGF; take two Syringes 1 and 2 absorb the shell solution and the core solution respectively, connect the coaxial electrospinning device, place the shell solution on the outer layer, and the core solution on the inner layer, adjust ...

Embodiment approach 3

[0067] On the basis of Embodiment 2, the core layer of the shell and core structural fibers constituting the bionic nerve guide of the present invention further includes polyethylene glycol.

[0068] Referring to the method described in Embodiment 2, the manufacturing method of the oriented nanofiber biomimetic nerve guide of the present invention is as follows:

[0069] Prepare 8% concentration of PLGA solution as the shell solution; take 10 μg of NGF freeze-dried powder and dissolve it in phosphate buffer solution (PBS) with a pH value of 7.2 to make NGF solution, add 400 mg of PEG to the NGF solution to make a concentration of 400 mg / ml of NGF / PEG solution as the core layer solution.

[0070] Take the syringe to absorb the core layer solution and the shell layer solution respectively, connect the coaxial electrospinning device, place the PLGA solution (shell layer solution) on the outer layer, and the NGF / PEG solution (core layer solution) on the inner layer, adjust the el...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an orientated nano fiber bionic nerve conduit and a manufacturing method thereof. A nano fiber membrane with orientation degree larger than or equal to 75% is prepared by means of coaxial electrostatic spinning, and then is curved to form the nerve conduit, NGF (nerve growth factor) is added into fibers so that the bionic nerve conduit is combined with various factors promoting nerve regeneration, such as 'nano bionics', 'contact guiding', 'drug release' and the like, and the bionic nerve conduit can effective promote nerve regeneration as proved by animal experiments.

Description

technical field [0001] The invention relates to a nerve repair conduit and a manufacturing method thereof, in particular to a nerve conduit capable of rapidly promoting nerve growth and a manufacturing method thereof. Background technique [0002] The nervous system controls the sensory and motor functions of the human body. Once a nerve is damaged, it means the loss of sensory and motor functions in certain parts, which brings great pain to patients. Therefore, nerve repair and regeneration have become the focus of attention. Autologous nerve transplantation is the most classic method of clinically repairing nerve injury, but this method needs to cut out the patient's self-reported healthy nerve, which not only increases the surgical site, but may also cause dysfunction in the innervation area; while allogeneic nerve transplantation requires combined application of immune Inhibitors have a lower transplant success rate. Therefore, the repair of peripheral nerve injuries ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61F2/04A61L29/06A61L29/12A61L29/16D01D5/00D01D5/16D01D5/34
Inventor 范存义汪春阳刘俊建
Owner SHANGHAI SIXTH PEOPLES HOSPITAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com