Ultrahigh toughness steel plate for deep-water pressure resistant shell and manufacture method thereof

An ultra-high-strength and pressure technology used in manufacturing tools, metal rolling, metal rolling, etc., which can solve the problems of reducing the sensitivity of ultra-high-strength steel plates to surface defects, low-temperature toughness, and weldability overquenching.
CN102851611BActive Publication Date: 2014-03-05BAOSHAN IRON & STEEL CO LTD
9 Cites 4 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
BAOSHAN IRON & STEEL CO LTD
Publication Date
2014-03-05

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses ultrahigh toughness steel plate for deep-water pressure resistant shell and manufacture method thereof. The steel plate comprises (by wt%) C 0.05-0.09, Si less than or equal to 0.10, Mn 0.45-0.95, P less than or equal to 0.012, S less than or equal to 0.0030, Cr 0.40-0.80, Mo 0.40-0.80, Ni 3.50-5.50, Cu 0.20-0.50, Ti 0.003-0.010, Als 0.010-0.030, V 0.040-0.080, N less than or equal to 0.0060, O less than or equal to 0.0030, Ca 0.001-0.004, and Fe and unavoidable impurity in balance. The method adopts optimized TMCP and offline quenching and tempering (QT) process, endows microscopic structure of product steel plate with fine low carbon tempered martensite and small amount of tempered bainite, with average packet size smaller than 15 Mum, solves the problem of overquenching of ultrahigh strength steel plate surface, and is especially suitable for use in hydroelectric pressure water pipe and steel yoke pipe of ultrahigh water head (greater than or equal to 1,200 m) power station, and polar ocean platform and deep-water pressure resistant shell.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The present invention relates to an ultra-high-strength steel plate and a manufacturing method thereof, in particular to an ultra-high-strength toughness steel plate for a deep-water pressure-resistant shell and a manufacturing method thereof. Single value) ≥ 100J, elongation at break δ 5 ≥17% and uniform elongation Ag≥7%, excellent weldability. Background technique

[0002] As we all know, low-carbon (high-strength) low-alloy steel is one of the most important engineering structural materials, widely used in oil and gas pipelines, offshore platforms, shipbuilding, bridge structures, boiler containers, building structures, automobile industry, railway transportation and machinery manufacturing. The performance of low-carbon (high-strength) low-alloy steel depends on its chemical composition and manufacturing process, among which strength, toughness, plasticity and weldability are the most important properties of low-carbon (high-strength) low-alloy st...