Rust-proof steel core rubber belt bucket elevator

A bucket elevator and belt technology, applied in the direction of metal material coating process, etc., can solve the problem of accelerating the rusting speed of steel core belt bucket elevator, the collapse of antirust steel core belt bucket elevator, and the steel core belt bucket Problems such as the decline in the mechanical performance of the type hoist

Inactive Publication Date: 2016-08-24
WUHU ADER CONVEYOR MACHINERY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main structure of the steel core belt bucket elevator is processed by metal parts. Although the metal parts have excellent mechanical properties, they are extremely easy to rust after a long period of use, especially cement, fly ash and other raw materials can further accelerate the steel The rusting speed of the core belt bucket elevator leads to the decline of the mechanical properties of the steel core belt bucket elevator, and sometimes even causes the collapse of the anti-rust steel core belt bucket elevator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1) Mix Aconitum Aconitum, Shuangpi, Jiangpi, Duheng, Tribulus, Shanbengzi, Shui Pinxia, ​​Shijiaocao and organic solvent (carbon tetrachloride) according to 121:67:46:68:48:118:49: 29:1000 by weight ratio, then decocted at 115°C for 4 hours, and then filtered to obtain the filtrate;

[0036] 2) At 25°C, α-pinene, diatomaceous earth, simethicone oil, potassium fluozirconate, fatty acid, sodium molybdate, morpholine, tolyltriazole, polymer film-forming agent (carboxymethyl Starch), surfactant (dioctyl sodium sulfosuccinate) and filtrate are mixed according to the weight ratio of 100:62:125:18:231:29:19:12:5:6:95 to form a rust inhibitor;

[0037] 3) Soak the metal body in anti-rust agent at 50°C for 10 hours, then take it out and dry it at 120°C for 6 hours to obtain anti-rust steel core belt bucket elevator A1.

Embodiment 2

[0039] 1) Combine Chuanwu, Shuangpi, Jiangpi, Duheng, Tribulus, Shanbengzi, Shuipinxia, ​​Shijiaocao and organic solvent (ethanol) according to the ratio of 114:64:40:65:42:110:45:25:1000 The weight ratio is mixed, then decocted at 110°C for 3h, and then filtered to get the filtrate;

[0040] 2) At 25°C, α-pinene, diatomaceous earth, simethicone oil, potassium fluorozirconate, fatty acid, sodium molybdate, morpholine, tolyltriazole, polymer film-forming agent (polyethylene glycol) Alcohol), surfactant (sodium dodecylbenzenesulfonate) and filtrate are mixed according to the weight ratio of 100:50:120:14:200:21:17:9:3:5:90 to form a rust inhibitor;

[0041] 3) Soak the metal body in anti-rust agent at 40°C for 8 hours, then take it out and dry it at 115°C for 5 hours to obtain anti-rust steel core belt bucket elevator A2.

Embodiment 3

[0043]1) Mix Aconitum Aconitum, Shuangpi, Jiangpi, Duheng, Tribulus, Shanbengzi, Shuipinxia, ​​Shijiaocao and organic solvent (toluene) according to the ratio of 125:73:56:78:58:123:66:37:1000 The weight ratio is mixed, then decocted at 125 ° C for 5 hours, and then filtered to get the filtrate;

[0044] 2) At 25°C, α-pinene, diatomaceous earth, simethicone oil, potassium fluorozirconate, fatty acid, sodium molybdate, morpholine, tolyltriazole, polymer film-forming agent (polyvinyl alcohol ), surfactant (tetradecyl alcohol polyoxyethylene ether) and filtrate are mixed according to the weight ratio of 100:72:135:32:241:36:25:15:7:8:108 to form a rust inhibitor;

[0045] 3) Soak the metal body in anti-rust agent at 60°C for 12 hours, then take it out and dry it at 130°C for 7 hours to obtain anti-rust steel core belt bucket elevator A3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rust-proof steel core rubber belt bucket elevator. The rust-proof steel core rubber belt bucket elevator is formed by carrying out rust-proof treatment on a metal body. A rust-proof treatment method comprises the steps that (1) Chinese herbal medicines are put into an organic solvent to be decocted, and then filter liquor is taken through filtering; (2) alpha-pinene, kieselguhr, simethicone, potassium fluozirconate, fatty acid, sodium molybdate, morpholine, tolyl triazole, a macromolecular film-forming agent, surfactant and the filter liquor are mixed to form a rust-proof agent; and (3) the metal body is put into the rust-proof agent to be soaked and then taken out to be dried to obtain the rust-proof steel core rubber belt bucket elevator, wherein the Chinese herbal medicines comprise radix aconiti, cortex mori radicis, ginger peels, wild ginger, caltrop, rhododendron simsii planch, rhizoma typhonii flagelliformis and beonninghausenia sessilicarpa. The rust-proof steel core rubber belt bucket elevator has the excellent rust-proof characteristic.

Description

technical field [0001] The invention relates to a conveying device, in particular to an antirust steel core belt bucket elevator. Background technique [0002] Steel belt bucket elevators are widely used in the transportation of industrial raw materials, such as cement, fly ash and other easily fluidized powder materials. The main structure of the steel core belt bucket elevator is processed by metal parts. Although the metal parts have excellent mechanical properties, they are extremely easy to rust after a long period of use, especially cement, fly ash and other raw materials can further accelerate the steel The rusting speed of the core belt bucket elevator leads to the decline of the mechanical properties of the steel core belt bucket elevator, and sometimes even causes the collapse of the anti-rust steel core belt bucket elevator. Contents of the invention [0003] The object of the present invention is to provide an antirust steel core belt bucket elevator which has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/02
CPCC23C22/02
Inventor 李开领贾真周勇
Owner WUHU ADER CONVEYOR MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap