A kind of antifogging and dripping composition containing polyol fatty acid ester and preparation method thereof

A fatty acid ester, anti-fog and dripping technology, applied in the direction of coating, etc., can solve the problems of poor compatibility of resins with high temperature resistance, and achieve the effects of strong compatibility, simple formula and convenient use

Active Publication Date: 2017-10-27
GUANGZHOU CARDLO BIOCHEM TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the technical deficiencies of the anti-fog and dripping agent in the plastic processing process in the prior art, which have poor high temperature resistance and resin compatibility, the present invention provides an anti-fog and dripping composition containing polyol fatty acid ester, which It is composed of monoalcohol polybasic acid ester and pentaerythritol fatty acid ester. The anti-fog and dripping agent prepared after the liquid phase mixing and melting of the two not only has excellent anti-fog and dripping performance, but also has the advantages of high temperature resistance and good compatibility with resin. Suitable for promotion and application in the field of plastic processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antifogging and dripping composition containing polyol fatty acid ester and preparation method thereof
  • A kind of antifogging and dripping composition containing polyol fatty acid ester and preparation method thereof
  • A kind of antifogging and dripping composition containing polyol fatty acid ester and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1 An anti-fogging and dripping composition containing polyol fatty acid ester and its preparation method

[0023] An anti-fog and drip composition containing polyol fatty acid ester, which is prepared from the following components:

[0024]

[0025] The preparation method of the anti-fog and dripping composition containing polyol fatty acid ester is: inject the monoalcohol polybasic acid ester into the liquid-phase mixing and melting tank, stir and raise the temperature to 50-65°C, and put it into the liquid-phase mixing-melting tank Sorbitan monooleate and pentaerythritol di-fatty acid ester or pentaerythritol mono-fatty acid ester, stir and heat up to 95-110°C, keep stirring under negative pressure for 30-50min, and empty the liquid phase mixing and melting tank to reduce the negative pressure to get mixed melting For the composition, send the miscible material into a powder spraying tower to spray resin powder, and cool to obtain the anti-fog dripping comp...

Embodiment 2

[0026] Example 2 An anti-fogging and dripping composition containing polyol fatty acid ester and its preparation method

[0027] An anti-fog and drip composition containing polyol fatty acid ester, which is prepared from the following components:

[0028]

[0029]The preparation method of the anti-fog and dripping composition containing polyol fatty acid ester is: inject the monoalcohol polybasic acid ester into the liquid-phase mixing and melting tank, stir and raise the temperature to 50-65°C, and put it into the liquid-phase mixing-melting tank Sorbitan monooleate and pentaerythritol di-fatty acid ester or pentaerythritol mono-fatty acid ester, stir and heat up to 95-110°C, keep stirring under negative pressure for 30-50min, and empty the liquid phase mixing and melting tank to reduce the negative pressure to get mixed melting For the composition, send the miscible material into a powder spraying tower to spray resin powder, and cool to obtain the anti-fog dripping compo...

Embodiment 3

[0030] Example 3 An anti-fogging and dripping composition containing polyol fatty acid ester and its preparation method

[0031] An anti-fog and drip composition containing polyol fatty acid ester, which is prepared from the following components:

[0032]

[0033] The preparation method of the anti-fog and dripping composition containing polyol fatty acid ester is: inject the monoalcohol polybasic acid ester into the liquid-phase mixing and melting tank, stir and raise the temperature to 50-65°C, and put it into the liquid-phase mixing-melting tank Sorbitan monooleate and pentaerythritol di-fatty acid ester or pentaerythritol mono-fatty acid ester, stir and heat up to 95-110°C, keep stirring under negative pressure for 30-50min, and empty the liquid phase mixing and melting tank to reduce the negative pressure to get mixed melting For the composition, send the miscible material into a powder spraying tower to spray resin powder, and cool to obtain the anti-fog dripping comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of macromolecular materials, and relates to an anti-fog and dripping composition containing polyol fatty acid ester and a preparation method thereof. In order to overcome the technical deficiencies of the anti-fog and dripping agents in the prior art, which have high temperature resistance and poor compatibility with resins, the present invention provides an anti-fog and drip composition containing polyhydric alcohol fatty acid ester, which is composed of unit alcohol polyhydric Pentaerythritol fatty acid ester and pentaerythritol fatty acid ester. The anti-fog and dripping agent prepared by mixing and melting the two liquid phases not only has excellent anti-fog and dripping performance, but also has the advantages of high temperature resistance and good compatibility with resins. It is suitable for plastic processing Field promotion and application.

Description

technical field [0001] The invention belongs to the field of macromolecular materials, and relates to an anti-fog and dripping composition containing polyol fatty acid ester and a preparation method thereof. Background technique [0002] Dripping agents and anti-fogging agents are generally compounded by a variety of ester compounds. These compounds are composed of hydrophilic groups and hydrophobic groups. After adding dripping agents and anti-fogging agents to plastic films, their molecular movements can be Through the gradual migration of the non-crystalline area inside the plastic to the surface of the film for directional alignment, the hydrophilic groups of the dripping agent and anti-fogging agent molecules are automatically arranged on the outside of the film, toward the side of the air, while the hydrophobic groups are automatically arranged on the inside of the film. Forms a hydrophilic film. Anti-fog agents can be divided into two categories according to the meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/1535C08K5/103C08K5/11C08L23/06C08J7/06
Inventor 徐怀义马银官郑炳云
Owner GUANGZHOU CARDLO BIOCHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap