A high-sensitivity rare earth-doped tungsten bronze fluorescent temperature detection material
A rare earth doping, high-sensitivity technology, applied in luminescent materials, chemical instruments and methods, etc., can solve the problems of low temperature detection sensitivity and unfavorable material application, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0014] Preparation of Ba 4 Gd 0.65-x Er 0.02 Yb x Nb 10 o 30 , where x=0, the preparation method is as follows:
[0015] Weigh 2.3920 g BaCO 3 (99%), 0.3534 g Gd 2 o 3 (99.9%), 0.0115 grams of Er 2 o 3 , 3.9872 g Nb 2 o 5 , placed in a clean agate jar, using absolute ethanol (99.7%) as a medium, and ball milling on a planetary ball mill for 24 hours. The ball-milled product is dried in an oven to obtain a dried powder. Grind the dried powder with an agate mortar, then place it in a corundum crucible, put it into a box furnace, and heat it up to 1300°C for 8 hours for pre-burning, and then stop the program after cooling down to 550°C. Grind the product obtained after cooling with the furnace with an agate mortar, add binder, grind thoroughly, mix evenly, then place it in a corundum crucible and calcine at 1350°C in the air for 5 hours, and finally grind it finely with an agate mortar to obtain upconversion Phosphor.
Embodiment 2
[0017] Preparation of Ba 4 Gd 0.65-x Er 0.02 Yb x Nb 10 o 30 , wherein x=0.1, the preparation method is as follows:
[0018] Weigh 2.3920 g BaCO 3 (99%), 0.3534 g Gd 2 o 3 (99.9%), 0.0115 grams of Er 2 o 3 , 0.0591 g Yb 2 o 3 , 3.9872 g Nb 2 o 5 , placed in a clean agate jar, using absolute ethanol (99.7%) as a medium, and ball milling on a planetary ball mill for 24 hours. The ball-milled product is dried in an oven to obtain a dried powder. Grind the dried powder with an agate mortar, then place it in a corundum crucible, put it into a box furnace, and heat it up to 1300°C for 8 hours for pre-burning, and then stop the program after cooling down to 550°C. Grind the product obtained after cooling with the furnace with an agate mortar, add binder, grind thoroughly, mix evenly, then place it in a corundum crucible and calcine at 1350°C in the air for 5 hours, and finally grind it finely with an agate mortar to obtain upconversion Phosphor.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com