CsLiCdP207 compound, CsLiCdP207 nonlinear optical crystal, preparation method of crystal and application of crystal

A technology of nonlinear optics and compounds, applied in phosphorus compounds, chemical instruments and methods, inorganic chemistry, etc., can solve problems such as small birefringence, CLBO is easy to deliquesce, limit output power and beam quality, and achieve stable physical and chemical properties , large nonlinear optical effect, and short UV absorption cut-off edge

Active Publication Date: 2017-03-15
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the birefringence of LBO is relatively small, and the quadrupling output of 1064nm wavelength laser cannot be realized; the birefringence of BBO is relatively large, and there is a photorefractive effect when used for quadrupling output of 1064nm wavelength laser, which limits its Output power and beam quality; while CLBO is extremely deliquescent and difficult to achieve commercial applications; KBBF is difficult to obtain crystals with a large c-thickness due to its serious layered growth habit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CsLiCdP207 compound, CsLiCdP207 nonlinear optical crystal, preparation method of crystal and application of crystal
  • CsLiCdP207 compound, CsLiCdP207 nonlinear optical crystal, preparation method of crystal and application of crystal
  • CsLiCdP207 compound, CsLiCdP207 nonlinear optical crystal, preparation method of crystal and application of crystal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Adopt solid phase reaction method, reaction equation is as follows:

[0039] 0.5Cs 2 CO 3 +LiOH·H 2 O+CdCO 3 +2NH 4 h 2 PO 4 =CsLiCdP 2 o 7 +1.5CO 2 ↑+4.5H 2 O↑+2NH 3 ↑

[0040] The dosages of the above four reagents are respectively: Cs 2 CO 3 1.629g (0.005mol), LiOH·H 2 O 0.4196g (0.010mol), CdCO 3 1.724g (0.010mol),NH 4 h 2 PO 4 2.301 g (0.020 mol).

[0041] The specific operation steps are: weigh the reagents according to the above dosages, put them into a mortar, mix and grind them evenly, then put them into a corundum ceramic crucible, compact them, put them into a muffle furnace, and heat them at 10°C / Heat up to 500°C at a rate of 1 hour, then heat-preserve and sinter for more than 12 hours. After cooling down to room temperature, take it out and grind it evenly. Phase CsLiCdP 2 o 7 compound.

[0042] Such as figure 2 As shown, the powder X-ray diffraction pattern of the compound prepared in this example is consistent with the pattern...

Embodiment 2

[0044] Preparation of powdered CsLiCdP 2 o 7 compound

[0045] Adopt solid phase reaction method, reaction equation is as follows:

[0046] 1CsNO 3 +0.5Li 2 CO 3 +Cd(NO 3 ) 2 +2(NH 4 ) 2 HPO 4 =CsLiCdP 2 o 7 +0.5CO 2 ↑+3H 2 O↑+0.75O 2 ↑+4NH 3 ↑+3NO 2 ↑

[0047] The dosage of the above four reagents:

[0048] cNO 3 1.949g (0.010mol), Li 2 CO 3 0.369g (0.005mol), CdCO 3 1.724g (0.010mol),NH 4 h 2 PO 4 2.301 g (0.020 mol).

[0049] The specific operation steps are: weigh the reagents according to the above dosage, put them into a mortar, mix and grind them evenly, then put them into a corundum ceramic crucible, compact them, put them into a muffle furnace, and heat them at 200 ° C / Heat up to 500°C at a rate of 1 hour, then heat-preserve and sinter for more than 12 hours, take it out and grind it evenly after cooling down to room temperature, then heat up to 600°C at a rate of 200°C / hour and sinter for more than 24 hours, take it out and grind it fo...

Embodiment 3～6

[0051] Embodiment 3~6 is to prepare CsLiCdP 2 o 7 the crystal

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a CsLiCdP207 compound, a CsLiCdP207 nonlinear optical crystal, a preparation method of the crystal and an application of the crystal. The crystal is transparent and free of inclusion and has the advantages of high growth speed, low cost, short ultraviolet absorption cutoff edge, high nonlinear optical effect, stable physical and chemical properties, good mechanical property, easiness in processing and the like. The crystal can be used for manufacturing a nonlinear optical device. The nonlinear optical device made of the nonlinear optical crystal can be used for a plurality of military and civil high-tech fields such as laser blind weapons, optical disk recording, laser projection televisions, optical computation and optical fiber communication.

Description

technical field [0001] The present invention relates to a kind of CsLiCdP 2 o 7 compound, CsLiCdP 2 o 7 Nonlinear optical crystal, CsLiCdP 2 o 7 Crystal preparation method, CsLiCdP 2 o 7 Use of crystals for fabricating nonlinear optical devices and comprising CsLiCdP 2 o 7 Optical devices for nonlinear optical crystals. Background technique [0002] The nonlinear optical effect of crystal refers to such an effect: when a beam of laser light with a certain polarization direction passes through a nonlinear optical crystal in a certain direction, the frequency of the beam will change. Crystals with nonlinear optical effects are called nonlinear optical crystals. Using the nonlinear optical effect of crystals, nonlinear optical devices such as second harmonic generators, up-down frequency converters, and optical parametric oscillators can be made. The all-solid-state laser using nonlinear optical crystals for frequency conversion is a development direction of lasers i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B25/45C30B29/14C30B9/12
CPCC01B25/45C01P2002/72C30B9/12C30B29/14
Inventor 罗军华沈耀国赵三根赵炳卿孙志华
Owner FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com