Ultrasonic transverse and longitudinal section element-separating detection method for stainless steel and nickel-based steel weld joint

A technology of ultrasonic testing and stainless steel, which is applied in the analysis of solids using sonic/ultrasonic/infrasonic waves, and can solve problems such as difficulty in ultrasonic testing of welds

Active Publication Date: 2016-06-29
SHANGHAI SHIPBUILDING TECH RES INST +1
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the interface of fusion lines or columnar grains can produce irregular reflections and mode conversions, and sometimes cannot even penetrate the weld metal, making ultrasonic inspection of such welds difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrasonic transverse and longitudinal section element-separating detection method for stainless steel and nickel-based steel weld joint
  • Ultrasonic transverse and longitudinal section element-separating detection method for stainless steel and nickel-based steel weld joint
  • Ultrasonic transverse and longitudinal section element-separating detection method for stainless steel and nickel-based steel weld joint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] In order to make the technical means, creative features, goals and effects achieved by the present invention easy to understand, the present invention will be further described below in conjunction with specific illustrations.

[0039] A kind of stainless steel, nickel base steel welding seam ultrasonic vertical and horizontal plane sub-element detection method of the present invention, comprises the following steps:

[0040] Step S1, see figure 1 , in the base metal of stainless steel and nickel-based steel, establish a series of standard reflectors with different depths that do not interfere with each other for ultrasonic testing (long horizontal holes Φ3*40mm are optional), and use this to establish the DAC curve. It should be noted that the double When the crystal angle probe detects standard reflectors, the peak wave drop is not greater than 6dB;

[0041] Step S2, see figure 2 , make the same welding seam comparison test plate as the on-site welding process. Gen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ultrasonic transverse and longitudinal section element-separating detection method for a stainless steel and nickel-based steel weld joint. According to the method, a scanning zone is divided into a plurality of same-size cross-sectional area elements along a scanning longitudinal section of a probe according to a matrix, the reason and differentiation degree of ultrasonic beam change during ultrasonic detection of the stainless steel and nickel-based steel weld joint under the same type of welding process conditions are found by conducting relative quantification and orientation and recording and analysis on standard reflector echoes in the different cross-sectional area elements, further more accurate qualitative and quantitative analysis is conducted on flaw wave echoes during the ultrasonic detection, the ultrasonic detection reliability of the weld joint is improved, and the safe usage of the weld joint is guaranteed.

Description

technical field [0001] The invention relates to the technical field of steel weld detection technology, in particular to an ultrasonic vertical and horizontal plane component detection method for stainless steel and nickel-based steel welds used in pressure vessels, pressure pipes and structural parts, which is suitable for agriculture, industry, national defense, and ships. Industries and applications where stainless steel and nickel-based alloy steel welds are used, such as electric power, etc. Background technique [0002] Stainless steel is often divided into martensitic steel, ferritic steel, austenitic steel, austenitic-ferritic (duplex) stainless steel and precipitation hardening stainless steel according to the organizational state. Among them, stainless steel and nickel-based steel are widely used. It is used in materials with high temperature resistance, low temperature resistance and corrosion resistance. The working conditions of these materials are relatively ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N29/07
CPCG01N29/07
Inventor 陆雷俊
Owner SHANGHAI SHIPBUILDING TECH RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products