Non-woven fabric with excellent moisture-proof property

A moisture-proof performance, non-woven fabric technology, applied in the direction of non-woven fabrics, textiles and papermaking, conjugated synthetic polymer artificial filaments, etc., can solve the problems that cannot meet the needs of the market, and the moisture-proof performance of the non-woven fabric base is not high. , to achieve excellent hydrophobic surface, weaken particle aggregation, and good mechanical stability

Inactive Publication Date: 2018-11-13
HEFEI JIENUO MEDICAL PROD CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The moisture-proof performance of the non-woven base of the existing synthetic leather is not high, which cannot meet the needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A non-woven fabric with excellent moisture-proof performance proposed by the present invention, its raw materials include by weight: 40 parts of polyethylene, 23 parts of latex, 5 parts of methyl stearate, 11.5 parts of moisture-proof compound, 3 parts of montmorillonite, Phosphate ester 9 parts, polytetrafluoroethylene 1.2 parts.

Embodiment 2

[0018] A non-woven fabric with excellent moisture-proof performance, its raw materials include, by weight, 55 parts of polyethylene, 16 parts of latex, 11 parts of methyl stearate, 6 parts of moisture-proof compound, 5 parts of montmorillonite, and 2.5 parts of phosphoric acid ester , 5.6 parts of polytetrafluoroethylene;

[0019] Wherein, the preparation method of the moisture-proof compound is as follows: add an appropriate amount of polyglycidyl methacrylate to 1 weight part of micron-sized bamboo leaf powder, heat up, perform a heat preservation reaction, add 2.6 weight parts of nano-titanium dioxide, and continue to heat up, For the second heat preservation reaction, add 2 parts by weight of gelatinized starch, mechanically stir, dry, and pulverize to obtain a moisture-proof compound.

Embodiment 3

[0021] A non-woven fabric with excellent moisture-proof performance. The raw materials include: 48 parts of polyethylene, 19 parts of latex, 8 parts of methyl stearate, 8 parts of moisture-proof compound, 4 parts of montmorillonite, and 5 parts of phosphoric acid ester. , 3 parts of polytetrafluoroethylene;

[0022] Wherein, the preparation method of the moisture-proof composite is as follows: add an appropriate amount of polyglycidyl methacrylate to 1 weight part of micron-sized bamboo leaf powder, heat up, perform a heat preservation reaction, add 1.3 weight parts of nano-titanium dioxide, continue to heat up, For the second heat preservation reaction, add 2.8 parts by weight of gelatinized starch, mechanically stir, dry, and pulverize to obtain a moisture-proof compound;

[0023] The temperature of the first insulation reaction is 65°C, and the time is 2h;

[0024] The temperature of the second heat preservation reaction is 80°C, and the time is 2.5h;

[0025] The speed o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a non-woven fabric with an excellent moisture-proof property. The non-woven fabric is prepared from, by weight, 40-55 parts of polyethylene, 16-23 parts of latex, 5-11 parts ofmethyl stearate, 6-11.5 parts of moisture-proof compound, 3-5 parts of imvite, 2.5-9 parts of phosphate ester and 1.2-5.6 parts of polytetrafluoroethylene. The non-woven fabric has the excellent moisture-proof property.

Description

technical field [0001] The invention relates to a non-woven fabric, in particular to a non-woven fabric with excellent moisture-proof performance. Background technique [0002] In modern times, there are many kinds of synthetic leathers. In addition to the common characteristics of synthetic fiber non-woven fabric base and polyurethane microporous surface layer, all kinds of synthetic leather have different types of non-woven fabric fibers and processing techniques. For example, styrene-butadiene or nitrile latex base impregnating liquid is used to obtain a special combination between non-woven fabric fibers and polymers; the structure has different levels, including 3-layer, 2-layer and single-layer structures; surface embossing and tanning processes are used , Manufacture suede synthetic leather, etc. [0003] The moisture-proof performance of the non-woven base of the existing synthetic leather is not high, and cannot meet the demand of the market. Contents of the inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/413D01F8/06D01F1/10
CPCD04H1/4382D01F1/10D01F8/06D04H1/413D10B2401/021
Inventor 张德满
Owner HEFEI JIENUO MEDICAL PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap