A kind of silica crystal stone material containing seaweed silica powder and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of seaweed silicon and silicon crystal, which is applied in the field of silicon crystal stone and its preparation, to achieve the effect of uniform coloring, simple and easy preparation method, and suitable for industrial production
Active Publication Date: 2016-01-20
ZHUHAI SESALI HEALTH STONE CO LTD
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although resin-based artificial stone can meet the requirements of daily applications and has been widely used, there is still room for further optimization of performance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0029] A silicon crystal stone material containing seaweed silica powder, its preparation raw materials include the following materials in parts by weight: 3 parts of silicon powder, 5 parts of seaweed mud, 50 parts of quartz sand, 20 parts of glass powder, 0.1 part of color paste, polyester resin 5 parts, 0.05 parts of curing agent, 0.05 parts of coupling agent. Wherein the curing agent is methyl ethyl ketone peroxide, and the coupling agent is a silane coupling agent (KH-570).
Embodiment 2
[0031] A silicon crystal stone material containing seaweed silica powder, its preparation raw materials include the following materials in parts by weight: 3-10 parts of silicon powder, 15 parts of seaweed mud, 70 parts of quartz sand, 35 parts of glass powder, 1 part of color paste, poly 10 parts of ester resin, 0.1 part of curing agent, 0.1 part of coupling agent. Wherein the curing agent is tert-butyl peroxybenzoate, and the coupling agent is a silane coupling agent (KH-570).
Embodiment 3
[0033] A silicon crystal stone material containing seaweed silica powder, its preparation raw materials include the following materials in parts by weight: 10 parts of silicon powder, 30 parts of seaweed mud, 90 parts of quartz sand, 50 parts of glass powder, 10 parts of color paste, polyester resin 15 parts, 0.15 parts of curing agent, 0.15 parts of coupling agent. Wherein the curing agent is methyl ethyl ketone peroxide, and the coupling agent is a silane coupling agent (KH-570).
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a silicon crystal stone material containing seaweed silica powder. The preparation raw materials include the following materials in parts by weight: 3-10 parts of silicon powder, 5-30 parts of seaweed mud, 50-90 parts of quartz sand, and 20 parts of glass powder. -50 parts, 0.1-10 parts of color paste, 5-15 parts of polyester resin, 0.05-0.15 parts of curing agent, 0.05-0.15 parts of coupling agent. The invention also discloses a preparation method of the resin-type stone, which includes steps: 1) taking each material according to the amount; 2) mixing materials: mixing quartz sand, glass powder, silicon powder, seaweed mud, and polyester resin, stirring for 1 After -5 minutes, add color paste, curing agent and coupling agent, mix and stir to form stone mud; 3) press the stone mud under vacuum; 4) solidify and demould at room temperature, and then cut and polish to obtain finished product. The stone material of the invention can be used in an environment with low temperature and excessive humidity, has enhanced impermeability, strength, salt resistance, corrosion resistance, is more beautiful, and can purify air.
Description
technical field [0001] The invention relates to an artificial stone and a preparation method thereof, in particular to a silicon crystal stone and a preparation method thereof. Background technique [0002] With the improvement of people's living standards and the development of the construction industry, the stone industry is also booming, and people have higher and higher requirements for stone. [0003] Stone materials for architectural decoration can be mainly divided into two categories: natural stone and artificial stone. Natural stone can be divided into granite, marble and so on. However, the use of natural stone is limited by natural resources and processing methods. Compared with natural stone, artificial stone has the advantages of bright color, high finish, uniform color and light weight. With the continuous advancement of science and technology, artificial stone products have been used more and more widely. According to the classification of raw materials, a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more