A special protective film formula for brushed aluminum plate

A brushed aluminum plate and protective film technology, applied in the formulation field of special protective film for brushed aluminum plate, can solve the problems of processing toughness, weather resistance defects, scratches, pollution, etc., achieve excellent scratch resistance and corrosion resistance, and form fast and convenient. , to maintain the effect of stickiness

Active Publication Date: 2017-05-03
昆山金华安电子科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing process, the stamping and coating of the aluminum plate are carried out simultaneously. When stamping and coating the wire-drawn aluminum plate, problems such as residual glue, sticking, indentation, scratches and pollution are prone to occur. Moreover, the existing Films with known formulations have defects in processing toughness and weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A special protective film formula for brushed aluminum plate
  • A special protective film formula for brushed aluminum plate
  • A special protective film formula for brushed aluminum plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further described in detail below in conjunction with the embodiments, so that those skilled in the art can implement it with reference to the description.

[0024] This case proposes an embodiment of a special protective film formula for brushed aluminum plates, including the following materials by weight:

[0025]

[0026] Among them, the density of low density polyethylene is 0.898 ~ 0.918g / cm 3 , the density of linear low density polyethylene is 0.920~0.932g / cm 3 . In this case, linear low-density polyethylene (LLDPE) is not only different from low-density polyethylene (LDPE) in terms of density and molecular weight, but also has obvious differences in structure. Linear low-density polyethylene does not have long-chain branches in its structure. Although low-density polyethylene may not have long-chain branches in theory, in reality, low-density polyethylene contains a certain amount of long-chain branches. Therefore, in this case,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula for a special protective film of a brushed aluminum plate. The formula comprises the following materials in parts by weight: 50-60 parts of low-density polyethylene, 20-30 parts of linear low-density polyethylene, 5-10 parts of SEBS, 0.1-0.3 part of an antioxidant, 0.2-0.3 part of polyethylene wax, and 0.1-0.2 part of oleamide. Through the adoption of the elasticity and self adhesive force of SEBS, the problem of glue residues on a glue coating film is effectively solved, and the problems of indentation, scratch, pollution and the like appearing in a stamping process of the brushed aluminum plate are solved; through the addition of the polyethylene wax, the protective film can be quicker and more convenient to form and easy to peel off, so that the sticky phenomenon after stamping of the brushed aluminum sheet is prevented, that is, not only can the stickiness be kept, but also the protective film can be conveniently tore down; through the introduction of a composite antioxidant in the formula, the ageing-resistant performance of the protective film is greatly improved, and the weathering-resistant performance of the brushed aluminum plate is improved. Therefore, the protective film is more durable.

Description

technical field [0001] The invention relates to a formula of a polymer film, in particular to a formula of a special protective film for a wire drawing aluminum plate. Background technique [0002] The special protective film for the brushed aluminum plate is used to protect the brushed aluminum plate, covering a layer of special polymer film pasted on the surface of the brushed aluminum plate. This kind of film requires stable viscosity, easy to use, easy to tear and stick, no residual glue, high elongation, strong fracture resistance, good packaging performance, moisture-proof and rain-proof. However, in the existing process, the stamping and coating of the aluminum plate are carried out simultaneously. When stamping and coating the wire-drawn aluminum plate, problems such as residual glue, sticking, indentation, scratches and pollution are prone to occur. Moreover, the existing Films of known formulations have defects in processing toughness and weather resistance. Con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/08C08L53/02C08L27/16C08K13/02C08K3/22C08K5/20C08K5/18C08K5/13C08K5/372C08K5/3437
CPCC08J5/18C08J2323/06C08J2423/08C08J2427/16C08J2453/02C08L23/06C08L2201/08C08L2203/16C08L2205/025C08L2205/035C08L2207/066C08L23/0815C08L53/025C08L27/16C08K13/02C08K5/20C08K5/18C08K5/13C08K5/372C08K5/3437C08K2003/2296C08K2003/2231C08K2003/221
Inventor 徐秀坤陈林杰潘翌泉梁业彬潘德海
Owner 昆山金华安电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com