Lightweight soundproof thermal insulation wall brick and preparation method thereof

A wall brick, lightweight technology, applied in the field of building filling materials, can solve the problems of high density and low strength of foam bricks, and achieve the effect of good corrosion resistance and fire resistance

Inactive Publication Date: 2016-12-07
GUIZHOU HONGYI ENVIRONMENTAL PROTECTION BUILDING MATERIAL
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is: aiming at the problems of excessive density and low str

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Example 1, Preparation of raw materials, every 1 m 3 The raw materials required for wall bricks are as follows: silica sand 180Kg, cement 85Kg, lime 40Kg, phosphogypsum 20Kg, coal ash 30Kg, water 340Kg, aluminum powder 0.41Kg, mica powder 28.4Kg.

[0016] Preparation Process:

[0017] 1. Weigh the ingredients according to the proportion, grind all the materials except aluminum powder into powder, mix at a temperature of 38℃, add water and stir, add aluminum powder after complete mixing, and stir for 40 seconds;

[0018] 2. Heat to 58°C for foaming, the foaming time is 150 minutes;

[0019] 3. Divide into blocks;

[0020] 4. After dividing, enter the steam room for steaming, the steaming pressure is 1.2-1.4MPa, the steaming temperature is 200℃, and the steaming time is 8 hours.

Embodiment 2

[0021] Example 2: Preparation of raw materials, every 1 m 3 The raw materials required for wall bricks are as follows: silica sand 185Kg, cement 87Kg, lime 42Kg, phosphogypsum 24Kg, coal ash 31Kg, water 330Kg, aluminum powder 0.43Kg, mica powder 28.6Kg.

[0022] Preparation Process:

[0023] 1. Weigh the ingredients according to the proportion, grind all the materials except aluminum powder into powder, mix at a temperature of 38℃, add water and stir, add aluminum powder after complete mixing, and stir for 40 seconds;

[0024] 2. Heat to 59°C for foaming, the foaming time is 140 minutes;

[0025] 3. Divide into blocks;

[0026] 4. After dividing, enter the steam room for steaming, the steaming pressure is 1.2-1.4MPa, the steaming temperature is 210℃, and the steaming time is 8 hours.

Embodiment 3

[0027] Example 3: Preparation of raw materials, every 1 m 3 The raw materials required for wall bricks are as follows: silica sand 190Kg, cement 85Kg, lime 35Kg, phosphogypsum 17Kg, coal ash 30Kg, aluminum powder 0.5Kg, mica powder 30Kg, and water 360Kg. .

[0028] Preparation Process:

[0029] 1. Weigh the ingredients according to the ratio, grind all the materials except aluminum powder into powder, mix at 38℃, add water and stir, add aluminum powder after complete mixing, and stir for 45 seconds;

[0030] 2. Heat to 59°C for foaming, and the foaming time is 150 minutes;

[0031] 3. Divide into blocks;

[0032] 4. After dividing, enter the steam room for steaming, the steaming pressure is 1.2-1.4MPa, the steaming temperature is 220℃, and the steaming time is 8 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lightweight soundproof thermal insulation wall brick. The wall brick is prepared from, by weight, 170-190 parts of silica sand, 80-90 parts of cement, 35-45 parts of lime, 17-24 parts of ardealite, 25-35 parts of coal ash, 0.3-0.5 part of aluminum powder, mica powder and 320-360 parts of water, wherein the mica powder accounts for 7-9% of the total dry weight. Compared with an organic foaming method, an inorganic foaming method has advantages of high corrosion resistance, fireproof performance and environment friendliness. The wall brick prepared from the raw materials according to the method is about 0.34g/cm<3> in bulk density, 1.6Mpa in compressive strength, 0.07W/m.K in thermal conductivity and 40db in soundproof effect.

Description

Technical field [0001] The invention relates to the technical field of building filling materials, in particular to a foamed wall brick and a manufacturing method thereof. Background technique [0002] Normal indoor partition walls are made of lightweight bricks, and the density of lightweight bricks is only 600-700Kg / m 3 , Lightweight bricks generally refer to foamed bricks. At present, more foamed bricks mainly use organic foaming technology, and organic foaming mainly has the disadvantages of poor anti-corrosion and fire resistance. Lightweight bricks can not only effectively reduce the load on the floor, but also have good sound insulation and heat insulation effects, but the strength of lightweight bricks is poor. For example, the Chinese patent with application number 01310397200.0 discloses a lightweight wall brick with a density of 650Kg / m 3 , The compressive strength is 1.6Mpa. Therefore, how to obtain lighter and stronger wall tiles is a subject that is always pursued ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B28/14C04B111/52C04B111/28
CPCC04B28/143C04B2111/28C04B2111/52C04B2201/20C04B2201/32C04B2201/50C04B14/06C04B7/00C04B22/064C04B18/08C04B14/042C04B22/04C04B38/02C04B38/0067
Inventor 董志斌董德良杨立勇刘友群谢治林
Owner GUIZHOU HONGYI ENVIRONMENTAL PROTECTION BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap