Thin slab layer for formation of enhanced honeycomb structure and preparation method of honeycomb structure

A honeycomb structure and reinforced technology is applied in the field of preparation of thin plate layers and honeycomb structures. cost effect

Active Publication Date: 2016-02-03
北京金轮沃德科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dimensional accuracy of the formed corrugated sheet material is high, so the width of the formed sheet material is generally within 300mm, while the width of the stretched sheet material is generally 900mm. The process of forming / coating adhesive in the manufacturing process of the forming method is for To ensure dimensional accuracy and reduce the amount of springback after forming thin plate materials, the speed is generally within 3m / min, while the speed of stretching method can reach more than 36m / min, so the forming method is very efficient in manufacturing reinforced aramid paper honeycomb structure Low, and the forming method to manufacture reinforced honeycomb is basically not suitable for difficult-to-form materials such as aramid paper, and the materials used have a narrow range of application. Therefore, it is necessary to provide a new manufacturing method with high manufacturing efficiency and a wide range of material applications. Enables Fabrication of Enhanced Honeycomb Structures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thin slab layer for formation of enhanced honeycomb structure and preparation method of honeycomb structure
  • Thin slab layer for formation of enhanced honeycomb structure and preparation method of honeycomb structure
  • Thin slab layer for formation of enhanced honeycomb structure and preparation method of honeycomb structure

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] In a further embodiment of the present invention, a method for preparing a sheet layer 20 for forming a reinforced honeycomb structure is provided, the method comprising the following steps:

[0057] (1), reinforcement layer 12,14,16 comprises upper surface and lower surface, all can be provided with adhesive 19 on upper surface and lower surface of reinforcement layer 12,14,16, each reinforcement layer 12,14,16 The width in the width direction is set to 3 unit wall widths, the adhesive 19 is arranged on the same side in the width direction of the reinforcing layers 12, 14, 16, and the width of the adhesive 19 is 1 unit wall width;

[0058] (2), at least three layers of sheet materials 11, 13, 15 are arranged vertically from top to bottom;

[0059] (3), at least two strengthening layers 12, 14, 16 in step (1) are arranged between the adjacent thin plate materials 11, 13, 15 in step (2), and each adjacent sheet on the same horizontal plane Step (1) in the strengthening ...

Embodiment 1

[0085] A thin layer for forming a reinforced aramid paper honeycomb structure and a method for preparing a reinforced aramid paper honeycomb structure

[0086] The materials and process conditions used are:

[0087] Both the sheet material and the strengthening layer are DuPont T412 type aramid paper with a thickness of 0.10mm;

[0088] The lines of the adhesive on the sheet material are coated with a T450-1 laboratory gravure coater; the width of the adhesive line is 5mm, the distance between the adhesive lines is 15mm, and the amount of adhesive is 1.5g / m 2 ;

[0089] The reinforcement layer is cut from a thin plate material coated with adhesive lines through a wallpaper knife. The width of the cut reinforcement layer is 15mm, and the adhesive lines are located at the edge of the reinforcement layer;

[0090] The adhesive is J-80B Nomex paper honeycomb sandwich adhesive developed by Heilongjiang Petrochemical Research Institute;

[0091] The resin is phenolic resin, whi...

Embodiment 2

[0104] A kind of reinforced polyimide paper honeycomb structure veneer layer and the preparation method of reinforced polyimide paper honeycomb used materials and process conditions are:

[0105] The sheet material and reinforcement layer are all polyimide paper with a thickness of 0.10mm from China Changchun Gaoqi Polyimide Material Co., Ltd.;

[0106] The lines of the adhesive on the sheet material are coated with a T450-1 laboratory gravure coater; the width of the adhesive line is 3mm, the distance between the adhesive lines is 9mm, and the amount of adhesive is 1.5g / m 2 ;

[0107] The reinforcement layer is cut from a sheet material coated with adhesive lines through a wallpaper knife. The width of the cut reinforcement layer is 9 mm, and the adhesive lines are located at the edge of the reinforcement layer;

[0108] The adhesive is J-80B Nomex paper honeycomb sandwich adhesive developed by Heilongjiang Petrochemical Research Institute;

[0109]The resin is GP445d05 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a thin slab layer for formation of an enhanced honeycomb structure and a preparation method of the honeycomb structure. The thin slab layer for formation of the enhanced honeycomb structure and the preparation method of the honeycomb structure have the following beneficial effects: the problem that an enhanced honeycomb structure can only be manufactured by a forming method but cannot be manufactured by a tension method in the prior art is solved; a thin slab material at cell gluing positions in the forming-mode manufacturing is replaced with a strengthening layer of three cell wall width, and the position of binder line is changed between the thin slab material and the strengthening layer so as to realize tension-mode manufacturing; and materials which are not easy to form, such as aromatic polyamide paper, can be used to make the enhanced honeycomb structure, so as to expand the material application range and reduce manufacturing cost. Strength of the honeycomb structure obtained by the preparation method is similar to strength of a honeycomb structure prepared by a conventional forming method. The preparation method has high manufacturing efficiency.

Description

technical field [0001] The invention belongs to the technical field of honeycomb structure materials, in particular to a thin plate layer for forming a reinforced honeycomb structure and a preparation method of the honeycomb structure. Background technique [0002] The honeycomb structure is a series of hexagonal, quadrilateral and other shapes of porous solid materials made of metal materials, glass fibers or composite materials. The honeycomb structure has excellent properties such as light weight, sound insulation, fire prevention, non-fragile, strong rigidity, and environmental protection. , Widely used in building curtain walls and indoor and outdoor decoration, luxury car and ship interior decoration, high-speed trains, aerospace and aviation, etc. Due to the unique advantages of the honeycomb structure, the honeycomb has been developed in the long run. [0003] With the development of honeycomb technology, there are more and more types of honeycomb. The main constitue...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B3/12B32B7/12B32B37/12B32B27/28B32B27/34B32B38/00
CPCB32B3/12B32B7/12B32B27/281B32B27/34B32B37/12B32B38/0012B32B2038/0028B32B2250/03B32B2305/024B32B2377/00B32B2379/08
Inventor 杨艳黄静波
Owner 北京金轮沃德科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com