Antirust air cushion belt conveyor

A technology of belt conveyor and air cushion, which is applied in the direction of conveyor, transportation and packaging, metal material coating technology, etc., can solve the problem of rust-prone, anti-rust air cushion belt conveyor collapse, and accelerate the production of air cushion belt conveyor Rust speed etc.

Inactive Publication Date: 2016-08-24
WUHU ADER CONVEYOR MACHINERY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main structure of the air-cushion belt conveyor is made of metal parts. Although the metal parts have excellent mechanical properties, they are extremely prone to rust after a long period of use, especially raw materials such as cement and fly ash can further accelerate the speed of the air-cushion belt conveyor. The rusting speed of the conveyor leads to the decline of the mechanical properties of the air cushion belt conveyor, and sometimes even causes the collapse of the antirust air cushion belt conveyor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1) Mix pinitol, Gentiana chinensis, Yaxiang, aconite, hand ginseng, notoginseng, horsetail flower, Shijiao grass and organic solvent (carbon tetrachloride) according to 84:66:48:69:48:116:49 : 29: 1000 by weight and mixed, then decocted at 115°C for 4 hours, and then filtered to obtain the filtrate;

[0036] 2) At 25°C, α-pinene, kaolin, simethicone, potassium fluozirconate, oxalic acid, sodium molybdate, morpholine, tolyltriazole, polymer film-forming agent (carboxymethyl starch) 1. Surfactant (dioctyl sodium sulfosuccinate) and filtrate are mixed according to the weight ratio of 100:62:125:22:221:28:19:11:5:6:104 to form a rust inhibitor;

[0037] 3) Soak the metal body in anti-rust agent at 50°C for 10 hours, then take it out and dry it at 120°C for 6 hours to obtain anti-rust air cushion belt conveyor A1.

Embodiment 2

[0039] 1) Combine pinitol, Gentiana chinensis, Yaxiang, aconite, hand ginseng, notoginseng, horsetail flower, Shijiao grass and organic solvent (ethanol) according to 78:55:40:65:42:114:45:25: Mixed at a weight ratio of 1000, then decocted at 110°C for 3 hours, and then filtered to obtain the filtrate;

[0040] 2) At 25°C, mix α-pinene, kaolin, simethicone, potassium fluorozirconate, oxalic acid, sodium molybdate, morpholine, tolyltriazole, polymer film-forming agent (polyethylene glycol) 1. Surfactant (sodium dodecylbenzene sulfonate) and filtrate are mixed according to the weight ratio of 100:50:120:14:200:21:17:9:3:5:90 to form a rust inhibitor;

[0041] 3) Soak the metal body in anti-rust agent at 40°C for 8 hours, then take it out and dry it at 115°C for 5 hours to obtain anti-rust air cushion belt conveyor A2.

Embodiment 3

[0043] 1) Combine pinitol, Gentiana chinensis, Yaxiang, aconite, hand ginseng, notoginseng, horsetail flower, Shijiao grass and organic solvent (toluene) according to 94:76:56:78:58:126:66:37: Mixed at a weight ratio of 1000, then decocted at 125°C for 5 hours, and then filtered to obtain the filtrate;

[0044]2) At 25°C, mix α-pinene, kaolin, simethicone, potassium fluozirconate, oxalic acid, sodium molybdate, morpholine, tolyltriazole, polymer film-forming agent (polyvinyl alcohol), The surfactant (tetradecyl alcohol polyoxyethylene ether) and the filtrate are mixed according to the weight ratio of 100:72:135:32:241:36:25:15:7:8:114 to form a rust inhibitor;

[0045] 3) Soak the metal body in anti-rust agent at 60°C for 12 hours, and then take it out and dry it at 130°C for 7 hours to obtain anti-rust air cushion belt conveyor A3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antirust air cushion belt conveyor. The antirust air cushion belt conveyor is obtained by carrying out rust prevention treatment on a metal main body. A rust prevention treatment method comprises the following steps of: (1) putting Chinese herbal medicines in an organic solvent so as to decoct the Chinese herbal medicines, and then filtering to obtain filtrate; (2) mixing alpha-pinene, kaolin, dimethyl silicon oil, potassium fluorozirconate, oxalic acid, sodium molybdate, morpholine, tolyl triazole, a film-forming agent of high polymer and a surface active agent with the filtrate to form an antirust agent; and (3) putting the metal main body in the antirust ageng so as to soak the metal main body, then taking out the metal main body and drying the metal main body so as to obtain the antirust air cushion belt conveyor, wherein the Chinese herbal medicines are pinitol, large-leaved gentian, agilawood, monkshood, rhezoma gymnadeniae, gynura japonica, scouring rush flowers and herb of sessilefruit chinaure. The antirust air cushion belt conveyor has an excellent antirust property.

Description

technical field [0001] The invention relates to a conveying device, in particular to an antirust air cushion belt conveyor. Background technique [0002] Air-cushion belt conveyors are widely used in the transportation of industrial raw materials, such as cement, fly ash and other easily fluidized powder materials. The main structure of the air-cushion belt conveyor is made of metal parts. Although the metal parts have excellent mechanical properties, they are extremely prone to rust after a long period of use, especially raw materials such as cement and fly ash can further accelerate the speed of the air-cushion belt conveyor. The rusting speed of the conveyor leads to the decline of the mechanical properties of the air cushion belt conveyor, and sometimes even causes the collapse of the antirust air cushion belt conveyor. Contents of the invention [0003] An object of the present invention is to provide a rust-proof air-cushion belt conveyor having excellent rust-proof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/02C23F11/00B65G15/60
CPCC23C22/02B65G15/60C23F11/00
Inventor 贾真李开领周勇
Owner WUHU ADER CONVEYOR MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap