Jade-like composite and preparation method thereof

A composition and imitation jade technology, applied in the field of resin composition, can solve the problems of poor dispersibility of inorganic optical additives, high cost of organic optical additives, imitation of jade haze, etc., and achieve the goal of reducing physical damage or chemical oxidation Possibility, excellent mechanical properties, and structurally stable effects

Inactive Publication Date: 2018-06-19
DONGGUAN JISHUO IND CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of resin is generally composed of matrix resin, optical additives, processing aids and other raw materials, but generally can only show the color sense of jade, and cannot imitate the hazy feeling of jade.
[0004] Moreover, among the optical additives, the cost of the organic optical additives is relatively high, and the dispersion of the inorganic optical additives is poor, so the optical effect formed is unsatisfactory.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jade-like composite and preparation method thereof
  • Jade-like composite and preparation method thereof
  • Jade-like composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of imitation jade composition, comprises the raw material of following weight portion:

[0028]

[0029]

[0030] Wherein, the light-diffusing microspheres are core-shell structure microspheres, the core of the core-shell structure microspheres is a nanometer inorganic light diffusing agent, and the shell is transparent polyacrylamide.

[0031] Wherein, the preparation method of the light-diffusing microspheres is: (1), take a certain amount of N,N-dimethylformamide and raise the temperature to 70°C, dissolve the polyacrylamide to form a polyacrylamide solution, and the The mass percentage of polyacrylamide in the polyacrylamide solution is 15%; (2), adding the nano-inorganic light diffusing agent into the polyacrylamide solution obtained in step (1), stirring and homogenizing to form a suspension, said The dosage of the nano-inorganic light diffusing agent is 5wt% of the polyacrylamide solution; (3) adding absolute ethanol to the suspension and cooling it ...

Embodiment 2

[0041] A kind of imitation jade composition, comprises the raw material of following weight part:

[0042]

[0043] Wherein, the light-diffusing microspheres are core-shell structure microspheres, the core of the core-shell structure microspheres is a nanometer inorganic light diffusing agent, and the shell is transparent polyacrylamide.

[0044] Wherein, the preparation method of the light-diffusing microspheres is: (1), take a certain amount of N,N-dimethylformamide and raise the temperature to 50-90°C, dissolve the polyacrylamide to form a polyacrylamide solution, The mass percentage of polyacrylamide in the polyacrylamide solution is 10%; (2), adding the nano-inorganic light diffusing agent into the polyacrylamide solution obtained in step (1), stirring and homogenizing to form a suspension, The dosage of the nano-inorganic light diffusing agent is 4wt% of the polyacrylamide solution; (3) adding absolute ethanol to the suspension and cooling it down to 20°C, then standing...

Embodiment 3

[0054] A kind of imitation jade composition, comprises the raw material of following weight portion:

[0055]

[0056] Wherein, the light-diffusing microspheres are core-shell structure microspheres, the core of the core-shell structure microspheres is a nanometer inorganic light diffusing agent, and the shell is transparent polyacrylamide.

[0057] Wherein, the preparation method of the light-diffusing microspheres is: (1), take a certain amount of N,N-dimethylformamide and raise the temperature to 90°C, dissolve the polyacrylamide to form a polyacrylamide solution, and the The mass percentage of polyacrylamide in the polyacrylamide solution is 20%; (2), adding the nano-inorganic light diffusing agent into the polyacrylamide solution obtained in step (1), stirring and homogenizing to form a suspension, said The dosage of the nano-inorganic light diffusing agent is 6wt% of the polyacrylamide solution; (3) adding absolute ethanol to the suspension and cooling it down to 25° ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of resin composites, in particular to a jade-like composite and a preparation method thereof. The jade-like composite comprises matrix resin, light diffusion microspheres, antioxidant, light stabilizer, ultraviolet light absorber, toner and the like. The composite disclosed by the invention presents an evenly dispersed natural jade appearance, and in addition, nanometer inorganic light diffusant enables the jade-like composite to own the advantages of high haze, high refractive index and the like due to the size effect of the nanometer inorganic light diffusant. In addition, the jade-like composite can serve as the interlayer of double-layer glass, so that the jade effect has third dimension, the jade composite can be favorably protected, and the possibility of the physical damage or the chemical oxidization of the jade composite is reduced.

Description

technical field [0001] The invention relates to the technical field of resin compositions, in particular to an imitation jade composition and a preparation method thereof. Background technique [0002] The ancients wore jade to show the virtue of a gentleman, and modern people also regard it as a symbol of increasing luck and social status. The Chinese love jade is always the same. Looking at today's domestic market, all kinds of jade are all over the market, and the price ranges from a few yuan for small ornaments to tens of millions of ancient jade. [0003] With the continuous development of technology, aesthetic resins can achieve a variety of effects, such as spray-painted silver, electroplated silver, pearlescent red, silvery black, and starry sky. In addition, aesthetic resins that imitate natural effects are also constantly developing, imitating jade Advanced aesthetic resins are also being developed continuously. This type of resin is generally composed of matrix ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L33/26C08L23/12C08K13/02C08K3/22C08K3/36C08K3/30C08K5/20
CPCC08K2003/2241C08K2003/3045C08K2201/003C08K2201/011C08K2201/014C08L23/12C08L77/00C08L2205/03C08L2205/18C08L33/26C08K13/02C08K3/22C08K3/36C08K3/30C08K5/20
Inventor 王勇
Owner DONGGUAN JISHUO IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com