Frit used for producing Longquan celadon, Longquan celadon frit glaze and production method of frit glaze

A technology of frit glaze and Longquan porcelain clay, which is applied in the field of Longquan celadon glaze, can solve a large number of problems, achieve the effects of reducing manufacturing costs, improving suspension and coloring capabilities, and wide sources

Active Publication Date: 2016-12-07
LISHUI UNIV
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a frit for preparing Longquan celadon, which solves the problem that the existing frit needs to use a large amount of high-quality Longquan celadon raw materials, and needs to add colorants or other ceramic coloring chemical raw materials, making Longquan celadon The color of the porcelain glaze is more colorful

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A kind of Longquan celadon frit glaze of the present embodiment is prepared by the following method:

[0044] (1) Preparation of frit

[0045] The raw materials of the frit are mixed uniformly according to the following weight percentages:

[0046] Rare earth tailings 90%, Longquan china clay 2.5%, alumina powder 1.5%, kaolin 3%, yellow Glaze clay 1.5%, potassium feldspar 0.5%, quartz 0.5%, talc 0.5%;

[0047] After mixing evenly, use a high-temperature frit furnace to melt at 1300°C without stopping stirring; then, after water quenching, ball mill for 5 hours, and dry to obtain a frit;

[0048] (2) Preparation of glaze slurry

[0049] Mix the raw materials of the glaze according to the following weight percentages:

[0050] 90% of frit, 0.5% of lingen glaze clay, 1.2% of quartz, 0.3% of limestone, 5% of kaolin, 3% of purple gold clay;

[0051] After mixing evenly, perform ball milling for 5 hours according to the ratio of material: ball: water = 1:2:0.5, and add ...

Embodiment 2

[0059] A kind of Longquan celadon frit glaze of the present embodiment is prepared by the following method:

[0060] (1) Preparation of frit

[0061] The raw materials of the frit are mixed uniformly according to the following weight percentages:

[0062] Rare earth tailings 95%, Longquan china clay 1%, alumina powder 1%, kaolin 1%, yellow Glazed soil 1%, potassium feldspar 0.5%, talc 0.5%;

[0063] After mixing evenly, use a high-temperature frit furnace to melt at 1380 °C without stopping stirring; then, after water quenching, ball mill for 12 hours, and dry to obtain a frit;

[0064] (2) Preparation of glaze slurry

[0065] Mix the raw materials of the glaze according to the following weight percentages:

[0066] 70% of frit, 20% of lingen glaze clay, 2% of quartz, 1% of limestone, 4% of kaolin, 3% of purple gold clay;

[0067] After mixing evenly, perform ball milling for 20 hours according to the ratio of material: ball: water = 1:2:0.7, and add 0.5% methyl cellulos...

Embodiment 3

[0075] A kind of Longquan celadon frit glaze of the present embodiment is prepared by the following method:

[0076] (1) Preparation of frit

[0077] The raw materials of the frit are mixed uniformly according to the following weight percentages:

[0078] Rare earth tailings 80%, Longquan china clay 5%, alumina powder 3%, kaolin 5%, yellow Glazed soil 5%, potassium feldspar 1%, quartz 1%;

[0079] After mixing evenly, use a high-temperature frit furnace to melt at 1300°C without stopping stirring; then, after water quenching, ball mill for 5 hours, and dry to obtain a frit;

[0080] (2) Preparation of glaze slurry

[0081] Mix the raw materials of the glaze according to the following weight percentages:

[0082] 95% frit, 1% lingen glaze clay, 1% limestone, 2% kaolin, 1% purple gold clay;

[0083] After mixing evenly, perform ball milling for 5 hours according to the ratio of material: ball: water = 1:2:0.5, and add 0.5% polypropylene alcohol as suspending agent during t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a frit used for producing Longquan celadon, a Longquan celadon frit glaze and a production method of the frit glaze. Raw materials of the frit comprise, by weight, 45-95% of rare earth tailings, 1-30% of Longquan porcelain clay, 1-25% of alumina powder, 1-15% of kaolin, 1-30% of yellow glaze soil, 0-25% of potash feldspar, 0-20% of quartz and 0-10% of talcum. The rare earth tailings are adopted as a main raw material of the frit, so the recycling of the rare earth tailings is realized, and the use amounts of other routine Longquan celadon raw materials are greatly reduced; and trace rare earth elements in the rare earth tailings have an obvious color development promoting effect on the celadon glaze, so extra addition of a coloring agent or a ceramic coloring chemical engineering raw material to the glaze is prevented, thereby the manufacturing cost of the Longquan celadon frit glaze is reduced, the color appearance of the glaze is stable, and industrial large-scale production is facilitated.

Description

technical field [0001] The invention relates to a Longquan celadon glaze, in particular to a frit for preparing Longquan celadon, a Longquan celadon frit glaze and a preparation method of the frit glaze. Background technique [0002] my country has rich reserves of rare earth ore resources, but due to the low grade of rare earth ores, rare earth ores will produce rare earth tailings after being extracted and utilized. At present, the treatment methods of rare earth tailings are mainly stacking or landfilling. This treatment method not only occupies a large area and wastes a lot of land resources; it also causes serious pollution to water and soil resources, destroys the ecological balance, and hinders the sustainable development of the economy. develop. Therefore, the resource reuse of rare earth tailings is an important way to realize the sustainable development of mineral resources. This is not only the strategic demand for the development of my country's rare earth indus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/02C03C8/14C04B33/24C04B33/34C04B41/86
CPCC03C8/02C03C8/14C04B33/24C04B33/34C04B41/5022C04B41/86
Inventor 施群周灵
Owner LISHUI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka