Flame-retardant polyurethane foam plastic and preparation method thereof

A technology of foam plastics and polyurethane, applied in the field of flame-retardant polyurethane foam plastics, can solve the problems of polyurethane foam materials such as decreased compressive strength, poor compatibility, and unsustainable flame-retardant performance, and achieve low cost, good controllability, The effect of simple process operation

Active Publication Date: 2019-01-18
湖南科旺科技有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor compatibility of ammonium polyphosphate and polyurethane foam base material, the compressiv...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant polyurethane foam plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 48 parts of diphenylmethane diisocyanate, 52 parts of polyether polyol, 2 parts of water, 0.24 parts of triethylenediamine, 0.4 parts of dibutyltin dilaurate, 0.5 parts of methyl silicone oil 201, lignin-diisocyanate-polyphosphoric acid Add 20 parts of ammonium (the mass ratio of lignin / diisocyanate / ammonium polyphosphate is 1:0.2:1) to the reactor at one time, mix and foam under high-speed stirring conditions to obtain flame-retardant polyurethane foam.

Embodiment 2

[0022] 35 parts of toluene diisocyanate, 65 parts of polyether polyol, 1.5 parts of water, 0.4 parts of triethanolamine, 0.45 parts of dibutyltin dilaurate, 0.45 parts of methyl silicone oil 201, lignin-diisocyanate-ammonium polyphosphate (lignin / The mass ratio of diisocyanate / ammonium polyphosphate is 1:0.25:1.1) Add 30 parts into the reactor at one time, mix and foam under high-speed stirring conditions to obtain flame-retardant polyurethane foam.

Embodiment 3

[0024] 40 parts of hexamethylene diisocyanate, 60 parts of polyether polyol, 2.5 parts of water, 0.35 parts of triethanolamine, 0.42 parts of dibutyltin dilaurate, 0.45 parts of methyl silicone oil 201, lignin-diisocyanate-ammonium polyphosphate ( The mass ratio of lignin / diisocyanate / ammonium polyphosphate is 1:0.2:1.2) 35 parts are added into the reactor at one time, mixed and foamed under high-speed stirring conditions to obtain flame-retardant polyurethane foam.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a flame-retardant polyurethane foam plastic. The foam plastic is prepared from the following components in parts by mass: 35-50 parts of toluene diisocynate, 52-65 parts of polyether polyol, 1.5-2.5 parts of water, 0.24-0.4 part of triethanolamine, 0.4-0.45 part of dibutyltin dilaurate, 0.45-0.5 part of methylsilicone oil 201 type and 20-30 parts of flame retardant. The flame-retardant polyurethane foam plastic is prepared by adopting a one-step foaming process, is simple in process operation, excellent in controllability and low in cost, and is easy to realize industrial production.

Description

technical field [0001] The invention relates to the field of flame-retardant polyurethane foam, in particular to a flame-retardant polyurethane foam and a preparation method thereof. Background technique [0002] Polyurethane foam is widely used in many fields of production and life because of its porosity, low density, and excellent mechanical properties, photoelectrochemical properties, and chemical corrosion resistance. It is the most widely used polyurethane product. One of the widest range of products. However, while polyurethane foam brings convenience to people, it also poses a huge threat to the safety of people's lives and properties because of its low ignition point and the shortcomings of being extremely flammable. In order to improve the safety of people's life and property, flame-retardant polyurethane foam came into being and developed rapidly. [0003] The flame retardancy of polyurethane foam mainly includes additive flame retardancy and reactive flame reta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/48C08G18/32C08G18/64C08G18/73C08G18/76C08G18/79C08K3/32
CPCC08G18/3281C08G18/48C08G18/6492C08G18/73C08G18/7614C08G18/7671C08G18/794C08K3/32C08K2003/323C08G2110/0083
Inventor 苏胜培夏新红舒友杨峻基何雨欣
Owner 湖南科旺科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap