Non-halogen flame-retardant polyethylene sheath insulating material and preparation method thereof

A flame retardant polyethylene and insulating material technology, applied in insulators, insulated conductors, insulated cables, etc., can solve problems such as large gaps, achieve high insulation resistance, improve thermal deformation resistance, and reduce quality.

Inactive Publication Date: 2016-11-09
浙江太湖远大新材料股份有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, in the industry, the temperature grade of 105°C and below can meet the requirements no matter whether XLPE, XLPVC or PVC is used. Above 150°C, the application of silicone rubber, fluoroplastics, polyimide and other varieties has also matured, but in the middle temperature grade (such as 125°C, 150°C) application development, there is a big gap with foreign countries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-halogen flame-retardant polyethylene sheath insulating material and preparation method thereof
  • Non-halogen flame-retardant polyethylene sheath insulating material and preparation method thereof
  • Non-halogen flame-retardant polyethylene sheath insulating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A halogen-free flame-retardant polyethylene sheath insulating material, which is prepared from the following components by weight percentage:

[0045]

[0046] and catalyst masterbatch;

[0047] Described catalyst masterbatch is made of following component:

[0048]

[0049] The two-step method for preparing the above-mentioned halogen-free flame-retardant polyethylene sheath insulating material mainly consists of two parts, one is the preparation of the catalyst masterbatch, and the other is the preparation of the finished product.

[0050] 1. Catalyst masterbatch preparation:

[0051] Stir the above materials in the mixer, first stir at low speed for 1 minute and then at high speed for 3 minutes, then release and pour into the hopper of the extruder (extruder temperature: 140-180°C), extrude through the twin-screw, and then pass through the cooling water tank for cooling , and then blown dry by a fan before cutting into pellets. The pellets are dried in a dryi...

Embodiment 2

[0061] A halogen-free flame-retardant polyethylene sheath insulating material, which is prepared from the following components by weight percentage:

[0062]

[0063] and catalyst masterbatch;

[0064] Described catalyst masterbatch is made of following component:

[0065]

[0066]

[0067] The insulating material mentioned above was prepared by the two-step method of Example 1.

Embodiment 3

[0069] A halogen-free flame-retardant polyethylene sheath insulating material, which is prepared from the following components by weight percentage:

[0070]

[0071] and catalyst masterbatch;

[0072] Described catalyst masterbatch is made of following component:

[0073]

[0074] The one-step method for preparing the above-mentioned halogen-free flame-retardant polyethylene sheath insulating material mainly consists of two parts, one is the preparation of the catalyst masterbatch, and the other is the preparation of the finished product.

[0075] 1) Catalyst masterbatch preparation: Stir the above catalyst masterbatch materials in a mixer, first stir at low speed for 1 minute, then stir at high speed for 3 minutes, then release and pour into the hopper of the extruder. After the screw is extruded, it is cooled by the cooling water tank, and then dried by the fan before being pelletized. The pellets are dried in the drying tower at 80°C for more than 2 hours, and then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of insulating materials, in particular to a non-halogen flame-retardant polyethylene sheath insulating material and a preparation method thereof. The non-halogen flame-retardant polyethylene sheath insulating material is prepared from components as follows: LLDPE-7042 (linear low density polyethylene-7042), LDPE (low-density polyethylene), a silane coupling agent, a cross-linking agent DCP, an antioxidant 300 and a catalyst masterbatch, wherein the catalyst masterbatch comprises components as follows: LLDPE-7042, LLDPE-8320, PP (polypropylene), an antioxidant 1010, an antioxidant DLTP, an antioxidant 1024, organic tin, a fluororubber masterbatch and a non-halogen intumescent flame retardant. The material is mainly applied to an insulating layer of a cable and is mainly used for replacing a current PVC (polyvinyl chloride) material, the insulating property of the material is superior to that of PVC, and the silane insulating material is non-toxic and harmless while PVC can release toxic and harmful gas when a wire is on fire caused by aging and the like.

Description

technical field [0001] The invention relates to the field of insulating materials, in particular to a halogen-free flame-retardant polyethylene sheath insulating material and a preparation method thereof. Background technique [0002] The types of polyolefins used in the cable industry mainly include PE, PP, EVA and EEA, etc. Among them, the relatively large amount and long application history are mainly PE, which include HDPE, MDPE, LDPE, LLDPE and cross-linked XLPE. Their application Needless to say. The current application and development trends of polyolefins in the industry mainly focus on the following aspects: [0003] (1) Serialization and perfection of halogen-free and low-smoke materials [0004] Halogen-free, low-smoke, flame-retardant cable materials have been developing rapidly in recent years, and thermoplastic materials that meet the requirements of the IEC92-359 standard have been more and more widely used. With the requirements of cables for oil platforms...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L23/12C08K5/00C08K5/14C08K5/54C08K5/134C08J3/22H01B3/44H01B7/295
CPCC08L23/06C08J3/226C08J2323/06C08J2423/08C08L2201/02C08L2201/08C08L2201/22C08L2203/202C08L2205/02C08L2205/025C08L2205/035C08L2207/066C08L2312/00H01B3/441H01B7/295C08L23/0815C08L23/12C08K5/00C08K5/14C08K5/54C08K5/1345
Inventor 赵勇俞丽琴蔡煜明李顺利郑颜
Owner 浙江太湖远大新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap