Process for manufacturing vacuum glass

A manufacturing process and vacuum glass technology, which is applied in the field of vacuum glass sealing, can solve the problems of interlayer condensation, easy falling off of bonding parts, glass mildew, etc., and achieve good effect and good heat insulation effect

Inactive Publication Date: 2013-07-24
佛山晨阳玻璃科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing vacuum glass, a circle of aluminum alloy frame is sandwiched between the upper and lower pieces of glass, and most of them are bonded by adhesives. Since there is no special adhesive, after long-term use or harsh environments, The bonding part is easy to fall off, and water vapor will enter the vacuum glass, dew condensation in the interlayer, and mildew on the glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] A manufacturing process of vacuum glass, comprising the following steps:

[0017] (1) Preparation of hot melt adhesive film:

[0018] The parts by weight of the hot-melt film raw material composition are:

[0019] High-density polyethylene 100, poly-1-butene 2, modified rosin 10, N-2-(aminoethyl)-3-aminopropyltrimethoxysilane 2, vinyl tris(β-methoxyethyl) Oxygen) silane 3, dioctyl ester 2, monoglyceride stearate 2, sepiolite powder 5;

[0020] Preparation method: put each raw material into the mixing chamber of the granulator, heat and mix and stir to make granules; put the granules into the casting machine to obtain a hot-melt adhesive film; and cut into strips;

[0021] Described modified rosin is obtained by the following method:

[0022] First, add 30 parts (by weight, the same below) of rosin, 6 parts of terpene resin, 10 parts of ethylene glycol diglycidyl ether, and 1 part of alum powder into the reaction vessel, stir, and react at 95-110°C for 2 hours; The s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for manufacturing vacuum glass. The process comprises the steps of: preparing the hot-melt adhesive films, cutting an upper flat glass sheet and a low flat glass sheet, clamping aluminum alloy frames between surrounding edges of the upper and lower glass sheets, forming a sealed cavity body through enclosing the aluminum alloy frames, the upper flat glass sheet and the low flat glass sheet, forming an exhausting hole in one aluminum alloy frame, placing hot-melt adhesive film strips on joints between the aluminum alloy frames and the upper and lower glass sheets, clamping through pressurizing, feeding to a heating furnace, keeping the temperature of 130-145 DEG C for 4-5 minutes, taking out and cooling; coating glass cement on junctions between outer sides of the aluminum alloy frames and the glass sheets; and vacuumizing, plugging the exhausting hole, and mounting frames on the periphery of the vacuum glass. According to the process, the prepared hot-melt adhesive films are adopted to seal the glass sheets and the aluminum alloy frames, and the effect is good; and shown by detection on a vacuum glass window which is manufactured by the method and is used more than two years, sealed portions are in good condition and are free of degumming phenomena, the vacuum degree of the interior of an interlayer still maintains a high level, the interior of the interlayer is free of situations, such as condensation and mildewing, and the heat preservation and insulation effects are good.

Description

technical field [0001] The invention relates to a vacuum glass sealing method. Background technique [0002] Vacuum glass, which is composed of multiple glass plates, has attracted people's attention for its excellent sound insulation, heat insulation, and thermal insulation properties, and has been widely used in buildings. In the existing vacuum glass, a circle of aluminum alloy frame is sandwiched between the upper and lower pieces of glass, and most of them are bonded by adhesives. Since there is no special adhesive, after long-term use or harsh environments, The bonding part is easy to fall off, and water vapor will enter the vacuum glass, dew condensation in the interlayer, and glass mildew. Contents of the invention [0003] In view of the deficiencies in the prior art, the object of the present invention is to provide a vacuum glass manufacturing process, which is simple and convenient, and the sealing is reliable and firm. [0004] Technical scheme of the presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C27/00
Inventor 张百庆韩立平
Owner 佛山晨阳玻璃科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products