Alkali-resistant chopped glass fiber sizing

A technology of chopped glass fiber and sizing agent, which is applied in the field of glass fiber surface treatment agent, which can solve the problems of alkali resistance, poor water resistance and wear resistance, low strength and unevenness of cement products, etc., and achieve good alkali resistance effect

Active Publication Date: 2016-01-20
陕西汇友友基新材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Alkali-resistant chopped fibers have higher requirements for sizing agents. Most of the existing alkali-resistant glass fiber sizing agents use polyacrylate and vinyl acetate as the main film-forming agent, such as US Patent US.4289536. : 1. It can only meet the chopped fibers of 12㎜-24㎜, and the chopped fibers of 4㎜, 6㎜, and 8㎜ can produce a large amount of hairiness
2. Alkali resistance, water resistance and wear resistance are poor. After the cement mortar is stirred, some fibers will open and produce hairballs, resulting in low strength, uneven surface and rough surface of cement products, which cannot meet the requirements for use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1. Put 30 kg of deionized water in the preparation tank, add 0.01 kg of glacial acetic acid and stir well:

[0052] 2. Add 0.1 kg of coupling agent (GE Silicones, A-174, USA) into the mixture and stir, hydrolyze for 30-60 minutes, it becomes a transparent liquid without oil droplets, and the stirring speed is 60r / m;

[0053] 3. Combine 2.0 kg of polyacrylate film-forming agent (Xi'an Youji Composite Material Co., Ltd., YG5016), 15 kg of epoxy resin emulsion film-forming agent (Xi'an Youji Composite Material Co., Ltd., YG1250) and 1 kg of water-soluble epoxy resin Add film agent (Xi'an Youji Composite Material Co., Ltd., YG801) into the reaction kettle and stir for 10-20min at a stirring speed of 60r / m;

[0054] 4. Add the dilution of 0.01 kg of silicone lubricant (Xi'an Zhongchuang Composite Materials Co., Ltd., ZC-315) with 0.1 kg of deionized water at 50-80°C to the preparation tank, and add the dilution with 50-80°C 0.1 kg of deionized water to dilute 0.01 kg of cat...

Embodiment 2

[0061] 1. Put 30 kg of deionized water in the preparation tank, add 0.03 kg of glacial acetic acid and stir well:

[0062] 2. Add 0.2 kg of coupling agent (GE Silicones, A-174, USA) into the mixture and stir, hydrolyze for 30-60 minutes, it becomes a transparent liquid without oil droplets, and the stirring speed is 60r / m;

[0063] 3. Mix 7.0 kg of polyacrylate film-forming agent (Xi'an Youji Composite Material Co., Ltd., YG5016), 10 kg of epoxy resin emulsion film-forming agent (Xi'an Youji Composite Material Co., Ltd., YG1250) and 3.0 kg of water-soluble epoxy forming agent. Add film agent (Xi'an Youji Composite Material Co., Ltd., YG801) into the reaction kettle and stir for 10-20min at a stirring speed of 60r / m;

[0064] 4. Add the dilution of 0.05 kg of silicone lubricant (Xi'an Zhongchuang Composite Materials Co., Ltd., ZC-315) with 0.5 kg of deionized water at 50-80 ° C to the preparation tank, add the pre-diluted solution with 50-80 ° C 0.5 kg of deionized water to di...

Embodiment 3

[0071] 1. Put 30 kg of deionized water in the preparation tank, add 0.04 kg of glacial acetic acid and stir well:

[0072] 2. Add 0.3 kg of coupling agent (GE Silicones, A-174 in the United States) and stir, hydrolyze for 30-60 minutes, and it becomes a transparent liquid without oil droplets, and the stirring speed is 60r / m;

[0073] 3. Mix 6.0 kg of polyacrylate film-forming agent (Xi'an Youji Composite Material Co., Ltd., YG5016), 7.0 kg of epoxy resin emulsion film-forming agent (Xi'an Youji Composite Material Co., Ltd., YG1250) and 7.0 kg of water-soluble epoxy resin Add film agent (Xi'an Youji Composite Material Co., Ltd., YG801) into the reaction kettle and stir for 10-20min at a stirring speed of 60r / m;

[0074] 4. Add the dilution of 0.1 kg of silicone lubricant (Xi'an Zhongchuang Composite Materials Co., Ltd., ZC-315) with 1.0 kg of deionized water at 50-80 ° C to the preparation tank, add the pre-diluted solution with 50-80 ° C 1.0 kg of deionized water to dilute 0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an alkali-resistant chopped glass fiber soakage agent and relates to a glass fiber surface treating agent containing an organic material. The alkali-resistant chopped glass fiber soakage agent is composed of a film-forming agent, a coupling agent, a lubricant, an antistatic agent, a pH regulator and de-ionized water, wherein the film-forming agent refers to a polyacrylate film-forming agent, an epoxy resin emulsion film-forming agent and a water soluble epoxy resin film-forming agent in the mass ratio of (2.0-20.0): (15.0-2.5): (1.0-10). The alkali-resistant chopped glass fiber soakage agent provided by the invention is suitable for 4 mm to 24 mm alkali-resistant chopped glass fibers; the alkali-resistant chopped glass fibers produced through impregnation in the soakage agent are excellent in alkali resistance, bundling, wear resistance, water resistance, choppability, dispersibility and antistatic property. In the mixing and stirring process of cement, the alkali-resistant chopped glass fiber soakage agent is capable of keeping the bundled state of the previous raw yarns without loosening.

Description

technical field [0001] The invention relates to a glass fiber surface treatment agent containing organic materials. Background technique [0002] Alkali-resistant glass fiber, also known as AR glass fiber, English: alkali-resistant glass fiber, is mainly used to strengthen the reinforced substrate of cement products (GRC for short), and is an ideal substitute for steel and asbestos in non-load-bearing cement components. Ordinary glass fibers are not alkali-resistant, and the main glass components of alkali-resistant glass fibers contain SiO 2 (58%-62%), Na 2 In addition to O (8%-13%), it also contains ZrO 2 (13%-16%), TiO 2 (4%-8%), it is characterized by good alkali resistance, can effectively resist the erosion of high alkali substances in cement, elastic modulus, impact resistance, tensile strength, and high flexural strength, 90% in 5% NaOH solution Corroded at ℃ for 72 hours, the weight loss is 4%. [0003] The glass component of the alkali-resistant fiber contains...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C25/40
Inventor 任川荣张棋任二室张永海
Owner 陕西汇友友基新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products