High-hardness and long-service-life steel wire cut shot producing method and production line

A technology for cutting steel wire shot and production method, which is applied in the field of cutting steel wire shot with high hardness and long life, and achieves the effects of low crushing rate, high hardness and long Owen life.

Inactive Publication Date: 2014-01-22
山东开泰工业科技有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the current steel wire cut shot production process, steel wire with predetermined specifications is generally used to cut the shot directly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hardness and long-service-life steel wire cut shot producing method and production line
  • High-hardness and long-service-life steel wire cut shot producing method and production line
  • High-hardness and long-service-life steel wire cut shot producing method and production line

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Such as Figure 1 to Figure 5 As shown,

[0025] The principle is: using selected raw material scrap steel, adding rare metals and alloys with the best ratio, smelting by electric furnace, transforming into steel wire produced by modern equipment, and undergoing multiple electric heat treatment, drawing, cutting shots, rounding passivation, automatic Screening, in the process of liquid metal forming steel grains, its chemical composition and particle size are strictly controlled to ensure that its mechanical properties meet various uses. Every production link has the most rigorous quality management. The produced steel shot has a tight internal organization, is not easy to be broken, has a uniform particle size distribution, has appropriate hardness, has strong impact resistance and has a long life.

[0026] The following is a detailed description of it in conjunction with the process:

[0027] A production method and production line for cutting steel wire shot with high har...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is a high-hardness and long-service-life steel wire cut shot producing method and production line. The high-hardness and long-service-life steel wire cut shot producing method is characterized by comprising the following steps of coarsely drawing and annealing steel wires, finely draying the steel wires and cutting, rounding, passivating and sieving the steel wires. The steel wire cut shots produced in the method are high in hardness, the hardness of the steel wire cut shots can reach 58-60 HRC, the steel wire cut shots are low in broken rate and long in durability, and the durability is more than 4000 times. The producing method is high in processing speed and can meet the requirements of domestic shot blasting industries.

Description

technical field [0001] The invention relates to a production method of cut steel wire shot, in particular to a production method of cut steel wire shot with high hardness and long service life. Background technique [0002] At present, domestic metal abrasives for shot peening mainly include cast steel shot, steel wire cut shot, stainless steel shot and cast iron shot. The cast steel shot is cast, and shrinkage cavity or looseness is easy to form in the center of the cast steel shot, which reduces the performance of the cast steel shot; the hardness of the stainless steel cut shot is very low, and it can only process stainless steel and aluminum parts with low hardness. The Owen life of cast iron shot is the lowest, with an average of only about 600 times, and the pollution is serious, the production cost is high, and it is now facing elimination; the cut steel shot is made of steel wire, and the structure of the cut steel shot is very dense. Owen has a long life, high hard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23P15/00B21C1/02B21C9/00
CPCB23P15/00B21C1/02B21F11/00
Inventor 刘立艳王勇杰王学亮张嘎肖辰王守仁
Owner 山东开泰工业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap