Aluminum alloy precise casting solidification defect control method
A precision casting and control method technology, applied in the field of aluminum alloy casting, can solve problems such as difficult processing and no solution, and achieve the effects of increasing solidification speed, suppressing loose defects, and increasing cooling speed
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] In this embodiment, the method for controlling solidification defects in aluminum alloy precision casting, the castings are cabins, and the outline dimensions are The wall thickness is 2.5mm, the material is ZL114A aluminum-silicon cast aluminum alloy, and the investment plaster type vacuum pressure casting process is adopted. The steps are as follows:
[0023] When casting the gypsum with the wax model of the investment casting cabin, a "U" wax pattern with a diameter of 30mm is set in the mold, and the distance between the sidewall of the "U" wax pattern and the mold cavity is 30mm. After dewaxing at 200°C and firing at 700°C, the mold temperature is reduced to 300°C, and the "U"-shaped channel is filled with iron powder. The particle size of the iron powder is 40 mesh. Before casting the ZL114A melt, connect the vent pipe firmly to the side of the upper plane of the "U"-shaped channel close to the casting. After filling the mold under -0.05MPa vacuum, ...
Example Embodiment
[0025] Example 2
[0026] In this embodiment, the method for controlling solidification defects in aluminum alloy precision casting, the casting is a shell type, and the outline size is The wall thickness of the main body is 3.0mm, the material is ZL205A aluminum-copper cast aluminum alloy, and the investment plaster type gravity casting process is adopted. The steps are as follows:
[0027] When the investment casting shell wax pattern is poured into plaster, a "U"-shaped wax sample with a diameter of 40mm is set in the mold, and the distance between the sidewall of the "U"-shaped wax sample and the mold cavity is 20mm. After dewaxing at 200°C and high-temperature roasting at 700°C, the mold temperature is reduced to 250°C, and the "U"-shaped channel is filled with chromite sand with a particle size of 20 mesh. Before the ZL205A melt is poured, the vent pipe is firmly connected to the side of the "U"-shaped channel on the plane close to the casting. After the filling is completed...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Elongation after break | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap