Bio-diesel catalyst Ca-Mg-Zn-Al-O and preparation method thereof

A biodiesel and catalyst technology, applied in the field of biodiesel catalyst Ca-Mg-Zn-Al-O and preparation, biodiesel catalyst, can solve the problems of slow catalytic reaction rate, harsh requirements, poor activity, etc., and achieve high catalytic activity , Improve adaptability and reduce the effect of harsh requirements

Inactive Publication Date: 2015-03-04
TAIYUAN INST OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

From the two rankings, it can be seen that the Ca-Al-O catalyst has strong activity and fast catalytic reaction rate, but its ability to resist acid, water and saponification is poor, and it has strict requirements on raw materials; Zn-Al-O catalyst is resistant to acid, water and saponification. Strong water resistance and saponification resistance, loose requirements on raw materials, but poor activity, slow catalytic reaction rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bio-diesel catalyst Ca-Mg-Zn-Al-O and preparation method thereof
  • Bio-diesel catalyst Ca-Mg-Zn-Al-O and preparation method thereof
  • Bio-diesel catalyst Ca-Mg-Zn-Al-O and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A biodiesel catalyst Ca-Mg-Zn-Al-O, wherein the molar ratio n (Ca): n (Mg): n (Zn): n (Al): n (O) = 0.5:2:0.5:1:4.5.

[0024] Its preparation method is as follows:

[0025] (1), Moore ratio n (Ca): n (Mg): n (Zn): n (Al): n (OH - ): n (CO 3 2- ) =0.5:2:0.5:1:6:3, weigh 3.54gCa(NO 3 ) 2 4H 2 O (0.015mol), 15.38g Mg(NO 3 ) 2 ·6H 2 O (0.060mol), 4.46g Zn(NO 3 ) 2 ·6H 2 O (0.015mol) and 11.25g Al(NO 3 ) 3 9H 2 O (0.030mol), put it into a 250mL Erlenmeyer flask, add 100mL deionized water to dissolve to obtain aqueous solution A; weigh 7.20g NaOH (0.180mol) and 9.54g NaOH 2 CO 3 (0.090mol), put it into another 250mL Erlenmeyer flask, add 75mL deionized water to dissolve to obtain aqueous solution B.

[0026] (2) Put the aqueous solution A and the aqueous solution B into two constant-pressure dropping funnels respectively, put 100mL deionized water into a 500mL four-neck flask, turn on the stirrer, and adjust the two constant-pressure dropping funnel...

Embodiment 2

[0032] A biodiesel catalyst Ca-Mg-Zn-Al-O, wherein the molar ratio n (Ca): n (Mg): n (Zn): n (Al): n (O) = 0.3:2:0.7:1:4.5.

[0033] Its preparation method is as follows:

[0034] (1), Moore ratio n (Ca): n (Mg): n (Zn): n (Al): n (OH - ): n (CO 3 2- ) =0.3:2:0.7:1:6:3, weigh 2.13g Ca(NO 3 ) 2 4H 2 O (0.009mol), 15.38g Mg(NO 3 ) 2 ·6H 2 O (0.060mol), 6.25g Zn(NO 3 ) 2 ·6H 2 O (0.021mol) and 11.25g Al(NO 3 ) 3 9H 2 O (0.030mol), put it into a 250mL Erlenmeyer flask, add 100mL deionized water to dissolve to obtain aqueous solution A; weigh 7.20g NaOH (0.180mol) and 9.54g NaOH 2 CO 3 (0.090mol), put it into another 250mL Erlenmeyer flask, add 75mL deionized water to dissolve to obtain aqueous solution B.

[0035] (2) Put the aqueous solution A and the aqueous solution B into two constant-pressure dropping funnels respectively, put 100mL deionized water into a 500mL four-neck flask, turn on the stirrer, and adjust the two constant-pressure dropping funne...

Embodiment 3

[0041] A biodiesel catalyst Ca-Mg-Zn-Al-O, wherein the molar ratio n (Ca): n (Mg): n (Zn): n (Al): n (O) = 0.7:2:0.3:1:4.5.

[0042] Its preparation method is as follows:

[0043] (1), Moore ratio n (Ca): n (Mg): n (Zn): n (Al): n (OH - ): n (CO 3 2- ) = 0.7:2:0.3:1:6:3, weigh 4.96g Ca(NO 3 ) 2 4H 2 O (0.021mol), 15.38g Mg(NO 3 ) 2 ·6H 2 O (0.060mol), 2.68g Zn(NO 3 ) 2 ·6H 2 O (0.009mol) and 11.25g Al(NO 3 ) 3 9H 2 O (0.030mol), put it into a 250mL Erlenmeyer flask, add 100mL deionized water to dissolve to obtain aqueous solution A; weigh 7.20g NaOH (0.180mol) and 9.54g NaOH 2 CO 3 (0.090mol), put it into another 250mL Erlenmeyer flask, add 75mL deionized water to dissolve to obtain aqueous solution B.

[0044] (2) Put the aqueous solution A and the aqueous solution B into two constant-pressure dropping funnels respectively, put 100mL deionized water into a 500mL four-neck flask, turn on the stirrer, and adjust the two constant-pressure dropping funn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a solid catalyst preparation and bio-diesel synthesis technology, in particular relates to a bio-diesel catalyst, and specifically relates to a bio-diesel catalyst Ca-Mg-Zn-Al-O and a preparation method thereof. According to the technical scheme adopted by the invention, Ca-Mg-Zn-Al hydrotalcite is firstly prepared by a co-precipitation reaction of nitrate solutions of calcium, magnesium, zinc and aluminum, which are in a molar ratio of n (Ca):n(Mg):n(Zn):n(Al):n(O) of (0.3-0.7):2:(0.3-0.7):1:(4.1-4.9), a sodium hydroxide solution and a sodium carbonate solution; the Ca-Mg-Zn-Al-O solid base catalyst is obtained by roasting at a high temperature. By utilizing the advantages of Ca-Al-O solid base catalyst, Mg-Al-O solid base catalyst and Zn-Al-O solid base catalyst and avoiding defects of the solid base catalysts, the invention provides Ca-Mg-Zn-Al-O solid base as well as a preparation method and application thereof in catalyzing and synthesizing bio-diesel.

Description

technical field [0001] The invention relates to the technical field of solid catalyst preparation and biodiesel synthesis, in particular to a biodiesel catalyst, specifically a biodiesel catalyst Ca-Mg-Zn-Al-O and a preparation method thereof. Background technique [0002] Ca-Al-O, Mg-Al-O and Zn-Al-O composite oxides alone have been reported as biodiesel catalysts, and their catalytic activity order is: Ca-Al-O>Mg-Al-O>Zn -Al-O; the order of resistance to acid, water and saponification is: Zn-Al-O>Mg-Al-O>Ca-Al-O. From the two rankings, it can be seen that the Ca-Al-O catalyst has strong activity and fast catalytic reaction rate, but its ability to resist acid, water and saponification is poor, and it has strict requirements on raw materials; Zn-Al-O catalyst is resistant to acid, water and saponification. The ability to resist water and saponification is strong, and the requirements for raw materials are loose, but the activity is poor, and the catalytic react...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/06C10L1/02
CPCY02E50/13Y02E50/10
Inventor 靳福全赵金安李晓红李东红张颖
Owner TAIYUAN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com