A kind of preparation method of bulletproof helmet

A bulletproof helmet and helmet body technology, applied in protective equipment, protective equipment, chemical instruments and methods, etc., can solve the problems of uncomfortable wearing, limited elastic modulus and tensile strength, and large helmet dent.

Active Publication Date: 2018-11-27
SHENYANG JIHUA 3547 SPECIAL TYPE ARMAMENT
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Bulletproof helmets on the market include two types, metal and non-metal: metal bulletproof helmets are cheap, but the shell is heavy and uncomfortable to wear; non-metal bulletproof helmets are mainly made of aramid Ⅱ, although the bulletproof made of aramid Ⅱ The helmet solves the shortcomings of the metal helmet, but due to the limited elastic modulus and tensile strength of the aramid fiber II, the impact effect of the helmet is not very good under certain conditions, and the impact depression of the helmet is large, which cannot meet the standard Requirements: In the past molding method, the aramid fabric should first be spread into the die, and the materials should be rotated and overlapped. In this way, the material needs to be larger than the size of the helmet shell, that is, part of the material must be outside the mold to ensure the helmet shell Dimensions and ease of ejection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of bulletproof helmet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The technological process of making bulletproof helmets is as follows:

[0036] 1. Cutting:

[0037] According to the requirements, use a pencil to draw lines on the aramid cloth according to the template, a total of 16 specifications, and then use an automatic sharpening and cutting machine to cut according to the lines. No. 1-8 is aramid fiber II, and No. 9-16 is aramid fiber III. Finally, use a band saw cutting machine to cut and trim No. 1-16.

[0038] technical standard:

[0039] (1) Typesetting and cutting according to the requirements.

[0040] (2) Mark the number of layers of the blank according to the specified requirements.

[0041] Process requirements:

[0042] (1) When spreading the cloth, the edge of the cloth should be aligned with one side, and the order of cutting should be based on the small piece first.

[0043] (2) When cutting, it should be cut strictly according to the line to prevent cutting and uneven secant lines.

[0044] (3) Mark and com...

Embodiment 2

[0146] Utilize the bombardment result of the ballistic helmet described in the embodiment 1 that aramid fiber Ⅱ and aramid fiber Ⅲ mix and make as follows table: Ministry of Public Security two grades, 51 formula 7.62mm pistol bullets (lead core)

[0147] serial number

[0148] The ballistic results of bulletproof helmets made of aramid Ⅱ on the market are as follows:

[0149] Ministry of Public Security Level 2, Type 51 7.62mm pistol bullet (lead core)

[0150] serial number

[0151] From the data in the above scale, it can be seen that the sag is significantly reduced. The size of the helmet sag is a direct standard to measure the bulletproof performance of the helmet, and it is also an important indicator to measure the quality of the helmet. Because the helmet sag is too large, it will cause damage to the human head. The injury directly threatens life and health, and the dent of the helmet used is an important symbol to measure the quality of the helmet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a bulletproof helmet. The preparation method mainly comprises steps as follows: cutting, pasting forming, prepressing, edge cutting, forming, edge trimming, drilling, bonding of edge sealing rubber strips, surface treatment, paint spraying of the inner surface, bonding of a cap lining, paint spraying of the outer surface, inspecting and packaging. The method has the advantages that a shell of the bulletproof helmet is made of aramid II / III, so that bulletproof performance of the helmet is improved, and mass of the helmet is reduced.

Description

technical field [0001] The invention belongs to the technical field of bulletproof protective equipment materials, and relates to a preparation method of a bulletproof helmet. Background technique [0002] In recent years, terrorist attacks have continued to occur in various countries, and personnel from various countries have stepped up research and development in the field of security protection. With the development of society and economy in our country, people's awareness of safety protection has increased, and the demand for safety protection equipment has increased. The country also clearly stated in the "Twelfth Five-Year Plan" that it will increase support for the field of public safety. In order to effectively prevent the occurrence of terrorist incidents, serious crimes must be severely cracked down. In view of the particularity of these vicious terrorist incidents, it is necessary to strengthen the protection of our public security officers and security personnel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F41H1/04B32B37/10B32B37/06
CPCB32B37/06B32B37/10B32B2262/0269B32B2571/02F41H1/04
Inventor 张巾玲龙钦生王宝刚马兴海吴丽丽李响刘英环周晶毕书桂
Owner SHENYANG JIHUA 3547 SPECIAL TYPE ARMAMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap