Acrylic ester solid restickable adhesive and preparation and coating method thereof

A technology of acrylate and coating method, applied in the direction of adhesive, ester copolymer adhesive, adhesive type, etc., can solve the problems of spacer paper coating variation, environmental pollution of solvent-based adhesive, insufficient adhesive force, etc. To achieve the effect of reducing electricity consumption, simple and effective coating method, and enhancing initial adhesion

Active Publication Date: 2019-02-12
深圳市久久天一纸制品有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide an acrylate solid repositionable adhesive and its preparation and coating method, which completely solves the problems of spacer paper coating deformation and insufficient adhesion, and completely maintains the original flatness of the paper , to achieve 100% no bending, and solve the problem of serious environmental pollution caused by solvent-based adhesives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic ester solid restickable adhesive and preparation and coating method thereof
  • Acrylic ester solid restickable adhesive and preparation and coating method thereof
  • Acrylic ester solid restickable adhesive and preparation and coating method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The preparation method of acrylate solid repositionable adhesive comprises the following steps:

[0030] (1) Mixing: mix the acrylate monomer, unsaturated acid, functional monomer, special monomer, crosslinking agent and initiator uniformly by weight to obtain a mixture;

[0031] (2) The first stage of reaction: heat the mixture obtained in step (1) and maintain it in the temperature range of 80-90°C, and when the mixture becomes viscous, cool down to 50-70°C and keep it warm for 2 hours;

[0032] (3) Second stage reaction: heat the mixture obtained in step (2) to a temperature range of 150-180°C for reaction, stop the reaction when it reaches a fluid state, and the reaction time is 40-45 minutes to obtain a fluid polymer .

[0033] (4) Solidification: Cool the fluid polymer obtained in step (3) to below minus 70° C., the fluid polymer solidifies into a solid state, and obtains an acrylate solid repositionable adhesive.

[0034]It completely solves the problem of defo...

Embodiment 1

[0050] A kind of acrylate solid repositionable adhesive, its raw material composition is as shown in table 1:

[0051] The raw material composition of the acrylate solid repositionable adhesive of table 1 embodiment 1

[0052]

[0053]

[0054] The preparation method of the above-mentioned acrylate solid repositionable adhesive comprises the following steps:

[0055] (1) Mixing: mix the acrylate monomer, unsaturated acid, functional monomer, special monomer, crosslinking agent and initiator uniformly by weight to obtain a mixture;

[0056] (2) The first stage of reaction: heat the mixture obtained in step (1) and maintain it in the temperature range of 80-90°C, and when the mixture becomes viscous, cool down to 50-70°C and keep it warm for 2 hours;

[0057] (3) Second stage reaction: heat the mixture obtained in step (2) to a temperature range of 150-180°C for reaction, stop the reaction when it reaches a fluid state, and the reaction time is 40-45 minutes to obtain a f...

Embodiment 2

[0060] A kind of acrylate solid repositionable adhesive, its raw material composition is as shown in table 2:

[0061] The raw material composition of the acrylate solid repositionable adhesive of table 2 embodiment 2

[0062]

[0063] The preparation method of the above-mentioned acrylate solid repositionable adhesive comprises the following steps:

[0064] (1) Mixing: mix the acrylate monomer, unsaturated acid, functional monomer, special monomer, crosslinking agent and initiator uniformly by weight to obtain a mixture;

[0065] (2) The first stage of reaction: heat the mixture obtained in step (1) and maintain it in the temperature range of 80-90°C, and when the mixture becomes viscous, cool down to 50-70°C and keep it warm for 2 hours;

[0066] (3) Second stage reaction: heat the mixture obtained in step (2) to a temperature range of 150-180°C for reaction, stop the reaction when it reaches a fluid state, and the reaction time is 40-45 minutes to obtain a fluid polymer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an acrylic ester solid restickable adhesive and a preparation and coating method thereof. The acrylic ester solid restickable adhesive is prepared from the following raw materials in parts by weight: 60-95 parts of acrylic ester monomer, 0-6 parts of unsaturated acid, 0-6 parts of functional monomer, 1-20 parts of special monomer, 0.5-3 parts of an initiator and 0.1-1 partof a crosslinking agent. The preparation method of the acrylic ester solid restickable adhesive comprises the following steps of (1) mixing; (2) first-stage reaction; (3) second-stage reaction; and (4) solidification. The coating method of the acrylic ester solid restickable adhesive comprises the following steps that (1) the acrylic ester solid restickable adhesive is heated to 120-350 DEG C to become fluid by using a hot melting box; and (2) a base material is coated with the acrylic ester solid restickable adhesive at the fluid state obtained in the step (1), and the adhesive is solidifiedat the room temperature.

Description

technical field [0001] The invention belongs to the field of polymer material technology and hot melt adhesive coating, and specifically relates to an acrylate solid repositionable adhesive and a preparation and coating method thereof. Background technique [0002] Re-stickable notes are sticky notes that can be pasted repeatedly. Currently, re-stickable notes are emerging in China. The disadvantages of known solvent repositionable adhesives are obvious, that is, they are not very environmentally friendly (solvents are mostly harmful). Solvent-based adhesives pollute the environment very seriously. With the improvement of people's environmental awareness and the establishment and improvement of related laws, the application of solvent-based adhesives has been banned and declined rapidly. The manufacturer produces equipment, develops water-based glue, and creates a re-attachable manufacturing model with Chinese characteristics; the water-based pressure-sensitive removable ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J135/02C09J7/21C09J7/24C09J7/30C08F220/18C08F220/06C08F220/20C08F222/14C08F220/14
CPCC09J7/21C09J7/243C09J7/30C09J135/02C08F220/18C09J2400/283C09J2423/106C08F220/1808C08F220/06C08F220/20C08F222/14C08F222/102C08F220/14C08F220/1802
Inventor 贺鸿武
Owner 深圳市久久天一纸制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap