EVA composite adhesive film used for photovoltaic packaging and having anti-PID performance

A composite adhesive, photovoltaic technology, applied in the direction of film/sheet adhesives, adhesives, adhesive types, etc., can solve the problems of photovoltaic module products failing to pass PID test, battery power reduction, etc., to achieve good PID performance , the effect of improving service life and improving efficiency

Inactive Publication Date: 2016-08-03
SAITERUI SOLAR ENERGY SUZHOU CO LTD
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, although some progress has been made in the research of photovoltaic EVA packaging film for anti-PID technology, it requires simultaneous PID treatment at the solar cell end, including UV lamp, laughing gas, ozone and other oxidation treatments on the solar cell, and this After treatment, the power of the cell will be reduced by about 1%; if the anti-PIDEVA packaging film is used with the cell without PID treatment, the photovoltaic module produced will not pass the PID test

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • EVA composite adhesive film used for photovoltaic packaging and having anti-PID performance
  • EVA composite adhesive film used for photovoltaic packaging and having anti-PID performance
  • EVA composite adhesive film used for photovoltaic packaging and having anti-PID performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] combined with figure 1 As shown, the present embodiment provides a kind of EVA composite adhesive film with anti-PID performance for photovoltaic encapsulation, which comprises an anti-ultraviolet EVA adhesive film layer 1, a transparent EVA adhesive film layer 2 and a white reflective EVA adhesive film layer 3 successively, wherein, The transparent EVA film layer 2 and the side of the reflective EVA film layer 3 are fixed to form a bag-shaped structure with one side opening, the solar cells are placed in the bag-shaped structure, and the ultraviolet-proof EVA film layer 1 is arranged on the front side of the battery sheet; the surface of the transparent EVA film layer 2 opposite to the reflective EVA film layer 3 is provided with patterns.

[0046]Wherein, the VA content of the anti-ultraviolet EVA film layer is 20%, the VA content of the transparent EVA film layer is 22%, and the VA content of the white reflective EVA film layer is 24%.

[0047] The thicknesses of th...

Embodiment 2

[0062] combined with figure 1 As shown, the present embodiment provides a kind of EVA composite adhesive film for photovoltaic encapsulation with anti-PID performance, it comprises anti-ultraviolet EVA adhesive film layer 1, transparent EVA adhesive film layer 2 and white reflective EVA adhesive film layer 3 successively, wherein, The transparent EVA film layer 2 and the side of the white reflective EVA film layer 3 are fixed to form a bag-like structure with one side opening, the solar cells are placed in the bag-like structure, and the ultraviolet-proof EVA film Layer 1 is arranged on the front side of the battery sheet; the surface of the transparent EVA film layer 2 opposite to the white reflective EVA film layer 3 is provided with patterns.

[0063] Wherein, the VA content of the anti-ultraviolet EVA film layer is 22%, the VA content of the transparent EVA film layer is 24%, and the VA content of the white reflective EVA film layer is 26%.

[0064] The thicknesses of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an EVA composite adhesive film for photovoltaic packaging with anti-PID performance, which includes: 0.05-7% of acrylamide crosslinking agent; 0.05-3% of co-crosslinking agent; 0.02-0.5% of ultraviolet light stabilizer; Auxiliary antioxidant 0.02-0.5%; tackifier 0.02-0.5%; conventional additives and the balance EVA. The EVA composite adhesive film for photovoltaic encapsulation with anti-PID performance provided by the present invention aims to make the EVA composite adhesive film possess high anti-PID performance through the adjustment of EVA formula and the improvement of structure.

Description

technical field [0001] The invention relates to an EVA composite adhesive film, in particular to an EVA composite adhesive film for photovoltaic packaging with anti-PID performance. Background technique [0002] Solar energy is a green, non-polluting and inexhaustible energy source. Compared with other energy sources, solar energy is ubiquitous and can be used locally in most areas of the earth. Therefore, in the past ten years, the solar energy industry It has become the focus of the development of countries all over the world. The utilization of solar energy is mainly to convert it into electrical energy through solar panels, and then do other purposes, such as solar air conditioners, street lamps, electric vehicles and so on. Since the working environment of solar cell modules is mainly outdoors, and cells for photovoltaic modules cannot be directly exposed to natural conditions such as sunlight and rain, it is necessary to seal them. [0003] U.S. Patent No. 2001 / 00452...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/00C09J131/04C09J11/06
CPCC09J7/00C08K5/098C08K5/20C08K5/3492C08K5/526C08K5/5425C08L2201/08C08L2203/16C08L2203/20C09J11/06C09J131/04
Inventor 杨同禄
Owner SAITERUI SOLAR ENERGY SUZHOU CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap