A kind of ultraviolet curing adhesive and preparation method thereof

A technology of curing glue and ultraviolet light, applied in the direction of adhesives, adhesive additives, adhesive types, etc., can solve the problems of no UV-curable adhesives, decline in product yield, slow manual operation, etc., to improve product quality. Quality, improved productivity, small diameter effect

Active Publication Date: 2020-05-22
YANTAI SEAYU NEW MATERIALS CORP LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nowadays, rubber plugs or pressure-sensitive tapes are mostly used in the process, which is slow in manual operation and low in accuracy, and is prone to falling off during CNC processing, resulting in a significant drop in product yield.
[0003] There are currently no UV-curable adhesives for temporary protection of metal enclosures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultraviolet curing adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] It consists of the following raw materials in parts by weight: 40 parts of self-made bifunctional urethane acrylate prepolymer, 10 parts of multifunctional urethane acrylate prepolymer, 8 parts of polyester acrylate prepolymer, and 12 parts of reactive amine complexing agent , 20 parts of acrylate reactive diluent, 2 parts of leveling and wetting agent, 2 parts of photoinitiator, 1 part of titanium dioxide nano powder, 5 parts of fumed silica;

[0050] The self-made bifunctional polyurethane acrylate prepolymer is carried out according to the following steps:

[0051] Dehydrate the polyether diol at a temperature of 110°C and a pressure of -0.098MPa for 1.5 hours; add diisocyanate at a temperature of 60°C and a pressure of -0.098, stir for 0.6h, add a catalyst, and React at 75°C and pressure -0.098MPa for 2h; Add polymerization inhibitor and hydroxyl-containing acrylate in sequence and stir for 2h at temperature 70°C and pressure -0.098MPa, take samples every 30min with...

Embodiment 2

[0062] It consists of the following raw materials in parts by weight: 40 parts of self-made bifunctional urethane acrylate prepolymer, 10 parts of multifunctional urethane acrylate prepolymer, 8 parts of polyester acrylate prepolymer, and 12 parts of reactive amine complexing agent , 20 parts of acrylate reactive diluent, 2 parts of leveling wetting agent, 2 parts of photoinitiator, 1.5 parts of titanium dioxide nano powder, 4.5 parts of fumed silica;

[0063] The self-made bifunctional polyurethane acrylate prepolymer is carried out according to the following steps:

[0064] Dehydrate the polyether diol at a temperature of 110°C and a pressure of -0.098MPa for 1.5 hours; add diisocyanate at a temperature of 60°C and a pressure of -0.098, stir for 0.6h, add a catalyst, and React at 75°C and pressure -0.098MPa for 2h; Add polymerization inhibitor and hydroxyl-containing acrylate in sequence and stir for 2h at temperature 70°C and pressure -0.098MPa, take samples every 30min wit...

Embodiment 3

[0075] It consists of the following raw materials in parts by weight: 40 parts of self-made bifunctional urethane acrylate prepolymer, 10 parts of multifunctional urethane acrylate prepolymer, 8 parts of polyester acrylate prepolymer, and 12 parts of reactive amine complexing agent , 20 parts of acrylate reactive diluent, 2 parts of leveling wetting agent, 2 parts of photoinitiator, 2 parts of titanium dioxide nano powder, 4 parts of fumed silica;

[0076] The self-made bifunctional polyurethane acrylate prepolymer is carried out according to the following steps:

[0077] Dehydrate the polyether diol at a temperature of 110°C and a pressure of -0.098MPa for 1.5 hours; add diisocyanate at a temperature of 60°C and a pressure of -0.098, stir for 0.6h, add a catalyst, and React at 75°C and pressure -0.098MPa for 2h; Add polymerization inhibitor and hydroxyl-containing acrylate in sequence and stir for 2h at temperature 70°C and pressure -0.098MPa, take samples every 30min with in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultraviolet-curing adhesive and a preparation method of same. The ultraviolet-curing adhesive is composed of, by weight, 20-60 parts of a self-made bifunctional polyurethane-acrylate prepolymer, 5-15 parts of a multifunctional polyurethane-acrylate prepolymer, 5-15 parts of a polyester-acrylate prepolymer, 5-20 parts of a reactive amine compounding agent, 10-30 parts of an acrylate-type activity diluent, 0.5-5% of a flatting and wetting agent, 1-5% of a photoinitiator, 0.5-5 parts of titanium dioxide nano-powder, and 0.1-10 parts of fumed silica. The ultraviolet light curing adhesive is suitable for temporary protection for metal shells, has protective effect during a later-period treatment process of CNC and can be easily stripped-off after the CNC machining. The adhesive has no residue and stripping off on the metal shells.

Description

technical field [0001] The invention relates to an ultraviolet light curing adhesive and a preparation method thereof. Background technique [0002] With the continuous expansion of the application field of ultraviolet light technology, ultraviolet light curing adhesives play an important role in electronic products such as mobile phones, televisions, and computers. In this era when user experience is highly valued, more and more manufacturers of mobile phones, notebooks, and wearable devices have begun to focus on shell materials. From the perspective of the mobile phone field, the shell material is gradually transitioning from engineering plastics to metal. When it comes to all metal, CNC must be mentioned. At present, the all-metal casings of 3C products are basically processed by CNC machine tools (Computer numerical control machine tools, CNC). Because of its advantages of high efficiency, high precision and stable processing quality, CNC has become an essential equi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/14C09J167/06C09J11/04C08G18/67C08G18/48
CPCC08G18/4833C08G18/672C08K2003/2241C08K2201/011C08L2205/025C08L2205/03C09J11/04C09J175/14C08L75/14C08L67/06C08K3/22C08K3/36C08G18/48
Inventor 李不悔李峰贺国新张利文
Owner YANTAI SEAYU NEW MATERIALS CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com