A river bank revetment and high-strength technology, applied in the field of permeable bricks, can solve the problems of deteriorating bank revetment greening environment, declining urban ecological benefits, affecting quality of life, etc., to achieve the effect of improving life quality, increasing product added value, and reducing urban garbage

Inactive Publication Date: 2018-06-08
DINGYUAN COUNTY MINGYOU WALL MATERIALS
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the case of heavy rain in many cities, the accumulated rainwater cannot seep quickly, which can easily cause urban waterlogging and deteriorate the revetment greening environment, resulting in a decline in urban ecological benefits and affecting people's quality of life in the city

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A high-strength permeable brick for urban river revetment, its raw materials include: aggregate 110kg, Portland cement 45kg, diatomite 20kg, water 30kg, forming stabilizer 12kg, river sand 40kg, water reducing agent 1kg, dispersant 2kg .

[0013] Aggregate includes: waste concrete 50kg, cinder 15kg, waste brick powder 4kg, dried silt 18kg, mineral waste 14kg. The particle size of waste concrete is 22mm, and its apparent density is 2150kg / m 3 , the water absorption rate is 3.8%, and the water content rate is 0.5%. Forming stabilizers include: waste asphalt 15kg, diatomaceous earth 2kg.

Embodiment 2

[0015] A high-strength permeable brick for urban river revetment, its raw materials include: aggregate 120kg, Portland cement 35kg, diatomite 40kg, water 15kg, forming stabilizer 18kg, river sand 20kg, water reducing agent 2kg, dispersant 1kg .

[0016] Aggregate includes: waste concrete 65kg, cinder 5kg, waste brick powder 12kg, dried sludge 10kg, mineral waste 25kg. The particle size of waste concrete is 10mm, and its apparent density is 2200kg / m 3 , the water absorption rate is 3.5%, and the water content rate is 1.2%. Forming stabilizers include: waste asphalt 4kg, diatomaceous earth 8kg.

Embodiment 3

[0018] A high-strength permeable brick for urban river revetment, its raw materials include: aggregate 112kg, Portland cement 42kg, diatomite 25kg, water 25kg, forming stabilizer 14kg, river sand 35kg, water reducing agent 1.2kg, dispersant 1.7kg.

[0019] Aggregate includes: waste concrete 55kg, cinder 12kg, waste brick powder 6kg, dried sludge 16kg, mineral waste 18kg. The particle size of waste concrete is 10mm, and its apparent density is 2100kg / m 3 , the water absorption rate is 3.5%, and the water content rate is 0.5%. Forming stabilizers include: waste asphalt 12kg, diatomaceous earth 4kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength water-permeable brick for an urban channel revetment. The high-strength water-permeable brick for the urban channel revetment comprises the following raw materials in parts by weight: 110 to 120 parts of aggregate, 35 to 45 parts of silicate cement, 20 to 40 parts of diatomite, 15 to 30 parts of water, 12 to 18 parts of forming stabilizer, 20 to 40 parts ofriver sand, 1 to 2 parts of water-reducing agent and 1 to 2 parts of dispersing agent. The high-strength water-permeable brick for the urban channel revetment has high compressive strength, is not liable to deformation, can effectively reduce urban garbage and save the use amount of natural aggregate, is low in cost, high in strength, dense in surface, energy-saving and environment-friendly, has high water-permeable and air-permeable properties, enables rainwater to be permeated into underground rapidly and improves the life quality of people in the city.

Description

technical field [0001] The invention relates to the technical field of permeable bricks, in particular to a high-strength permeable brick for urban river revetment. Background technique [0002] The impermeable river revetment is very harmful to the urban environment. In the event of heavy rain in many cities, the accumulated rainwater cannot seep quickly, which can easily cause urban waterlogging and deteriorate the revetment greening environment, resulting in a decline in urban ecological benefits and affecting people's quality of life in the city. How to prepare a kind of permeable brick for river revetment, which has high strength on the basis of ensuring the water permeable effect, and can meet the pavement requirements of urban river revetment, has become a technical problem to be solved at present. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a high-strength permeable brick ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00284C04B2201/50C04B18/16C04B18/103C04B18/167C04B18/0418C04B18/12C04B14/08C04B18/20C04B14/068C04B2103/302C04B2103/408
Inventor 余明友胡翠田
Owner DINGYUAN COUNTY MINGYOU WALL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap