A new environmentally friendly synthetic slagging material
A technology of slagging and environmental protection, which is applied in the field of steelmaking and refining, can solve the problems of insufficient slagging capacity of the converter, failure to achieve rapid slagging, slow slagging speed, etc., and achieve considerable benefits, superior slagging performance, and less slag volume Effect
Active Publication Date: 2017-09-15
山东济钢泰航合金有限公司
View PDF1 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The disadvantage is that the content of MnO is too high, while the content of FeO most needed for CaO and MgO melting is too low, resulting in slow slagging speed and high cost, which does not meet the conditions required for rapid slagging in the early stage of the converter
Also in the article "Application of Depleted Manganese Ore in Converter Steelmaking Process" in "Steelmaking", Volume 20, No. 2, February 2004, only MnO of depleted manganese ore was used, which increased the Mn content at the end of steelmaking, but did not completely Solve the problem of insufficient slag removal capacity in the early stage of converter
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] Formula: The parts by weight of raw materials are as follows: CaO: 12 parts, aluminum ash powder: 15 parts, SiO 2 : 72 parts, MnO: 2 parts, FeO: 9 parts, yttrium oxide Y 2 o 3 : 4.5 servings.
[0032] Preparation:
[0033] 1) crushing aluminum slag and ball milling into powder to obtain aluminum ash powder;
[0034] 2) Add other raw materials and mix well, that is.
Embodiment 2
[0036] Formula: The parts by weight of raw materials are as follows: CaO: 11 parts, aluminum ash powder: 5 parts, SiO 2 : 70 parts, MnO: 1 part, FeO: 8 parts, yttrium oxide Y 2 o 3 : 2 servings.
[0037] The preparation method is the same as in Example 1.
Embodiment 3
[0039] Formula: The parts by weight of raw materials are as follows: CaO: 14 parts, aluminum ash powder: 25 parts, SiO 2 : 73 parts, MnO: 2 parts, FeO: 10 parts, yttrium oxide Y 2 o 3 : 5 servings.
[0040] The preparation method is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides a novel environment-friendly synthetic slag forming material which comprises the following raw material components in parts by weight: 11-14 parts of CaO, 5-25 parts of aluminum ash powder, 70-73 parts of SiO2, 1-2 parts of MnO, 8-10 parts of FeO and 2-5 parts of Y2O3. The novel environmental-friendly synthetic slag forming material is environment-friendly, superior in slag forming performance, and wide in raw material sources, belongs to a resource recycling material, is low in pollution on molten steel during the steel-making using process, and small in generated slag quantity, can remarkably improve the comprehensive performance of a steel-making slag system, and improves the quality of molten steel. The novel environment-friendly synthetic slag forming material, namely a slag former, belongs to comprehensive utilization of industrial wastes, and is reliable in process, low in cost, and profitable.
Description
technical field [0001] The invention belongs to the fields of LF / VOD / VD steelmaking and refining, and particularly relates to a novel environment-friendly synthetic slagging material. Background technique [0002] Slagging is an essential part of the steelmaking and ironmaking process. Steelmaking and ironmaking need to reduce the impurities in the steel. These impurities are separated and enter the slag. Because the slag has a light specific gravity and floats on the molten steel, it is easier to remove. In addition, the slag can also protect the molten steel from direct contact with the atmosphere. Slagging is the addition of steelmaking substances called slagging agents, such as calcium fluoride or calcium oxide, during the steelmaking process to form slag. [0003] Under the conditions of the existing steelmaking process, materials such as lime (calcium oxide) and fluorite (calcium fluoride) are mainly used for slagging. In traditional slag-making materials, the lime ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/36C21C7/076
CPCC21C5/36C21C7/076Y02P10/20
Inventor 王铮李传承张海涛王磊朱慧
Owner 山东济钢泰航合金有限公司