Foam glass suitable for interior decoration and production technology of foam glass

A foam glass and interior decoration technology, which is applied in glass forming, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of thermal insulation effect, sound insulation effect and strength to be improved, and achieve improved thermal insulation and sound insulation effects, Improve foam expansion ability and promote foaming effect

Inactive Publication Date: 2017-12-01
合肥钢骨玻璃制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the thermal insulation effect, sound insulation effect and strength of the existing foam glass need to be improved when it is used for interior decoration, the object of th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foam glass suitable for interior decoration and production technology of foam glass
  • Foam glass suitable for interior decoration and production technology of foam glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A foam glass suitable for interior decoration, comprising the following raw materials in parts by weight: 105 parts of waste flat glass, 35 parts of fly ash, 4 parts of silicon micropowder, 6 parts of foaming agent, 4 parts of flux, and 1.2 parts of foam stabilizer , 4.2 parts of surfactant, 2 parts of release agent and 1.7 parts of foam accelerator.

[0031] The foaming agent is graphite, which is conducive to the formation of foamed glass with a thin and uniform closed pore structure, and improves the thermal insulation and sound insulation effects of the foamed glass.

[0032] The flux is manganese dioxide, which helps to adjust the surface properties of the glass particles, reduces the viscosity of the glass, and makes the glass easy to melt.

[0033] Foam stabilizers are phosphates that help stabilize the cell structure by preventing the cells from combining with each other to form interconnected cells or from collapsing.

[0034] The surfactant is industrial alco...

Embodiment 2

[0044] A foam glass suitable for interior decoration, comprising the following raw materials in parts by weight: 100 parts of waste flat glass, 25 parts of fly ash, 2 parts of silicon micropowder, 5 parts of foaming agent, 2 parts of flux, and 0.9 parts of foam stabilizer , 2.4 parts of surfactant, 1 part of release agent and 1 part of foam accelerator.

[0045] The foaming agent is graphite, which is conducive to the formation of foamed glass with a thin and uniform closed pore structure, and improves the thermal insulation and sound insulation effects of the foamed glass.

[0046] The flux is manganese dioxide, which helps to adjust the surface properties of the glass particles, reduces the viscosity of the glass, and makes the glass easy to melt.

[0047] Foam stabilizers are phosphates that help stabilize the cell structure by preventing the cells from combining with each other to form interconnected cells or from collapsing.

[0048] The surfactant is industrial alcohol,...

Embodiment 3

[0058] A foam glass suitable for interior decoration, comprising the following raw materials in parts by weight: 110 parts of waste flat glass, 45 parts of fly ash, 6 parts of silicon micropowder, 7 parts of foaming agent, 6 parts of flux, and 1.5 parts of foam stabilizer , 6.0 parts of surfactant, 3 parts of release agent and 2.4 parts of foam accelerator.

[0059] The foaming agent is graphite, which is conducive to the formation of foamed glass with a thin and uniform closed pore structure, and improves the thermal insulation and sound insulation effects of the foamed glass.

[0060] The flux is manganese dioxide, which helps to adjust the surface properties of the glass particles, reduces the viscosity of the glass, and makes the glass easy to melt.

[0061] Foam stabilizers are phosphates that help stabilize the cell structure by preventing the cells from combining with each other to form interconnected cells or from collapsing.

[0062] The surfactant is industrial alco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides foam glass suitable for interior decoration and its production process, which relates to the field of glass technology. The foam glass suitable for interior decoration includes the following raw materials in parts by weight: 100-110 parts of waste flat glass, 25-45 parts of fly ash Parts, 2-6 parts of silicon powder, 5-7 parts of foaming agent, 2-6 parts of flux, 0.9-1.5 parts of foam stabilizer, 2.4-6.0 parts of surfactant, 1-3 parts of release agent and foaming Accelerator 1-2.4 parts; the production process includes the following steps: (1) weighing raw materials, (2) mixing and pulverizing, (3) melting, (4) foaming, (5) annealing. The invention solves the problem that the thermal insulation effect, sound insulation effect and strength of the existing foam glass need to be improved when it is used for interior decoration.

Description

technical field [0001] The invention belongs to the technical field of glass, and in particular relates to foam glass suitable for interior decoration and a production process thereof. Background technique [0002] Foam glass was first invented by Corning Corporation of Pittsburgh in the United States. It is made of broken glass, foaming agent, modified additives and foaming accelerators. And made of inorganic non-metallic glass materials. It is composed of a large number of uniform cell structures with a diameter of 1-2 mm. Among them, the sound-absorbing foam glass has more than 50% open-cell bubbles, and the heat-insulating foam glass has more than 75% closed-cell bubbles, which can be adjusted by changing the production technical parameters according to the requirements of use. [0003] Because this new material has the functions of moisture-proof, fire-proof and anti-corrosion, and the glass material has the advantages of no deterioration in long-term service performa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C11/00C03B19/08C03C6/04C03B40/00
CPCC03C11/007C03B19/08C03B40/00C03C1/002
Inventor 朱明静
Owner 合肥钢骨玻璃制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap