pgs/pcl double-layer artificial blood vessel with mesh sheath structure and its construction method

A technology of artificial blood vessels and construction methods, applied in medical science, prostheses, etc., to achieve the effect of strong clinical transformation ability

Active Publication Date: 2021-07-16
FOURTH MILITARY MEDICAL UNIVERSITY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a PGS / PCL double-layer artificial blood vessel with a reticular sheath structure and a construction method thereof for the above-mentioned problems existing in the existing artificial blood vessel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • pgs/pcl double-layer artificial blood vessel with mesh sheath structure and its construction method
  • pgs/pcl double-layer artificial blood vessel with mesh sheath structure and its construction method
  • pgs/pcl double-layer artificial blood vessel with mesh sheath structure and its construction method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The construction method of the PGS / PCL double-layer artificial blood vessel of mesh sheath structure, the steps are as follows:

[0036] S1. Dissolve polycaprolactone in 2,2,2-trifluoroethanol, dissolve at 50°C-55°C for 2h, then shake for 1h to form a uniform polycaprolactone-trifluoroethanol mixed solution, wait use;

[0037] Among them, 0.14g of polycaprolactone is dissolved in every 100mL of 2,2,2-trifluoroethanol;

[0038]In this example, 0.035 mg of polycaprolactone was dissolved in 25 μL of 2,2,2-trifluoroethanol;

[0039] S2. Using electrospinning technology, extract the polycaprolactone-trifluoroethanol mixed solution in S1 with a 1mL syringe connected to the syringe pump, and then fix the syringe containing the mixed solution on the syringe pump;

[0040] Then, adjust the distance between the spinning needle of the electrospinning machine and the receiving iron plate to be 25cm;

[0041] Adjust the advance speed of the syringe pump to 1.275mm / min;

[0042] ...

Embodiment 2

[0053] The construction method of the PGS / PCL double-layer artificial blood vessel of mesh sheath structure, the steps are as follows:

[0054] S1. Dissolve polycaprolactone in 2,2,2-trifluoroethanol, dissolve at 50°C to 55°C for 2.5h, then shake for 1.5h to form a uniform polycaprolactone-trifluoroethanol mixed solution ,stand-by;

[0055] Among them, 0.14g of polycaprolactone is dissolved in every 100mL of 2,2,2-trifluoroethanol;

[0056] In this example, 0.035 mg of polycaprolactone was dissolved in 25 μL of 2,2,2-trifluoroethanol;

[0057] S2. Using electrospinning technology, extract the polycaprolactone-trifluoroethanol mixed solution in S1 with a 1mL syringe connected to the syringe pump, and then fix the syringe containing the mixed solution on the syringe pump;

[0058] Then, adjust the distance between the spinning needle of the electrospinning machine and the receiving iron plate to be 25cm;

[0059] Adjust the advance speed of the syringe pump to 1.275mm / min;

...

Embodiment 3

[0071] The construction method of the PGS / PCL double-layer artificial blood vessel of mesh sheath structure, the steps are as follows:

[0072] S1. Dissolve polycaprolactone in 2,2,2-trifluoroethanol, dissolve at 50°C to 55°C for 3 hours, then shake for 2 hours to form a uniform polycaprolactone-trifluoroethanol mixed solution. use;

[0073] Among them, 0.14g of polycaprolactone is dissolved in every 100mL of 2,2,2-trifluoroethanol;

[0074] In this example, 0.035 mg of polycaprolactone was dissolved in 25 μL of 2,2,2-trifluoroethanol;

[0075] S2. Using electrospinning technology, extract the polycaprolactone-trifluoroethanol mixed solution in S1 with a 1mL syringe connected to the syringe pump, and then fix the syringe containing the mixed solution on the syringe pump;

[0076] Then, adjust the distance between the spinning needle of the electrospinning machine and the receiving iron plate to be 25cm;

[0077] Adjust the advance speed of the syringe pump to 1.275mm / min; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of artificial blood vessel preparation, and discloses a PGS / PCL double-layer artificial blood vessel with a mesh sheath structure and a construction method thereof. The artificial blood vessel is a double-layer tubular structure composed of porous and interconnected polyglycerol sebacate PGS and polycaprolactone PCL with a network structure. The acid lactone is wrapped around the tube core as a sheath. The artificial blood vessel is prepared by electrospinning technology. The PCL spinning solution is 0.14g polycaprolactone dissolved in 100mL 2,2,2-trifluoroethanol. The advancing speed of the syringe pump is 1.275mm / min; the rotational speed of the rotating motor is 120r / min. The artificial blood vessel of the present application can not only complete the function of guiding blood flow as a part of a physiological blood vessel, but also can be transformed into a new blood vessel that is very similar in appearance, histological performance and mechanical properties to the autologous blood vessel after being implanted in the body for one year. strong ability.

Description

technical field [0001] The invention belongs to the technical field of artificial blood vessel preparation, in particular to a PGS / PCL double-layer artificial blood vessel with a mesh sheath structure and a construction method thereof. Background technique [0002] Diseases such as coronary heart disease, arteriosclerotic occlusive disease of the lower extremities, dialysis treatment of chronic renal failure, and congenital malformations of cardiovascular diseases in children seriously threaten people's health. Effective and ideal treatment of these diseases requires a healthy blood vessel To replace the diseased blood vessels in the body. At present, there are two main types of transplanted blood vessels used clinically to replace diseased blood vessels in the body: (1) autologous blood vessels, including autologous arterial blood vessels and autologous venous blood vessels; (2) commercial artificial blood vessels constructed of polymers, such as Artificial blood vessels m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/40A61L27/18A61L27/50A61L27/56
CPCA61L27/18A61L27/50A61L27/507A61L27/56C08L67/04C08L67/00
Inventor 吴炜杨欣
Owner FOURTH MILITARY MEDICAL UNIVERSITY