Boron-containing cold-rolled enamel steel suitable for continuous annealing production and its manufacturing method

A manufacturing method and enamelled steel technology, applied in the field of boron-containing cold-rolled enameled steel and its manufacture, can solve the problems of less production practice of cold-rolled low-carbon enameled steel, etc., and achieve improved anti-scaling performance and strong enameled deformation resistance , The effect of small change in steel plate strength

Active Publication Date: 2017-09-26
NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the production practice of cold-rolled low-carbon enamelled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Boron-containing cold-rolled enamel steel suitable for continuous annealing production and its manufacturing method
  • Boron-containing cold-rolled enamel steel suitable for continuous annealing production and its manufacturing method
  • Boron-containing cold-rolled enamel steel suitable for continuous annealing production and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] The present invention will be further illustrated below in conjunction with examples. The purpose is only to better understand the content of the present invention, and the examples cited do not limit the scope of the claims of the present invention.

[0037] The chemical composition (mass percentage) of the examples and comparative examples of the present invention are shown in Table 1:

[0038] Table 1

[0039]

[0040] The main production process parameters of the embodiment of the invention and the comparative example are shown in Table 2:

[0041] Table 2

[0042]

[0043] The production steps of each embodiment and comparative example are as follows:

[0044] 1. Hot metal pretreatment, converter smelting, refining, and casting into billets;

[0045] 2. Slab heating, the heating temperature is controlled at 1200-1250℃;

[0046] 3. Hot continuous rolling and coiling, the final rolling temperature is controlled at 860-930℃, and the coiling temperature is controlled at 680-740℃;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a boron-containing cold-rolled enamel steel suitable for continuous annealing production and a manufacturing method thereof. The chemical composition mass percentage of the steel is: C 0.03-0.05%; Si≤0.02%; Mn 0.20-0.40%; P≤0.020% ; S 0.020‑0.035%; Als 0.020‑0.07%; B 0.0010‑0.0020%; N 0.0020‑0.0060%; the balance is Fe and inevitable impurities. It can be used for thin-gauge water heater liner and decorative panels for subways and tunnels, yield strength 200-240MPa, tensile strength 290-340MPa, elongation 38-44%, hardening exponent n value greater than 0.20, average plastic strain ratio rm value greater than 1.6 , The hydrogen lag time of 1mm thick steel plate is more than 50min, no scale explosion occurs after enamel, and the enamel adhesion performance reaches the national standard.

Description

technical field [0001] The invention relates to enamelled steel and its manufacturing process, in particular to a boron-containing cold-rolled enamelled steel suitable for continuous annealing production and its manufacturing method. The steel can be applied to inner tanks of thin water heaters and decorative panels of subways and tunnels. Background technique [0002] Enamel steel combines the inherent strength, toughness and ease of processing of steel materials with the advantages of corrosion resistance and easy decoration of ceramic materials, and is widely used in light industry, household appliances, chemical industry, construction and other industries. [0003] In the field of home appliances and construction, the requirements for the deep drawing performance of enamelled steel are not high, but the requirements for strength and resistance to enamel deformation are relatively high. Since the enamelled steel used for the water heater inner tank and the enameled plate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/06C21D8/02
Inventor 董福涛薛飞杜林秀刘相华
Owner NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap