li 9 na 3 rb 2 (so 4 ) 7 Compound, nonlinear optical crystal and its preparation method and application

A nonlinear optics, SO4 technology, applied in the field of Li9Na3Rb27 compounds, can solve problems such as unfavorable long-term work

Active Publication Date: 2020-04-07
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the crystal contains crystal water, dehydration decomposition begins to occur at 83°C, which is not conducive to its long-term work under high-power laser irradiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • li <sub>9</sub> na <sub>3</sub> rb <sub>2</sub> (so <sub>4</sub> ) <sub>7</sub> Compound, nonlinear optical crystal and its preparation method and application
  • li <sub>9</sub> na <sub>3</sub> rb <sub>2</sub> (so <sub>4</sub> ) <sub>7</sub> Compound, nonlinear optical crystal and its preparation method and application
  • li <sub>9</sub> na <sub>3</sub> rb <sub>2</sub> (so <sub>4</sub> ) <sub>7</sub> Compound, nonlinear optical crystal and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Adopt solid phase reaction method, reaction equation is as follows:

[0045] (a)9Li 2 SO 4 ·H 2 O+3Na 2 SO 4 +2Rb 2 SO 4 =2Li 9 Na 3 Rb 2 (SO 4 ) 7 +9H 2 O↑

[0046] The dosage of the above three reagents: Li 2 SO 4 ·H 2 O 23.03 grams (0.18mol), Na 2 SO 4 8.52 grams (0.06mol), Rb 2 SO 4 10.68g (0.04mol)

[0047] The specific operation steps are: weigh the reagents according to the above dosage, put them into a mortar, mix and grind them evenly, then put them into a platinum crucible, compact them, put them into a muffle furnace, and heat them at 30°C / hour. The temperature was raised to 380°C at a rate of 100°C / hour, and then kept for sintering for 24 hours. After cooling down to room temperature, the Li 9 Na 3 Rb 2 (SO 4 ) 7 The pure phase of the compound.

[0048] Such as figure 2 As shown, the powder X-ray diffraction pattern obtained from the experiment is consistent with the pattern obtained by fitting according to its single crystal st...

Embodiment 2

[0050] Adopt solid phase reaction method, reaction equation is as follows:

[0051] (b)9Li 2 SO 4 +3Na 2 SO 4 +2Rb 2 SO 4 =2Li 9 Na 3 Rb 2 (SO 4 ) 7

[0052] The dosage of the above three reagents: Li 2 SO 4 19.79 g (0.18 mol), Na 2 SO 4 8.52 g (0.06 mol), Rb 2 SO 4 10.68g (0.04mol)

[0053] The specific operation steps are: weigh the reagents according to the above dosage, put them into a mortar, mix and grind them evenly, then put them into a platinum crucible, compact them, put them into a muffle furnace, and heat them at 30°C / hour. The temperature was raised to 380°C at a rate of 100°C / hour, and then kept for sintering for 24 hours. After cooling down to room temperature, the Li 9 Na 3 Rb 2 (SO 4 ) 7 The pure phase of the compound.

[0054] Such as figure 2 As shown, the powder X-ray diffraction pattern obtained from the experiment is consistent with the pattern obtained by fitting according to its single crystal structure.

Embodiment 3

[0056] Adopt solid phase reaction method, reaction equation is as follows:

[0057] (c)9Li 2 SO 4 ·H 2 O+3Na 2 SO 4 10H 2 O+2Rb 2 SO 4 =2Li 9 Na 3 Rb 2 (SO 4 ) 7 +39 H 2 O↑

[0058] The dosage of the above three reagents: Li 2 SO 4 ·H 2 O 23.03 grams (0.18mol), Na 2 SO 4 10H 2 O 19.33 g (0.06 mol), Rb 2 SO 4 10.68g (0.04mol)

[0059] The specific operation steps are: weigh the reagents according to the above dosage, put them into a mortar, mix and grind them evenly, then put them into a platinum crucible, compact them, put them into a muffle furnace, and heat them at 30°C / hour. The temperature was raised to 400°C at a rate of 100°C / hour, and then kept for sintering for 24 hours. After cooling down to room temperature, the Li 9 Na 3 Rb 2 (SO 4 ) 7 The pure phase of the compound.

[0060] Such as figure 2 As shown, the powder X-ray diffraction pattern obtained from the experiment is consistent with the pattern obtained by fitting according to its s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an Li9Na3Rb2(SO4)7 compound, nonlinear optical crystal and a preparation method and application thereof. The invention has the following beneficial effects: the crystal is easy to grow, is transparent and free of inclusion, and has the following advantages: growth speed is high, cost is low, and crystals with large size can be easily obtained. The crystal has advantages ofshort ultraviolet absorption cut-off edge, large non-linear optical effect, stable physical and chemical properties, good mechanical property and easy processing. The crystal can be used for manufacturing non-linear optical devices. A non-linear optical device prepared from the non-linear optical crystal can be used in some military and civilian high-tech fields, such as laser blinding weapon, optical disc recording, laser projection television, optical computing, fiber-optic communication, etc.

Description

technical field [0001] The present invention relates to a kind of Li 9 Na 3 Rb 2 (SO 4 ) 7 Compound, Li 9 Na 3 Rb 2 (SO 4 ) 7 Nonlinear optical crystals, Li 9 Na 3 Rb 2 (SO 4 ) 7 Crystal preparation method and Li 9 Na 3 Rb 2 (SO 4 ) 7 Crystals are used to make nonlinear optical devices. [0002] technical background [0003] The nonlinear optical effect of crystal refers to such an effect: when a beam of laser light with a certain polarization direction passes through a nonlinear optical crystal in a certain direction, the frequency of the beam will change. Crystals with nonlinear optical effects are called nonlinear optical crystals. Using the nonlinear optical effect of crystals, nonlinear optical devices such as second harmonic generators, up-down frequency converters, and optical parametric oscillators can be made. The all-solid-state laser using nonlinear optical crystals for frequency conversion is a development direction of lasers in the future, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01D17/00C30B29/46C30B11/02G02F1/355
CPCC01D17/003C01P2002/72C30B11/02C30B29/46G02F1/3551
Inventor 罗军华李雁强赵三根
Owner FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com