925 silver alloy with purple appearance and brittle failure resistance, and process thereof

A silver alloy and appearance technology, applied in the field of alloys, can solve problems affecting product market sales and user experience, limit market share, etc., and achieve excellent color appearance and processing performance, smelting and processing performance, and excellent toughness.

Inactive Publication Date: 2018-11-20
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The long-term unsolved problems in the industry not only affect the market sales and user experience of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A 925 silver alloy with purple appearance and brittle fracture resistance and its technology. In terms of weight percentage, the composition of the alloy is Be: 0.4wt.%, Li: 0.8wt.%, Al: 1.5wt.%, Ru: 0.2wt.%, Sc: 0.6wt.%, In: 1.5wt.% , Ag: 92.0.0wt.%, the balance is copper. The above-mentioned 925 silver alloy with purple appearance and resistance to brittle fracture and its technology comprises the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and adopting a graphite crucible; Minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1200 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%; after every two rollings, the intermediate annealing temperature is 60...

Embodiment 2

[0021] A 925 silver alloy with purple appearance and brittle fracture resistance and its technology. In terms of weight percentage, the composition of the alloy is Be: 0.6wt.%, Li: 1.2wt.%, Al: 1.6wt.%, Ru: 0.3wt.%, Sc: 0.8wt.%, In: 1.8wt.% , Ag: 93.0wt.%, the balance is copper. The above-mentioned 925 silver alloy with purple appearance and resistance to brittle fracture and its technology comprises the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and adopting a graphite crucible; Minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1200 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%; after every two rollings, the intermediate annealing temperature is 600 ...

Embodiment 3

[0024] A 925 silver alloy with purple appearance and brittle fracture resistance and its technology. In terms of weight percentage, the composition of the alloy is Be: 0.5wt.%, Li: 0.9wt.%, Al: 1.5wt.%, Ru: 0.2wt.%, Sc: 0.7wt.%, In: 1.6wt.% , Ag: 92.0.0wt.%, the balance is copper. The above-mentioned 925 silver alloy with purple appearance and resistance to brittle fracture and its technology comprises the following steps: adding the above proportioned raw materials into an induction furnace under an argon environment, and adopting a graphite crucible; Minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1200 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%; after every two rollings, the intermediate annealing temperature is 60...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a 925 silver alloy with the purple appearance and brittle failure resistance, and a process thereof. The 925 silver alloy comprises the components of, by weight, 0.4-0.6% of Be, 0.8-1.2% of Li, 1.5-1.6% of Al, 0.2-0.3% of Ru, 0.6-0.8% of Sc, 1.5-1.8% of In, 92.0-93.0% of Ag and the balance copper. The 925 silver alloy provides a brand-new material with the purple appearancefor 925 silver alloys for jewelry in China, and the 925 silver alloy has the excellent characteristic of brittle failure resistance. Implementation and industrialization of the 925 silver alloy can effectively promote the demands of product renewal and industry upgrading of the jewelry industry in China, and abundant economic gains and social benefits are obtained while the industry problems aresolved.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a silver alloy. Background technique [0002] Silver is a silver-white precious metal with a charming color, and it has been used to make jewelry since early. In addition, silver also has a very wide range of uses in industry, such as making use of its conductivity to make electronic components and instruments of various precision instruments. Because silver is too soft, it is often doped with other components to form silver alloys. The silver alloy commonly used to make jewelry is sterling silver, which has been used as standard silver in the UK for 800 years, and its composition is 92.5Ag-7.5Cu. This silver alloy is often referred to as 925 silver, which generally refers to a silver product with a silver content of about 92.5wt%. [0003] 925 silver quickly became popular all over the world because it can better inlay various gemstones and produce silver products with various...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C5/08C22C1/02C22F1/14A44C27/00
CPCC22C5/08A44C27/003C22C1/02C22F1/14
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap