A kind of preparation method of the coating slurry used in the leather preparation process

A preparation process and slurry technology, applied in the field of leather, can solve the problems of unsatisfactory antistatic properties, poor antibacterial properties, poor corrosion resistance, poor penetration, poor stability, etc., to reduce rapid fading, strong antibacterial ability, and antistatic properties strong effect

Active Publication Date: 2018-09-04
YANGZHOU DERWINS PLASTICS TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, during the coating process of leather preparation, the penetration and stability between the coated slurry and the base layer are poor, resulting in poor antibacterial and corrosion resistance of automotive leather during use. In the application of automobiles, antistatic Performance does not meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A coating slurry used in a leather preparation process is made of the following raw materials in parts by weight: 10 parts of water, 80 parts of water-based polyurethane resin, 120 parts of bagasse tapioca starch polylactic acid, 2 parts of methylenebisstearamide, 2 parts of butyl stearate, 0.5 parts of sodium starch glycolate, 0.5 parts of SP demulsifier, 1 part of dodecyl dimethyl amine oxide, 0.2 parts of betaine, N, N'-dinitrosopenta 0.2 parts of methylenetetramine, 0.2 parts of zinc dialkyldithiophosphate, 0.2 parts of EDTA, 0.3 parts of 3-nitro-4-hydroxyphenylarsonic acid, 0.2 parts of sodium pyrophosphate, and 0.1 parts of sodium acetate.

Embodiment 2

[0017] A kind of coating slurry used in the leather preparation process is made of the following raw materials in parts by weight: 12 parts of water, 100 parts of water-based polyurethane resin, 110 parts of bagasse tapioca starch polylactic acid, 3 parts of methylenebisstearamide, 3 parts of butyl stearate, 0.2 parts of sodium carboxymethyl starch, 0.7 parts of SP demulsifier, 2 parts of dodecyl dimethyl amine oxide, 0.3 parts of betaine, N, N'-dinitrosopenta 0.3 parts of methylenetetramine, 0.3 parts of zinc dialkyldithiophosphate, 0.3 parts of EDTA, 0.45 parts of 3-nitro-4-hydroxyphenylarsonic acid, 0.3 parts of sodium pyrophosphate, and 0.3 parts of sodium acetate.

Embodiment 3

[0019] A kind of coating slurry used in the leather preparation process is made of the following raw materials in parts by weight: 15 parts of water, 60 parts of water-based polyurethane resin, 115 parts of bagasse tapioca starch polylactic acid, 4 parts of methylenebisstearamide, 1 part of butyl stearate, 0.3 part of sodium carboxymethyl starch, 1.0 part of SP demulsifier, 4 parts of dodecyl dimethyl amine oxide, 0.5 part of betaine, N, N'-dinitrosopenta 0.5 parts of methylenetetramine, 0.5 parts of zinc dialkyldithiophosphate, 0.5 parts of EDTA, 0.6 parts of 3-nitro-4-hydroxyphenylarsonic acid, 0.5 parts of sodium pyrophosphate, and 0.5 parts of sodium acetate.

[0020] A method for preparing a coating slurry used in a leather preparation process, comprising the following steps: ① Divide water, water-based polyurethane resin, bagasse tapioca starch polylactic acid into two parts respectively; Polyurethane resin, bagasse tapioca starch polylactic acid and methylenebisstearami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a coating slurry used in a leather preparation process. The coating slurry is prepared from the following raw materials in parts by weight: 10-15 parts of water, 60-100 parts of water-based polyurethane resin, 110-120 parts of bagasse cassava starch polylactic acid, 2-4 parts of methylene-bis stearamide, 1-3 parts of butyl stearate, 0.2-0.5 part of sodium carboxymethyl starch, 0.5-1.0 part of SP demulsifier, 1-4 parts of lauryl dimethyl amine oxide, 0.2-0.5 part of betaine, 0.2-0.5 part of N,N'-dinitrosopentamethylene tetramine, 0.2-0.5 part of zinc dialkyl dithiophosphate, 0.2-0.5 part of EDTA (ethylene diamine tetraacetic acid), 0.3-0.6 part of 3-nitro-4-hydroxyphenylarsonic acid, 0.2-0.5 part of sodium pyrophosphate and 0.1-0.5 part of sodium acetate. The coated leather has the advantages of high antistatic property, high oxidation resistance, high corrosion resistance, high antimicrobial capacity, high surface elasticity and high surface tenderness.

Description

technical field [0001] The invention belongs to the field of leather, in particular to a coating slurry used in the leather preparation process and a preparation method thereof. Background technique [0002] At present, during the coating process of leather preparation, the penetration and stability between the coated slurry and the base layer are poor, resulting in poor antibacterial and corrosion resistance of automotive leather during use. In the application of automobiles, antistatic The performance is also not up to the mark. Contents of the invention [0003] The invention provides a coating slurry used in the leather preparation process and a preparation method thereof to solve the defects in the prior art. [0004] The present invention is achieved through the following technical solutions: [0005] A coating slurry used in the leather preparation process is made of the following raw materials in parts by weight: 10-15 parts of water, 60-100 parts of water-based ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C14C11/00C14C15/00
CPCC14C11/00C14C15/00
Inventor刘传庆刘顺兆徐蓉吴丽萍陈意
OwnerYANGZHOU DERWINS PLASTICS TECH