Anti-impact pencil-lead-fracture-resistant pencil, and preparation method thereof
An anti-break, pencil technology, applied in the direction of pencil lead, application, household utensils, etc., can solve the problems of difficult positioning, lead breakage, affecting normal use, etc., to reduce the consumption of wood, fine structure, rich and diverse. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0032] Example 1
[0033] A method for preparing a fall-resistant and broken core pencil includes the following steps:
[0034] S1. The wooden raw materials are pulverized to 220 meshes and sterilized by ultraviolet for 28 minutes to obtain wood powder; the wooden raw materials include sawdust, wheat straw, peanut shells, chestnut shells, the weight of the sawdust, wheat straw, peanut shells, and chestnut shells The ratio is 5.2:5.3:1.8:2.7;
[0035] S2. Mix 60 parts by weight of wood flour obtained in S1, 23 parts by weight of pozzolan, 9 parts by weight of starch, 2.8 parts by weight of sodium carbonate, 7 parts by weight of natural latex, and 26 parts by weight of water, knead for 14 minutes, and pour into a plate shape In the mold, let it stand and cure for 3.4 hours at a temperature of 50°C, then demold to obtain a pencil board;
[0036] S3. Place the pencil board obtained in S2 for 11 hours in an environment of 40°C for curing, planing into a grooved plate suitable for the diam...
Example Embodiment
[0043] Example 2
[0044] A method for preparing a fall-resistant and broken core pencil includes the following steps:
[0045] S1. The wooden raw materials are crushed to 240 meshes and sterilized by ultraviolet for 23 minutes to obtain wood powder; the wooden raw materials include sawdust, corn stalks, peanut shells, chestnut shells, the weight of the sawdust, corn stalks, peanut shells, and chestnut shells The ratio is 5.7:6.2:1.4:2.3;
[0046] S2. Mix 64 parts by weight of wood flour obtained in S1, 22 parts by weight of pozzolan, 10 parts by weight of starch, 1.3 parts by weight of sodium carbonate, 8 parts by weight of natural latex, and 22 parts by weight of water, knead for 11 minutes, and pour into a plate shape In the mold, let it stand and cure for 5 hours at a temperature of 60°C, then demold to obtain a pencil board;
[0047] S3. Place the pencil board obtained in S2 for 13 hours at 35°C for curing, planing into a grooved plate suitable for the diameter of the pencil lea...
Example Embodiment
[0054] Example 3
[0055] A method for preparing a fall-resistant and broken core pencil includes the following steps:
[0056] S1. The wooden raw materials are pulverized to 280 meshes and sterilized by ultraviolet for 26 minutes to obtain wood powder; the wooden raw materials include sawdust, rice straw, peanut shells, chestnut shells, the weight of the sawdust, rice straw, peanut shells, and chestnut shells The ratio is 4.3:5.8:1.2:3.7;
[0057] S2. Mix 57 parts by weight of wood flour obtained in S1, 24 parts by weight of pozzolan, 11 parts by weight of starch, 1.7 parts by weight of sodium carbonate, 10 parts by weight of natural latex, and 24 parts by weight of water, knead for 12 minutes, and pour into a plate shape In the mold, let it stand and cure for 4.5 hours at a temperature of 55°C, then demold to obtain a pencil board;
[0058] S3. Place the pencil board obtained in S2 for 12 hours in an environment of 45°C for curing, plan it into a grooved plate suitable for the diam...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap