Common high-solid-content medium temperature pitch and preparing method thereof

A high-solid content, medium-temperature technology, applied in building thermal insulation materials, building components, buildings, etc., can solve the problems of asphalt aging, the advent of technical solutions, and aging, and achieve the effects of reducing aging, wide construction temperature range, and reducing physical injuries.

Active Publication Date: 2016-06-15
WUHAN CHENGSHITONG ENVIRONMENTAL ASPHALT ENG CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 2. Aging during transportation, storage and heating
[0014] How to prevent the aging of asphalt during construction has always been a difficul

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Common high-solid-content medium temperature pitch and preparing method thereof
  • Common high-solid-content medium temperature pitch and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The equipment and process of the present invention will be further described in detail below in conjunction with specific examples.

[0033] The present invention designs a formula and preparation method of ordinary medium-temperature asphalt with high solid content (solid content as high as 75%), which can widen the temperature range of asphalt construction and can be constructed under climatic conditions below 10°C; compared The construction temperature of the modified asphalt in the prior art cannot be lower than 10°C, which can prolong the number of working days per year by 60 days.

[0034] The ordinary medium-temperature asphalt with high solid content is composed of the following components in parts by mass: 75-82 parts of base asphalt, 1-3 parts of ordinary medium-temperature modifier, and 16-23 parts of water.

[0035] Described common middle temperature modifier is made up of following components by mass parts:

[0036] 5-10 parts of 18 / 16 tertiary amine;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses common high-solid-content medium temperature pitch and a preparing method thereof. The common high-solid-content medium temperature pitch comprises 75-82 parts of matrix pitch, 1-3 parts of common medium-temperature modifying agent and 16-23 parts of water. The common medium-temperature modifying agent comprises, by mass, 5-10 parts of 18/16 tertiary amine, 5-12 parts of cationic additive, 1-5 parts of methyl alcohol, 40-50 parts of emulsifying agent, 1-3 parts of calcium chloride and 5-20 parts of deionized water, wherein the cationic additive is selected from 3-chlorine-2-hydroxypropyl-trimethylammonium chloride and trimethyl-dodecylammonium chloride; the emulsifying agent is selected from styrene-butadiene-styrene, butadiene styrene rubber, polyethylene, acrylonitrile-butadiene-styrene copolymer and high-polymer polypropylene and polystyrene. The pitch prepared with the method is wide in construction temperature range, construction can be carried out under the weather condition of being higher than -5 DEG C, and the requirement of road maintenance at the low temperature is met.

Description

technical field [0001] The invention relates to the preparation technology of asphalt in the field of road engineering, in particular to a common medium-temperature asphalt with high solid content, and also relates to a preparation method of the common medium-temperature asphalt with high solid content. Background technique [0002] Base asphalt is used to produce modified asphalt, which is modified by adding asphalt modifier. If it is petroleum asphalt obtained by exploiting and refining oil, it is also the base petroleum asphalt. For example, specifically, No. 70 Grade A asphalt is a common paving material. No. 70 A-grade asphalt is a natural substance extracted from petroleum. It is heated and mixed with aggregate to form asphalt mixture during construction. During construction, the heating temperature of No. 70 A-grade asphalt is 155-165°C. Asphalt will continue to age when heated for a long time, and it will begin to age when the temperature reaches 100°C. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L9/06C08L53/02C08L55/02C08L23/06C08L23/12C08L25/06C08K13/02C08K5/17C08K5/19C08K3/16
CPCC08L95/005C08L2205/03C08L2205/035C08L2555/84C08L2555/86C08L9/06C08L53/02C08L23/06C08K13/02C08K5/17C08K5/19C08K2003/162C08L55/02C08L25/06C08L23/12
Inventor 陈绍平
Owner WUHAN CHENGSHITONG ENVIRONMENTAL ASPHALT ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap