A controllable substance-doped strontium calcium phosphate powder and its preparation method

A technology of strontium calcium phosphate and powder, which is applied in the field of controllable substance-doped strontium calcium phosphate powder and its preparation, can solve the problems of difficult control of two-phase components and proportions, strict control of sintering temperature, and appearance of impurity phases, and achieve Improves the effect of osteoinductive properties and bioactivity

Active Publication Date: 2018-06-19
SOUTH CHINA UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still relatively few studies on the effect of Sr doping on the phase composition of HA and β-TCP in BCP ceramics and the phase regulation process
The existing BCP ceramics obtained according to the stoichiometric ratio method or by controlling the degree of calcium deficiency of the precursor and the sintering temperature are difficult to control the two-phase composition and ratio, and even impurity phases appear, and the sintering temperature control is also relatively strict

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A controllable substance-doped strontium calcium phosphate powder and its preparation method
  • A controllable substance-doped strontium calcium phosphate powder and its preparation method
  • A controllable substance-doped strontium calcium phosphate powder and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Prepare 0.5mol / L Ca(NO 3 ) 2 4H 2 O solution, 0.5mol / L Sr(NO 3 ) 2 solution and 0.25mol / L (NH 4 ) 3 PO 4 ·3H 2 O solution, as calcium source, strontium source and phosphorus source. According to the molar ratio of (Ca+Sr) / P=1.67, a certain amount of Ca(NO 3 ) 2 4H 2 O and Sr(NO 3 ) 2 After the solution is mixed, use concentrated ammonia water to adjust the pH of the solution to be greater than 11. After vigorously stirring at 30°C, add polyethylene glycol (molecular weight: 6000) dispersant, and stir for 30 minutes to obtain a mixed solution containing calcium source and strontium source.

[0028] (2) At the same time adjust with concentrated ammonia water (NH 4 ) 3 PO 4 ·3H 2 The pH value of the O solution is greater than 10 to obtain a solution containing a phosphorus source; after controlling the dropping rate to 4mL / min with a peristaltic pump, slowly drop the solution containing a phosphorus source into the mixed solution containing a calcium so...

Embodiment 2

[0036] (1) Prepare 0.5mol / L Ca(NO 3 ) 2 4H 2 O solution, 0.5mol / L Sr(NO 3 ) 2 solution and 0.25mol / L (NH 4 ) 3 PO 4 ·3H 2 O solution, as calcium source, strontium source and phosphorus source. According to the molar ratio of (Ca+Sr) / P=1.67, a certain amount of Ca(NO 3 ) 2 4H 2 O and Sr(NO 3 ) 2 After the solution is mixed, use concentrated ammonia water to adjust the pH of the solution to be greater than 11. After vigorously stirring at 30°C, add polyethylene glycol (molecular weight: 6000) dispersant, and stir for 30 minutes to obtain a mixed solution containing calcium source and strontium source.

[0037] (2) At the same time adjust with concentrated ammonia water (NH 4 ) 3 PO 4 ·3H 2 The pH value of the O solution is greater than 10 to obtain a solution containing a phosphorus source; after controlling the dropping rate to 4mL / min with a peristaltic pump, slowly drop the solution containing a phosphorus source into the mixed solution containing a calcium so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of biomedical materials and discloses controllable-phase strontium-doped calcium phosphate powder and a preparing method thereof. The preparing method comprises the steps of adding a (NH4)3PO4.3H2O solution to a Ca(NO3)2.4H2O and (NH4)3PO4.3H2O mixing solution dropwise for reaction according to the molar ratio of (Ca+Sr) / P=1.67, conducting centrifugal washing and drying on the reaction product, and conducting grinding to obtain strontium-doped calcium phosphate precursor powder; conducting heat preservation sintering on the strontium-doped calcium phosphate precursor powder at 900-1200 DEG C, and obtaining the controllable-phase strontium-doped calcium phosphate powder after cooling. Strontium-doped calcium phosphate biphase powder with different HA and beta-TCP proportions can be prepared in a controllable mode by adjusting the strontium doping amount, and higher biological activity and broader application prospects are realized compared with traditional calcium phosphate powder.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, and in particular relates to a controllable substance phase-doped strontium calcium phosphate powder and a preparation method thereof. Background technique [0002] Calcium phosphate biphasic ceramics (BCP) have the high strength, high bioactivity, stability of HA (hydroxyapatite) and the absorption and degradation characteristics of β-TCP. They are an important class of bone repair materials and have been widely studied and applied. At present, the BCP preparation methods mainly include: ①preparation of calcium-deficient apatite by wet method, and then sintering; ②solid-state reaction method; ③direct mechanical mixing of pure HA and pure β-TCP in a certain proportion. The mechanical mixing method is not easy to obtain nano-sized HA and β-TCP powder, and the uniformity of the dual-phase powder is not good enough; the solid-state reaction method has disadvantages such as low efficienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/04A61L27/12A61L27/54
CPCA61L27/047A61L27/12A61L27/54
Inventor 邓春林何丽泳
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com