A short-process rolling forming device and method for a three-layer metal composite plate

A metal clad plate, short process technology, applied in metal rolling and other directions, can solve the problems of many production processes, high material and energy consumption, long process flow, etc. Effect

Active Publication Date: 2016-06-29
GUANGDONG INST OF NEW MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, using these methods to prepare three-layer metal composite panels, the same production process is many, the process flow is long, and the consumption of materials and energy is large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A short-process rolling forming device and method for a three-layer metal composite plate
  • A short-process rolling forming device and method for a three-layer metal composite plate
  • A short-process rolling forming device and method for a three-layer metal composite plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Adopt the present invention to produce 4005 / 3003 / 4005 three-layer aluminum alloy composite board. This three-layer aluminum alloy composite board has the advantages of good welding performance of 4005 aluminum alloy and good corrosion resistance of 3003 aluminum alloy. It is often used in the manufacture of automobiles, electronics, Heat exchangers for electrical appliances, etc., as follows:

[0044] Step 1: Clean the surface of the core layer 3003 aluminum alloy plate to remove oil stains and scale on the surface;

[0045] Step 2: Pass the core layer 3003 aluminum alloy plate through the rectangular channel on the preheating device and the rectangular channel on the crystallizer in turn, and finally reach the gap between the two rolls, and then turn on the power of the preheating device to heat the core layer The metal plate is preheated, and the preheating temperature is 200°C;

[0046] Step 3: Heat and melt the 4005 aluminum alloy liquid in a resistance melting fur...

Embodiment 2

[0051] Adopt the present invention to produce 4005 / 3003 / 7002 three-layer aluminum alloy composite board, this kind of three-layer aluminum alloy composite board has the advantages of good welding performance of 4005 aluminum alloy, 7002 aluminum alloy and good corrosion resistance of 3003 aluminum alloy, and is also commonly used in Manufacture heat exchangers for automobiles, electronics, electrical appliances, etc., as follows:

[0052] Step 1: Clean the surface of the core layer 3003 aluminum alloy plate to remove oil stains and scale on the surface;

[0053] Step 2: Pass the core layer 3003 aluminum alloy plate through the rectangular channel on the preheating device and the rectangular channel on the crystallizer in turn, and finally reach the gap between the two rolls, and then turn on the power of the preheating device to heat the core layer The metal plate is preheated, and the preheating temperature is 200°C;

[0054] Step 3: Heat and melt 4005 aluminum alloy liquid ...

Embodiment 3

[0059] Adopt the present invention to produce steel / aluminum / steel three-layer metal composite board, steel is 304 stainless steel, aluminum is 6063 aluminum alloy, this kind of steel / aluminum / steel three-layer metal composite board is usually used in the manufacture of high-end cooking utensils such as oil-free pan, electric cooker, etc. The bottom of the pot has the advantages of uniform heat transfer, safety and environmental protection. The method is as follows:

[0060] Step 1: Clean the surface of the 6063 aluminum alloy plate on the core layer to remove oil and scale on the surface;

[0061] Step 2: Pass the core layer 6063 aluminum alloy plate through the rectangular channel on the preheating device and the rectangular channel on the crystallizer in turn, and finally reach the gap between the two rolls, and then turn on the power of the preheating device to heat the core layer The metal plate is preheated, and the preheating temperature is 150°C;

[0062] Step 3: Heat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A short-process rolling forming device and method for a three-layer metal composite plate, comprising a frame, two rollers installed horizontally side by side on the frame, a crystallizer installed on the two rollers, and two rollers installed on the crystallizer A tundish and a preheating device installed in the middle of the crystallizer and between the two tundishes, the center of the crystallizer and the center of the preheating device are provided with a rectangular channel for the core metal plate to pass through. The present invention has adopted the structure that two crystallization cavities are arranged between the crystallizer and the two rolls and a rectangular passage for the core layer metal plate to pass is arranged at the center of the crystallizer. In the two crystallization cavities, the The two cladding layer metal liquids are continuously cooled and stirred into a semi-solid slurry, and then they are directly compounded and rolled with the core metal plate to form a three-layer metal composite plate. The board quality is good and so on.

Description

technical field [0001] The invention belongs to the technical field of metal composite plate preparation, and in particular relates to a short-flow rolling forming device and method for a three-layer metal composite plate. Background technique [0002] The three-layer metal composite panel is a metal composite panel with a sandwich structure formed by covering the upper and lower sides of the core metal plate with two other layers of metal. The core metal and the cladding metal are combined by interface metallurgy. The core metal and the cladding metal on the upper and lower sides are different metals, and the cladding metal on the upper and lower sides can be the same metal. It can also be different metals. Therefore, the three-layer metal composite board combines the properties of two or three metals. It is a multi-functional and multi-purpose metal board that can be widely used in automobiles, electronic appliances, metallurgy, chemical industry aerospace and other field...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/46B21B1/38B22D11/06
CPCB21B1/38B21B1/46B22D11/06
Inventor 王顺成王海艳郑开宏李继林黎小辉农登
Owner GUANGDONG INST OF NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap