A kind of immobilized visible light responsive photocatalyst and preparation method thereof

A photocatalyst and visible light technology, applied in the direction of physical/chemical process catalysts, chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, etc. Restricting practical application and other issues, to achieve the effect of expanding the application field and scope, low cost of use, and firm adhesion

Active Publication Date: 2016-01-13
广州安坦科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the coating film is too thin, the contact area with pollutants is limited, and it is easy to fall off under the action of external force, which cannot play the role of photocatalyst, and its use is greatly restricted.
[0006] 3. The above-mentioned photocatalyst needs to be supplemented with ultraviolet light to reflect the effect of photocatalyst on degrading pollutants, which limits its practical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of immobilized visible light responsive photocatalyst and preparation method thereof
  • A kind of immobilized visible light responsive photocatalyst and preparation method thereof
  • A kind of immobilized visible light responsive photocatalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Photocatalytic material: 30 grams

[0043] Cerium-zirconium material (calculated as cerium-zirconium solid solution): 20 grams

[0044] Mixed lanthanum praseodymium: 10 grams

[0045] Poly aluminum: 25 grams

[0046] Silicon magnesium oxide (calculated as magnesium silicate): 15 grams

[0047] Water: 40 grams

[0048] Step A: Weigh the above-mentioned materials, mix them uniformly, and then disperse them in a grinder for 12 hours. Take out the ground liquid and adjust its pH to 6.5 to obtain a colloidal slurry;

[0049] Step B: Choose a ceramic or metal material of suitable shape and size as the carrier, and clean the oil, dirt, impurities, etc. on the surface;

[0050] Step C: According to the shape and structure of the carrier, apply the colloidal slurry to the carrier by dipping, spraying, brushing and other methods, and remove the excess liquid adhering to the carrier to form a layer on the skeleton carrier Uniform and continuous coating film with a thickness of 0.1 to 1.2mm;

...

Embodiment 2

[0053] Photocatalytic material: 55 grams

[0054] Cerium-zirconium material (calculated as cerium-zirconium solid solution): 15 grams

[0055] Mixed lanthanum praseodymium: 5 grams

[0056] Poly aluminum: 15 grams

[0057] Silicon magnesium oxide (calculated as magnesium silicate): 10 grams

[0058] Water: 60 grams

[0059] Step A: Weigh the above-mentioned materials, mix them uniformly, and then disperse them in a grinder for 20 hours. Take out the ground liquid and adjust its pH to 8.5 to obtain a colloidal slurry;

[0060] Step B: Choose a ceramic or metal material of suitable shape and size as the carrier, and clean the oil, dirt, impurities, etc. on the surface;

[0061] Step C: According to the shape and structure of the carrier, apply the colloidal slurry to the carrier by dipping, spraying, brushing and other methods, and remove the excess liquid adhering to the carrier to form a layer on the skeleton carrier Uniform and continuous coating film with a thickness of 0.1 to 1.2mm;

[...

Embodiment 3

[0064] Photocatalytic material: 40 grams

[0065] Cerium-zirconium material (calculated as cerium-zirconium solid solution): 18 grams

[0066] Mixed lanthanum praseodymium: 8 grams

[0067] Poly aluminum: 20 grams

[0068] Silicon magnesium oxide (calculated as magnesium silicate): 14 grams

[0069] Water: 50 grams

[0070] Step A: Weigh the above-mentioned materials, mix them uniformly, and then disperse them in a grinder for 16 hours. Take out the ground liquid and adjust its pH to 7 to obtain a colloidal slurry;

[0071] Step B: Choose a ceramic or metal material of suitable shape and size as the carrier, and clean the oil, dirt, impurities, etc. on the surface;

[0072] Step C: According to the shape and structure of the carrier, apply the colloidal slurry to the carrier by dipping, spraying, brushing and other methods, and remove the excess liquid adhering to the carrier to form a layer on the skeleton carrier Uniform and continuous coating film with a thickness of 0.1 to 1.2mm;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an immobilized visible light-responsive photocatalyst and a preparation method thereof, comprising: in parts by weight: photocatalytic material: 30 to 55 parts; cerium-zirconium solid solution: 15 to 20 parts; mixed lanthanum and praseodymium: 5 to 10 parts; polyaluminum: 15 to 25 parts; silicon magnesium oxide: 10 to 15 parts; water: 40 to 60 parts; among them, photocatalytic material, cerium-zirconium solid solution, mixed lanthanum and praseodymium, polyaluminum and silicon The sum of the parts of magnesium oxide is 100 parts. The beneficial effects of the present invention are: the use of different shapes of material skeletons as the carrier of the photocatalyst, the catalyst is adsorbed on the carrier, and solidified into an integral structure; the method of using the photocatalyst in powder or solution is changed, and the photocatalyst is omitted Separation from the substrate to avoid possible secondary pollution.

Description

technical field [0001] The invention relates to a catalyst for environmental protection and a preparation method thereof, in particular to a catalyst capable of harmlessly degrading gas-phase toxic and harmful pollutants in the environment under light conditions and a preparation method thereof. Background technique [0002] Photocatalysts can completely degrade pollutants (especially organic pollutants) in the atmosphere and water into substances that are harmless to the environment and the human body. More and more attention has been paid to environmental pollution control. It is the most effective and promising environmental protection method. technology. Existing photocatalysts are mainly used in the form of solution or powder. When in use, the photocatalyst is mixed with pollutants, and then irradiated with ultraviolet light to finally decompose the pollutants into harmless substances, so as to purify pollutants and protect the environment role. [0003] The above-men...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/31B01J35/10A62D3/17A62D101/20A62D101/26A62D101/28
Inventor 石江潭
Owner 广州安坦科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap