High elastic table tennis bat front rubber cover

A table tennis racket, high elasticity technology, applied in the field of positive rubber, can solve the problems of shortened service life, reduced strength and elongation, and easily damaged particles, and achieves the effect of stable hitting and fast ball return.

Active Publication Date: 2017-02-15
YANCHENG AST SPORTING GOODS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the proportion of butadiene rubber is too large, the hardness, strength and elongation of the rubber will be reduced, the particles will be easily damaged, and the service life will be shortened; Technical requirements, balancing high elasticity and high hardness is a major difficulty in the design of rubber compositions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The present embodiment provides a kind of high elastic table tennis racket positive glue rubber, and it comprises the raw material component of following parts by weight:

[0028] Natural rubber 50g;

[0029] Trans-1,4-polyisoprene rubber 30g;

[0030] 40g of butadiene rubber; (natural rubber, trans-1,4-polyisoprene rubber, and butadiene rubber are available conventionally);

[0031] Polyvinylimidazole (number average molecular weight 10000) 30g;

[0032] Polymethyl methacrylate (number average molecular weight 10000) 10g;

[0033] Hydroxy acrylic resin (number average molecular weight 10000) 20g;

[0034] Zinc carbonate 10g;

[0035] 2,2'-dithiodibenzothiazole 2g;

[0036] Sulfur 1g;

[0037] 2,6-di-tert-butyl-p-cresol 2g;

[0038] Nanoscale titanium dioxide 10g.

[0039] The preparation method of above-mentioned high-elasticity table tennis racket normal glue rubber, comprises the following steps:

[0040] (1) the natural rubber, trans-1,4-polyisoprene rubber...

Embodiment 2

[0043] This embodiment provides a high-elastic table tennis racket positive rubber, its preparation method is consistent with that in Example 1, the difference is that it includes the following raw material components in parts by weight:

[0044] Natural rubber 80g;

[0045] Trans-1,4-polyisoprene rubber 10g;

[0046] Butadiene rubber 10g;

[0047] Polyvinylimidazole (number average molecular weight 100000) 10g;

[0048] Polymethyl methacrylate (number average molecular weight 100000) 5g;

[0049] Hydroxy acrylic resin (number average molecular weight 100000) 10g;

[0050] Zinc oxide 5g;

[0051] 2-mercaptobenzothiazole 0.1g;

[0052] Sulfur 0.1g;

[0053] 2,2,4-trimethyl-1,2-dihydroquinoline polymer 0.1g;

[0054] Nanoscale barium sulfate 5g.

Embodiment 3

[0056] This embodiment provides a high-elastic table tennis racket positive rubber, its preparation method is consistent with that in Example 1, the difference is that it includes the following raw material components in parts by weight:

[0057] Natural rubber 60g;

[0058] Trans-1,4-polyisoprene rubber 20g;

[0059] Butadiene rubber 20g;

[0060] Polyvinylimidazole (number average molecular weight 75000) 20g;

[0061] Polymethyl methacrylate (number average molecular weight 75000) 8g;

[0062] Hydroxy acrylic resin (number average molecular weight 75000) 15g;

[0063] Stearic acid 8g;

[0064] Diphenylguanidine 1g;

[0065] Sulfur 0.5g;

[0066] 0.5 g of 2,6-di-tert-butyl-p-cresol.

[0067] The high-elasticity table tennis racket normal rubber rubber that makes in the above-mentioned embodiment is subjected to performance test, and specific data is listed in Table 1.

[0068] Table 1 Performance test data table of high elastic table tennis racket positive rubber

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high elastic table tennis bat front rubber cover. The cover is prepared from, by weight, 50-80 parts of natural rubber, 10-30 parts of trans -1,4- polyisoprene rubber,10-40 parts of butadiene rubber, 10-30 parts of polyvinyl imidazole, 5-10 parts of polymethyl methacrylate, 10-20 parts of hydroxy acrylic resin, 5-10 parts of vulcanizing activators, 0.1-2 parts of vulcanizing accelerators, 0.1-1 part of sulphur and 0.1-2 parts of antiagers. Through the formula formed by substances of the natural rubber, the trans -1,4- polyisoprene rubber, the butadiene rubber, the polyvinyl imidazole and the like, the prepared rubber cover achieves a good balance between elasticity and rigidity, and helps the athletes to give play to technical specialties such as fast ball return speed, stable ball hitting and no ball losing.

Description

technical field [0001] The invention relates to a positive rubber, in particular to a high-elastic positive rubber for a table tennis racket. Background technique [0002] The normal rubber of table tennis rackets is also called short-grain rubber. It should have high resilience and hardness, which is conducive to athletes to play the technical advantages of fast return speed, stable hitting, and no spin. It is suitable for fast attack near the table, especially the left The push right attack style is one of the most commonly used rubber types for straight fast break players. Generally, natural rubber is used and butadiene rubber with better elasticity is used as the base material. However, if the proportion of butadiene rubber is too large, the hardness, strength and elongation of the rubber will be reduced, the particles will be easily damaged, and the service life will be shortened; Technical requirements, balancing high elasticity and high hardness is a major difficult...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L39/04C08L33/12C08L33/00C08K13/02C08K3/26C08K5/47C08K3/06C08K5/13C08K3/22C08K3/30
CPCC08K2201/011C08L7/00C08L2205/02C08L2205/025C08L2205/035C08L9/00C08L39/04C08L33/12C08L33/00C08K13/02C08K3/26C08K5/47C08K3/06C08K5/13C08K2003/2296C08K2003/3045C08K5/09C08K5/31
Inventor 王旭升高焱汤小庆刘宗英黄田富
Owner YANCHENG AST SPORTING GOODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap