Air-purifying high-strength three-dimensional solid wood composite board and preparation method thereof

A technology that purifies air and has a high structure. It is applied in chemical instruments and methods, separation methods, gas treatment, etc. It can solve problems such as mechanical performance degradation, rough appearance of composite materials, and mechanical performance degradation of plates, so as to improve structural stability and shape. Stability, reduce the concentration of TVOC pollutants, improve the effect of binding strength

Active Publication Date: 2018-09-14
SHENZHEN SONGBOYU TIMBERING
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the appearance of this composite material is relatively rough, and the large amount of carbon powder used leads to the decline of its mechanical properties, dull color, and stiff shape, which is difficult to compete with solid wood panels with natural wood grain
At the same time, the filling of activated carbon will lead to a decrease in the mechanical properties of the sheet, resulting in the product being easily deformed under stress

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Air-purifying high-strength three-dimensional solid wood composite board and preparation method thereof
  • Air-purifying high-strength three-dimensional solid wood composite board and preparation method thereof
  • Air-purifying high-strength three-dimensional solid wood composite board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment provides a kind of air-purifying type high structural strength three-dimensional solid wood composite board, such as figure 1 , including the hard base layer 1, the first tolerance layer group 2 and the second tolerance layer group 3 arranged on both sides of the hard base layer 1; the first tolerance layer group 2 and the second tolerance layer group 3 are respectively set There are 2 layers of flexible accommodation layers; it also includes a surface layer 4 arranged on the surface of the first accommodation layer group 2; the surface layer 4 is provided with decorative grooves 5 parallel to each other, and the bottom of the decorative grooves 5 is embedded in the first The accommodating layer group 2 also includes an adsorption layer group 6 arranged on one side of the hard base layer 1, and the adsorption layer group 6 includes an adsorption layer; the adsorption layer is provided with a number of adsorption holes.

[0047] Further, the adsorption la...

Embodiment 2

[0055] This embodiment provides a kind of air-purifying type high structural strength three-dimensional solid wood composite board, such as image 3 , including the hard base layer 1, the second tolerance layer group 2 and the second tolerance layer group 3 arranged on both sides of the hard base layer 1; the second tolerance layer group 2 and the second tolerance layer group 3 are respectively set There are 2 layers of flexible accommodation layers; it also includes a surface layer 4 arranged on the surface of the second accommodation layer group 2; the surface layer 4 is provided with decorative grooves 5 parallel to each other, and the bottom of the decorative grooves 5 is embedded in the second The accommodating layer group 2 also includes an adsorption layer group 6 arranged on one side of the hard base layer 1, and the adsorption layer group 6 includes an adsorption layer; the adsorption layer is provided with a number of adsorption holes.

[0056] Further, the adsorptio...

Embodiment 3

[0064] This embodiment provides a kind of air-purifying type high structural strength three-dimensional solid wood composite board, such as Figure 4, including the hard base layer 1, the second tolerance layer group 2 and the second tolerance layer group 3 arranged on both sides of the hard base layer 1; the second tolerance layer group 2 and the second tolerance layer group 3 are respectively set There is one layer of flexible tolerance layer; it also includes a surface layer 4 arranged on the surface of the second tolerance layer group 2; the surface layer 4 is provided with decorative grooves 5 parallel to each other, and the bottom of the decorative groove 5 is embedded in the second The accommodating layer group 2 also includes an adsorption layer group 6 arranged on both sides of the hard base layer 1, and the adsorption layer group 6 includes two adsorption layers; the adsorption layer is provided with a number of adsorption holes.

[0065] Further, the adsorption laye...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an air purifying type high-structural-strength and three-dimensional solid wood composite board and a manufacturing method thereof. Particularly, an adsorption layer set is arranged outside a core board. Adsorption holes are formed in the adsorption layer set, the adsorption layer set has high adsorption force on TVOC type pollutants in air due to large specific area, and therefore the concentration of the TVOC type pollutants in air can be reduced, and the function of purifying indoor air is achieved. Due to the arrangement of a core board layer, the mechanical performance of the solid wood board containing an adsorption layer is improved, the solid wood board is not likely to be damaged, the thickness of the adsorption layer can be further reduced, and the appearance of the manufactured board is improved. Deeper decoration groove lines can be formed on the board, and a more three-dimensional visual effect is obtained. White emulsion serves as a bonding agent of the air purifying type high-structural-strength and three-dimensional solid wood composite board, volatile toxic substances in the solid wood board are reduced, and the environment friendliness of the solid wood board is improved. The air purifying type high-structural-strength and three-dimensional solid wood composite board can be widely applied to the fields of home decoration, artwork processing, commercial place decoration, municipal construction and the like.

Description

technical field [0001] The invention relates to a solid wood board and a preparation method thereof, in particular to an air-purifying high structural strength three-dimensional solid wood composite board and a preparation method thereof. Background technique [0002] The solid wood boards for furniture decoration in the current market are made of veneer, natural veneer, core board and other multi-layer solid wood materials laminated in a certain order, glued and pressed. High strength and other advantages. With the acceleration of urbanization, air pollution in cities is becoming more and more serious, and air purification is an urgent problem for human beings to solve. Existing solid wood boards are often treated with various organic solvents during the manufacturing process, and formaldehyde and other pollutants are likely to remain in the finished products. During use, the residual pollutants will volatilize and pollute the indoor environment. damage to human health. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27D1/04B27D1/08B32B21/04B32B37/10B32B37/12B32B3/24B01D53/04
CPCB01D53/04B01D2253/102B01D2253/202B01D2257/708B27D1/04B27D1/08B32B3/266B32B21/04B32B37/10B32B37/12B32B2307/758B32B2309/12
Inventor 詹雄光颜宝娟罗俊光黄远林
Owner SHENZHEN SONGBOYU TIMBERING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com