Fluorine-silicon sealant for fuel oil-resisting solvent part and preparation method for fluorine-silicon sealant
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A sealant, fuel-resistant technology for rubber applications
Inactive Publication Date: 2015-11-25
SUZHOU DATONG ADVANCED MATERIAL
View PDF2 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The purpose of the present invention is to prepare a kind of fluorosilicon s
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] The composition and content of the LED silicone potting compound by weight are:
[0022] Base material: Add hydroxyl-terminated fluorosilicone rubber, white carbon black and activated nano-calcium carbonate according to the formula, and stir at high speed under vacuum for 1 hour.
[0023] Auxiliary: Mix tetraethyl orthosilicate, accelerator and catalyst evenly according to the formula.
[0024] When in use, it is mixed evenly according to the ratio of base material to additives at 10:1, and it can be used after removing air bubbles under vacuum.
Embodiment 2
[0026] The composition and content of the LED silicone potting compound by weight are:
[0029] Base material: Add hydroxyl-terminated fluorosilicone rubber and white carbon black according to the formula, and stir at high speed under vacuum for 1 hour.
[0030] Auxiliary: Mix tetraethyl orthosilicate, accelerator and catalyst evenly according to the formula.
[0031] When in use, it is mixed evenly according to the ratio of base material to additives at 10:1, and it can be used after removing air bubbles under vacuum. Example 1:
[0032] The composition and content of the LED silicone potting compound by weight are:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a fluorine-silicon sealant for a fuel oil-resisting solvent part. The fluorine-silicon sealant is characterized by comprising the following components in parts by weight: 100 parts of hydroxyl end-capping fluorinated silicone rubber, 5-20 parts of white carbon black, 0-100 parts of nano calcium carbonate, 10-20 parts of a cross-linking agent, 1-5 parts of an accelerant, and 0.2-0.5 part of a curing agent. A preparation method for the sealant is characterized by comprising: preparing a base stock: adding the hydroxyl end-capping fluorinated silicone rubber, the white carbon black and the active nano calcium carbonate according to a formula, and stirring the mixture for one hour at a high speed in vacuum; preparing an auxiliary agent: uniformly mixing the tetraethylortho silicate, the accelerant and the catalyst according to the formula; and in use, adding 1 part of the auxiliary agent into 10 parts of the base stock, and uniformly stirring the mixture in vacuum to obtain the sealant. The product has good fuel oil resistance and excellent mechanical properties.
Description
technical field [0001] The invention belongs to the technical field of rubber, and in particular relates to a fluorosilicon sealant used for parts resistant to fuel oil solvents and a preparation method thereof. Background technique [0002] With the development of national defense and modern science and technology, the requirements for materials are becoming more and more stringent. The development of organosilicon materials began in the 1930s. Performance, aging resistance, self-extinguishing properties and other excellent properties; while fluorocarbon materials have good thermal stability, and have extremely superior resistance to fuel and chemical media. Dowcorning skillfully complements the advantages of fluorine materials with good oil resistance, chemical medium resistance and poor low temperature resistance with organic silicon materials, and develops a series of fluorosilicon products. [0003] Fluorosilicone rubber is widely used in the market, and has been used ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.