Color metallic orthodontic bracket as well as manufacturing method thereof and composite structure

A technology of orthodontic brackets and colored metals, applied in the direction of brackets, electrolytic coatings, surface reaction electrolytic coatings, etc., can solve the problems of no obvious improvement in appearance and few users of titanium brackets, and achieve excellent biocompatibility Sexuality, keeping the mood happy, and the effect of strong adhesion

Inactive Publication Date: 2015-04-01
GRINM MEDICAL INSTR BEIJING CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Titanium and titanium alloys have excellent corrosion resistance and biocompatibility, so pure titanium brackets appear on the market, but pure titanium brackets also have obvious metallic color like stainless steel brackets, and there is no obvious improvement in appearance, so titanium Not many bracket users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color metallic orthodontic bracket as well as manufacturing method thereof and composite structure
  • Color metallic orthodontic bracket as well as manufacturing method thereof and composite structure
  • Color metallic orthodontic bracket as well as manufacturing method thereof and composite structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Colorful orthodontic brackets with rainbow effect: The brackets are made of pure titanium grade TA2, and bracket blanks of various tooth positions are prepared according to the route of cutting-forming-welding-polishing-cleaning. The bracket is colored by anodic oxidation method, the electrolyte temperature is 18°C, and the electrolyte is 0.5mol / L H 2 SO 4 +0.5mol / L HCl+deionized water, the oxidation time is 10min, and the brackets of different tooth positions are anodized according to the process parameters in Table 1.

[0029] The process of anodic oxidation reaction is:

[0030] Ti → Ti 2+ ;

[0031] 2H 2 O→O 2 +2H 2 ;

[0032] Ti 2+ +2O 2- →TiO 2 ;

[0033] Table 1 Anodizing parameter list

[0034] tooth position

[0035] According to the order of the rainbow colors according to the arrangement of the teeth, the colorful brackets with rainbow effects can be obtained after combination packaging.

Embodiment 2

[0037] Colored orthodontic brackets with wave effect: The brackets are made of titanium alloy grade TC4, and bracket blanks of various tooth positions are prepared according to the route of cutting-forming-welding-polishing-cleaning. The bracket is colored by anodic oxidation method, the electrolyte temperature is 20°C, and the electrolyte is 0.5mol / L H 2 SO 4 +0.2mol / L of H 3 PO 4 + Deionized water, the oxidation time is 10 minutes, and the brackets of different tooth positions are anodized according to the process parameters in Table 2.

[0038] Table 2 Anodizing parameter list

[0039]

[0040] According to the arrangement of the teeth and in the order of the color of the waves, the colorful brackets with the effect of waves can be obtained after combination packaging.

Embodiment 3

[0042] Colored brackets with maple leaf effect: The brackets are made of titanium alloy grade TC4, and bracket blanks for various tooth positions are prepared according to the route of cutting-forming-welding-polishing-cleaning. The bracket is colored by anodic oxidation method, the electrolyte temperature is 18°C, and the electrolyte is 0.5mol / L H 2 SO 4 +0.5mol / L HCl+deionized water, the oxidation time is 10min, and the brackets of different tooth positions are anodized according to the process parameters in Table 3.

[0043] Table 3 Anodizing parameter list

[0044]

[0045] According to the arrangement of the teeth and in the order of the color of the maple leaf, the colored brackets with maple leaf effect can be obtained after combination packaging.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of orthodontics, and in particular relates to a color metallic orthodontic bracket as well as a manufacturing method thereof and a composite structure. The orthodontic bracket is manufactured by using titanium-based metals; the titanium-based metals are subjected to material cutting, formation, welding, polishing, cleaning and anode oxidization so that the outer surface of the manufactured orthodontic bracket is colored. By using the titanium-based metals with high biological performance, the titanium-based metals are suitable for environment of the oral cavity, so that the risk of anaphylaxis on a human body caused by nickel ions which are separated out in a traditional stainless steel bracket is avoided. According to the color metallic orthodontic bracket, a personalized dental aesthetic demand of a patient can be fully met; under the combination of the color metallic orthodontic bracket and a digital design technology of a current initial oral cavity aesthetics, the communication among patients, doctors and technicians can be effectively improved, and an application range of a titanium-based material surface anode oxidization technology on orthodontic appliances can be widened.

Description

technical field [0001] The invention belongs to the technical field of orthodontics, and in particular relates to a colored metal orthodontic bracket, a preparation method and a combined structure thereof. Background technique [0002] Orthodontic brackets are an important part of fixed appliances. Clinically, the brackets are required not only to have good mechanical properties and low friction, but also to have good biocompatibility, comfort and appearance. With the changes of the times, patients have higher and higher requirements for the aesthetics of brackets. Today's young people pay more attention to personalization, and to adapt to it, the concept of personalized aesthetic dental treatment has emerged, and colored brackets and colored dental arch wires have appeared in orthodontic materials. [0003] There are two ways to obtain colored brackets. One is colored plastic brackets, which have poor mechanical properties, are easy to fall off, and have poor correction e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61C7/14C22C14/00B23P15/00C25D11/26
Inventor 吝德智王胜难王江波袁志山崔跃李君涛尚再艳王越缪卫东朱明
Owner GRINM MEDICAL INSTR BEIJING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap