Manufacturing method for making decorative building materials with mixed color glass particles
A technology of glass particles and a manufacturing method, applied in the field of decoration engineering, can solve the problems of lack of three-dimensional effect, single surface color, cumbersome production process, etc., and achieve the effects of environmental protection, good artistic effect and energy saving.
Inactive Publication Date: 2017-04-12
EVERSTONE BUILDING MATERIALS QINGDAO
View PDF3 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
At present, the surface color of ceramic handicrafts is single and lacks a three-dimensional effect, and the production process of applying mixed color glass to the surface of ceramic handicrafts is relatively cumbersome
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0028] The present invention will be further described below in conjunction with embodiment.
[0029] A method for producing a blue system with a galaxy dream effect, comprising the following steps:
[0030] 1. Pre-treatment of glass particles:
[0031] De-angling glass shards;
[0032] Selection of glass particles: select glass particles with the same main formula, material properties, expansion coefficient and specifications;
[0033] 2. Prepare the mold: the mold is composed of a bottom plate and a coaming plate, and the inner surface of the bottom plate and the coaming plate is sprayed with isolation powder;
[0034] 3. Mixing: Mix the glass particles of various colors according to the different particle sizes: the particle size range is 0mm-25mm;
[0035] Fourth, the fabric of the pendulum board:
[0036] Lay the mold in step 2 flat;
[0037] Sprinkle multiple layers of glass particles according to the particle size from small to large from bottom to top;
[0038] 5...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention aims at providing a manufacture method for a decoration building material by using a mixed-color glass particle, and the manufacture method is simple in operation, energy-saving and environment-friendly, and is capable of realizing waste reutilization, and the manufactured decoration material has good aesthetic feeling and stereo perception. The method comprises the steps: performing early-stage processing on the glass particle, preparing a mold, mixing a material, putting a plate and distributing the material, compacting, feeding a furnace, discharging from the furnace, and cooling. Compared with the prior art, the beneficial effects comprise that the manufacture method for the decoration building material by using the mixed-color glass particle overcomes disadvantages in the prior art, the product produced by using waste and old glass particle possesses scraggly stereo perception, also products with various colors and industrial aesthetic feeling can be produced by matching color according to actual demands, and the product possesses extremely good artistic effect. Also, waste is changed into valuables, energy is saved and environment protection is facilitated.
Description
technical field [0001] The invention belongs to the technical field of decoration engineering for fixed buildings, and in particular relates to a method for manufacturing decorative materials—a method for manufacturing decorative building materials with mixed-color glass particles. Background technique [0002] There are many types of glass products available, the most extensive of which is hot-melt glass. Hot-melt glass is made by using a special hot-melting furnace, using flat glass and inorganic pigments as the main raw materials, setting a specific heating program and annealing curve, heating to above the softening point of the glass, and annealing after molding with a special mold. If necessary, subsequent processes such as engraving, drilling, and trimming are carried out. The flat glass can be processed into various artistic effects with concave and convex and different colors, and its application range is very wide because of its unique glass material and artistic e...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C03B19/06
CPCC03B19/09
Inventor 曾君
Owner EVERSTONE BUILDING MATERIALS QINGDAO