A negative lead paste for power lead-acid battery and preparation method thereof

A technology of lead-acid battery and negative electrode paste, applied in lead-acid battery, battery electrode, circuit, etc., can solve the problems of short cycle life and achieve the effects of improved cycle life, low-temperature capacity, and high specific energy

Active Publication Date: 2017-07-21
ANHUI CHAOWEI POWER
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the deficiencies of the prior art, and provides a lead paste for the negative pole of a power lead-acid battery and a preparation method thereof, thereby effectively improving the low-temperature performance of the power lead-acid battery and solving the problem of short cycle life in a low-temperature state.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A negative lead paste for power lead-acid battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] Such as figure 1 Shown is a schematic flow chart of a method for preparing the negative electrode paste of a power lead-acid battery according to the present invention. A kind of preparation method of power lead-acid storage battery negative lead paste of the present invention, comprises the following steps:

[0023] Step 1. Accurately weigh the following components by mass: 0.6 parts of synthetic fibers, 20 parts of barium sulfate, 0.5 parts of lignin, 1.5 parts of stannous sulfate, 1.5 parts of sodium lignosulfonate, and 15 parts of polyaniline; The synthetic fiber is a mixture of one or more of polyester fiber, polypropylene fiber and polyester fiber, and the length of the synthetic fiber is 2-4 mm.

[0024] Step 2. Preliminarily mix the components weighed in step 1, and then add them together to the paste mixer. Accurately weigh 1000 parts by mass of lead powder through the lead powder delivery pipeline and add it to the paste mixer. Turn on and Paste machine, dry...

specific Embodiment 2

[0030] Such as figure 1 Shown is a schematic flow chart of a method for preparing the negative electrode paste of a power lead-acid battery according to the present invention. A kind of preparation method of power lead-acid storage battery negative lead paste of the present invention, comprises the following steps:

[0031] Step 1. Accurately weigh the following components by mass: 0.9 parts of synthetic fibers, 30 parts of barium sulfate, 1.5 parts of lignin, 2 parts of stannous sulfate, 0.5 parts of sodium lignosulfonate, and 5 parts of polyaniline; The synthetic fiber is a mixture of one or more of polyester fiber, polypropylene fiber and polyester fiber, and the length of the synthetic fiber is 2-4 mm.

[0032] Step 2. Preliminarily mix the components weighed in step 1, and then add them together to the paste mixer. Accurately weigh 1000 parts by mass of lead powder through the lead powder delivery pipeline and add it to the paste mixer. Turn on and Paste machine, dry st...

specific Embodiment 3

[0038] Such as figure 1 Shown is a schematic flow chart of a method for preparing the negative electrode paste of a power lead-acid battery according to the present invention. A kind of preparation method of power lead-acid storage battery negative lead paste of the present invention, comprises the following steps:

[0039] Step 1. Accurately weigh the following components by mass: 0.8 parts of synthetic fibers, 10 parts of barium sulfate, 3 parts of lignin, 0.5 parts of stannous sulfate, 3 parts of sodium lignosulfonate, and 20 parts of polyaniline; The synthetic fiber is a mixture of one or more of polyester fiber, polypropylene fiber and polyester fiber, and the length of the synthetic fiber is 2-4 mm.

[0040] Step 2. Preliminarily mix the components weighed in step 1, and then add them together to the paste mixer. Accurately weigh 1000 parts by mass of lead powder through the lead powder delivery pipeline and add it to the paste mixer. Turn on and Paste machine, dry sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
oxidation stateaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anode lead paste for a power lead-acid storage battery. The anode lead paste comprises the following constituents by mass: 1,000 parts of lead powder, 90-110 parts of deionized water, 70-100 parts of sulfuric acid solution with mass percentage of 50%, 0.6-0.9 part of synthetic fiber, 10-30 parts of barium sulfate, 0.5-3 parts of lignin, 0.5-2 parts of tin sulfate, 0.5-3 parts of lignin sulfonic acid and 5-20 parts of polyaniline. The invention simultaneously discloses a preparation method of the anode lead paste for the power lead-acid storage battery. By the anode lead paste for the power lead-acid storage battery and the preparation method thereof, the low-temperature performance of the power lead-acid storage battery can be effectively improved, and the problem of a short cycle life at a low-temperature state is solved.

Description

technical field [0001] The invention relates to a negative electrode paste of a power lead-acid battery and a preparation method thereof, belonging to the technical field of power lead-acid battery production and manufacturing. Background technique [0002] According to information released by the China Bicycle Association in 2012, the social ownership of electric vehicles in my country has increased to 142 million, and the number of electric vehicles per 100 households in developed cities has exceeded 30. The survey shows that more than 95% of electric vehicle power sources use lead-acid batteries . Lead-acid power batteries are regarded as the "heart" of electric vehicles and have become the focus of attention in the electric vehicle industry. There are problems with the safety and cost performance of lithium batteries. Power lead-acid batteries will remain the best for a long time in the future. The position of the power source. [0003] The power lead-acid battery is a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/57H01M10/06
CPCH01M4/364H01M4/57H01M10/06Y02E60/10
Inventor 舒红群赵古龙潘志刚夏冬念向九五
Owner ANHUI CHAOWEI POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap